• 한국전기전자재료학회논문지
• /
• 제20권3호
• /
• pp.234-239
• /
• 2007

This paper describes the TiW ohmic contact characteristics under the surface treatment of the polycrystalline 3C-SiC thin film grown on $SiO_2/Si(100)$ wafers by APCVD. The poly 3C-SiC surface was polished by using CMP(chemical mechanical polishing) process and then oxidized by wet-oxidation process, and finally removed SiC oxide layers. A TiW thin film as a metalization process was deposited on the surface treated poly 3C-SiC layer and was annealed through a RTA(rapid thermal annealing) process. TiW/poly 3C-SiC was investigated to get mechanical, physical, and electrical characteristics using SEM, XRD, XPS, AFM, optical microscope, I-V characteristic, and four-point probe, respectively. Contact resistivity of the surface treated 3C-SiC was measured as the lowest $1.2{\times}10^{-5}{\Omega}cm^2$ at $900^{\circ}C$ for 45 sec. Therefore, the surface treatments of poly 3C-SiC are necessary to get better contact resistance for extreme environment MEMS applications.

• 한국대기환경학회지
• /
• 제20권6호
• /
• pp.759-771
• /
• 2004

This study analyzed concentrations of volatile organic compounds (VOCs) produced from incineration of plastic wastes at $600^{\circ}C$. The plastic wastes used in this study included polyethyleneterephthlate (PETE), high density polyethylene (HOPE), polyvinyl chloride (PVC), low density polyethylene (LOPE), polypropylene (PP), polystyrene (PS) and other. Plastic wastes were heated from room temperature upto $600^{\circ}C$ providing the compressed air inside of a small-scale electric furnace for 90 minutes and then they were oxidized (incinerated) for 60 minutes at $600^{\circ}C$ maintaining the same air supply. VOCs emitted from the incineration process were sampled using an air sampling pump and Tedlar air bags for 150 minutes and then the components and concentrations of the VOCs were analyzed by a GC-MS. The most prominent chemical structure of the VOCs obtained from the incineration process of the HOPE, LOPE and PP, which include ethylene groups in their main chains, was identified as aliphatic hydrocarbons such as 1-hexene. However, aromatics such as benzene were major chemical structure from the incineration of PETE, PVC and PS which include benzene rings in their main chains. This study estimated the total VOC production from the incineration of the plastic wastes based on the real plastic waste production and the emission factors. 64% and 27% of the total VOC emissions consisted of aliphatic hydrocarbons and aromatics, respectively, which have double bonds within their molecular structure and thus a high ground level ozone formation potential.

• 한국지하수토양환경학회:학술대회논문집
• /
• 한국지하수토양환경학회 2003년도 총회 및 춘계학술발표회
• /
• pp.107-110
• /
• 2003

Reduction of nitrate by zero valent iron (Fe$^{0}$ ) has been previously studied, but the proper treatment for the by-product of ammonium has not been reported. However, in terms of nitrogen contamination, ammonium may be regarded as another form of nitrogen contaminants since it can be oxidized to nitrate again under aerobic conditions. This study is focused on simultaneous removal of nitrate and its by-product of ammonium, with the ZanF (Zeolite anchored Fe), a product derived from zeolite modified by Fe(II) chloride followed by reduction with sodium borohydride. Batch experiments were performed without buffer at two different pH condition with ZanF, iron filing, Fe(II)-sorbed zeolite, and pure zeolite to estimate the nitrate reduction and the ammonium production. At higher pH, removal rate of nitrate was reduced in both ZanF and iron filings. ZnF removed 60 % of nitrate at initial pH of 3.3 with no production of ammonium, while iron filing showed equivalent production of ammonium to the reduced amount of nitrate. In terms of nitrogen contamination, ZanF removed about 60 % and 40 % at initial pH of 3.3 and 6, respectively, while iron filing presented negligible removal against total nitrogen including nitrate and ammonium.

• Corrosion Science and Technology
• /
• 제11권4호
• /
• pp.141-150
• /
• 2012

Stress corrosion cracks in Alloy 600 compact tension specimens tested at $325^{\circ}C$ in a simulated primary water environment of pressurized water reactor were analyzed by analytical transmission electron microscopy and secondary ion mass spectroscopy (SIMS). From a fine-probe chemical analysis, oxygen was found on the grain boundary just ahead of the crack tip, and chromium oxides were precipitated on the crack tip and the grain boundary attacked by the oxygen diffusion, leaving a Cr/Fe depletion (or Ni enrichment) zone. The oxide layer inside the crack was revealed to consist of a double (inner and outer) layer. Chromium oxides existed in the inner layer, with NiO and (Ni,Cr) spinels in the outer layer. From the nano-SIMS analysis, oxygen was detected at the locations of intergranular chromium carbides ahead of the crack tip, which means that oxygen diffused into the grain boundary and oxidized the surfaces of the chromium carbides. The intergranular chromium carbide blunted the crack tip, thereby suppressing the crack propagation.

• Corrosion Science and Technology
• /
• 제9권4호
• /
• pp.164-170
• /
• 2010

Thermodynamic consideration was performed for Alloy 617 exposed to an impure helium ($H_2$ 20pa, $H_2O$ 0.5pa, $CH_4$ 2pa and CO 5pa) at $950^{\circ}C$. Oxidation power was decreased in the order Al > Ti > Si > Cr > Mn. Decarburization and carburization reactions were available leading to carbon activity decrease and increase, respectively, depending on carbon and Cr activities. The thermodynamic prediction was compared with the experimental results obtained in similar conditions (($H_2$ 20pa, $H_2O$ 0.05pa, $CH_4$ 5pa and CO 2pa) and $950^{\circ}C$) by others for Alloy 617. The driving force for oxidation of Al, Ti and Si is very large to be oxidized at a given impure helium and the environment is actually carburizing towards the structural alloy, which is consistent with this work.

• 한국물환경학회지
• /
• 제31권2호
• /
• pp.209-215
• /
• 2015

The purpose of this study is to evaluate the characteristic of the iron oxide carrier for removing arsenic contained in the groundwater. 4 types of iron oxide carrier used in the study is iron oxide coated sand carrier (IOCSC), iron oxide coated zeolite carrier (IOCZC), iron oxide plasticity carrier (IOPC) and platinum iron oxide plasticity carrier (PIOPC). The results of this study, IOPC is showed high arsenic adsorption strength and the maximum amount of adsorption than the IOCC. Based on the results of the arsenic adsorption characteristic, by using IOCC was conducted to column test. As a result, PIOPC is showed a high arsenic adsorption amount than IOPC, it was found that the time required to reach the breakthrough point is also extended. Therefore it is determined that stably compliance with water quality standards enhanced drinking water when using the PIOPC.

• Nuclear Engineering and Technology
• /
• 제52권10호
• /
• pp.2299-2305
• /
• 2020

Zr alloy specimens were coated with Cr-Al alloy to enhance their resistance to oxidation. The coated samples were oxidized at 1200 ℃ in a steam environment for 300 s and showed extremely low oxidation when compared to uncoated Zr alloy specimens. The microstructure and elemental distribution of the oxides formed on the surface of Cr-Al alloys have been investigated by transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). A very thin protective layer of Cr₂O₃ formed on the outer surface of the Cr-Al alloy, and a thin Al₂O₃ layer was also observed in the Cr-Al alloy matrix, near the surface. Our results suggest that these two oxide layers near the surface confers excellent oxidation resistance to the Cr-Al alloy. Even after exposure to a high temperature of 1200 ℃, inter-diffusion between the Cr-Al alloy and the Zr alloy occurred in very few regions near the interface. Analysis of the inter-diffusion layer by high-resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray spectroscopy (EDS) measurement confirmed its identity as Cr₂Zr.

• 한국지하수토양환경학회지:지하수토양환경
• /
• 제28권6호
• /
• pp.16-23
• /
• 2023

Heavy metal (Zinc, Cadmium, Lead) adsorption onto surface modified activated carbon was performed in order to better understand the effect of sodium ion addition to activated carbon. Surface modification methods in this research included water washing, nitric acid washing, and sodium addition after nitric acid washing. These surface modifications generated oxygen functional groups with sodium ions on the surface of the activated carbon.. This caused the change of the specific surface area as well as in the ratio of the carboxyl groups. Heavy metal adsorption onto sodium-containing activated carbon was the most among the three modifications. After the adsorption of heavy metals, the carboxyl group ratio decreased and sodium ions on the surface of the activated carbon were almost non-existent after the adsorption of heavy metals onto sodium-containing activated carbon. The results from this research indicated that ion exchange with sodium ions in carboxyl groups effectively improved heavy metal adsorption rather than electrostatic adsorption and hydrogen ion exchange.

• Journal of Advanced Marine Engineering and Technology
• /
• 제17권3호
• /
• pp.42-49
• /
• 1993

Recently, because the lubricating oil showed a tendency to be emulsified and oxidized by high speed, high output and the extension of maintenance & conservation of marine engine, the cavitation erosion-corrosion at such an environment became a big problem on effective performance of engine. Therefore, there was a need to study the behavior and protection of erosion-corrosion damage, and then applied inhibitor to a protective method of cavitation erosion- corrosion damage. At this time, test environments were marine lubricating oil & various emulsified oil that mixed distilled water and sea water etc., and also used 20KHz, 24.mu.m piezoelectric vibrator as an experimental apparatus of cavitation erosion. With this apparatus, we investigated an influence of the emulsified oil on characteristics of erosion-corrosion and protection for erosion-corrosion by inhibitor at slide bearing metals.

• 한국연소학회:학술대회논문집
• /
• 한국연소학회 2001년도 제23회 KOSCO SYMPOSIUM 논문집
• /
• pp.27-34
• /
• 2001

The soot formation characteristics have been studied experimentally in concentric co-flow ethylene/propane diffusion flames. Comparing to the homogeneously mixed propane/ethylene case, the increase of soot formation is observed when propane is supplied through the outer nozzle, while the decrease is observed when propane is supplied through the inner nozzle. The reaction path of PAHs formed from the pyrolysis process of propane is likely to be responsible to the observed difference. When propane is supplied through the outer nozzle, PAHs formed during the combustion process are easy to be exposed to the oxidization environment; however, when propane is supplied through the inner nozzle, PAHs are not likely to be oxidized and thus get involved in soot formation process. The synergistic effect in ethylene/propane diffusion flames is affected not only by the composition of mixture but also by the way of mixing.