• 대한기계학회논문집A
• /
• 제20권6호
• /
• pp.1753-1761
• /
• 1996

The wear behaviors of ${Si_3}{N_4}$ under the different sliding conditions were investigated. The cylinder-on-disc wear tester was used. Using the servo-metor, the sliding speed did ot alternate due to the frictional forces. Threekinds of loads and speeds were selected to watch the variation of the wear rates and the frictional forces. Also three kinds of sliding condition under a constant speed were used to see the effects of the oxidationand the abrasion. The contact pressure was more effective than the repeated cycle on the wear behavior of ${Si_3}{N_4}$. With the low loads, the effect of the asperity-failure was more dominant than that of oxidation and abrasion. As increasing the load, the effects of oxidation and abrasion were increased, but the asperity-failure effects were decreased. The wear particles destroyed the ozide layers formed on sliding surfaces. The wear rate could be decreased due to delaying the oxidation. The frictional power and the wear weight per time were usefuel to see the transition of wear.

• 한국세라믹학회지
• /
• 제32권11호
• /
• pp.1315-1321
• /
• 1995

The optimal coating condition for chrominum carbide coating was selected by Taguchi method. The wear tests with coated specimens by HVOF method were performed in the temperature to 80$0^{\circ}C$. Applied normal loads were selected to be from 8N to 30N. The worn surfaces and subsurfaces were characterized by XRD, EPMA, AES and SEM. The wear track increased with increasing applied normal load, and in terms of the temperature range from 400 to $600^{\circ}C$, below that range, the wear track increased, and above that temperature ragne, the wear track decreased. The degree of oxidation caused by the test temperature and the frictional heating was responsible to the unique high temperature wear behavior chromium carbide coatings.

• Tribology and Lubricants
• /
• 제17권6호
• /
• pp.459-466
• /
• 2001

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk on friction characteristics in various sliding conditions were investigated. AISI52100 steel ball was used for the substrate of coated ball specimens, which were prepared by depositing TiN coating with 1(m in coating thickness. AISI1045 steel was used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of two materials, the tests were performed both in air for forming oxide layer on the contact parts and in nitrogen environment to avoid oxidation. From the test results, the frictional characteristic between the two materials was predominated by iron oxide layer that formed on wear tract of counter-body and this layer caused friction transition and high friction. And the adhesive wear occurred from steel disk to TiN coated ball caused the formation of oxide layer on counter parts between the two materials.

• 폴리머
• /
• 제25권1호
• /
• pp.133-141
• /
• 2001

산화억제제로 사용한 이규화 몰리브덴($MoSi_2$)의 함량에 따른 일방향 탄소/탄소 복합재료의 마찰 및 마모 특성에 관하여 대기상태 하에서 정속마찰시험기를 이용하여 측정하였다. 그 결과, 탄소/탄소 복합재료는 마찰온도 150~180${\circ}C$에서 급격한 마찰계수의 전이, 즉 normal wear 영역에서의 낮은 마찰계수(${\mu}$=0.15~0.2)에서 dusting wear 영역에서의 높은 마찰계수(${\mu}$=0.5~0.6)로의 전이를 나타내었다. 이렇게 마찰계수가 전이하는 온도범위의 존재는 탄소/탄소 복합재료로 만든 브레이크가 복합재료의 열적 특성에 큰 영향을 받는다는 것을 의미한다. 그리고 산화억제제인 $MoSi_2$를 가지는 탄소/탄소 복합재료는 이를 함유하지 않은 복합재료에 비해 약 1.5배 정도의 낮은 평균마찰계수 및 마모율을 나타내었으며, 특히 4 wt% $MoSi_2$ 함량을 가진 복합재료가 가장 큰 마모활성화 에너지 값을 나타내었다.

• 대한기계학회논문집A
• /
• 제27권3호
• /
• pp.335-342
• /
• 2003

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk in sliding are investigated. Also wear mechanism to from the oxide layer and the characteristics of the oxide layer formation are investigated. AISI 52100 steel ball is used for the substrate of coated ball specimens. Two types of coated ball specimens were prepared by depositing TiN coating with 1 and 4 ${\mu}{\textrm}{m}$ in coating thickness. AISI 1045 steel is used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of the two materials, the tests were performed both in air for forming oxide layer on the contact parts and in nitrogen environment to avoid oxidation. And to study the effects of surface roughness of counter-body, TiN coating thickness and contact load of sliding test on the characteristics of oxide layer formation on counter-body, various tests were carried out. From the results, the friction characteristics between the two materials was predominated by iron oxide layer that formed on wear track on counter-body and this layer caused the high friction. And the formation rate of the oxide layer on wear track increased as the real contact area between the two materials increased as the contact load increased, the TiN coating thickness decreased and the surface of counter-body smoothened.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제34회 추계학술대회 개최
• /
• pp.109-116
• /
• 2001

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk in sliding are investigated. Also wear mechanism to form the oxide layer and the characteristics of the oxide layer formation are investigated. AIS152100 steel ball is used for the substrate of coated ball specimens. Two types of coated ball specimens were prepared by depositing TiN coating with 1 and 4um in coating thickness. AISI1045 steel is used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of the two materials, the tests were performed both in ambient for forming oxide layer on the contact parts and in nitride environment to avoid oxidation. And to study the effects of surface roughness of counter-body, TiN coating thickness and contact load of sliding test on the characteristics of oxide layer formation on counter-body, various tests were carried out. From the results, the friction characteristics between the two materials was predominated by iron oxide layer that formed on wear track on counter-body and this layer caused the high friction. And the formation rate of the oxide layer on wear track increased as the real contact area between the two materials increased as the contact load increased, the TiN coating thickness decreased and the surface of counter-body smoothened.