• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.126-130
• /
• 2007

Oxidation behavior of CaO added Mg and Mg-5Al alloys was investigated. At $500^{\circ}C$, oxidation rate of pure Mg was abruptly increased, while that of CaO added Mg was remarkably reduced with increasing CaO content. As a result of surface analysis by AES, there was the thin oxide layer mixed with MgO and CaO in CaO added Mg. Oxidation behavior of CaO added Mg was similar to that of Ca added Mg. Oxidation rate of 0.6CaO added Mg-5Al alloy was much lower than that of Mg-5Al alloy at $500^{\circ}C$ and both alloys showed the linear weight change at $400^{\circ}C$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1149-1150
• /
• 2006

The oxidation of (W,Mo)$Si_2$ powders has been investigated at 400, 500 and $600^{\circ}C$ for 12.0 hours in air. It was shown that the low temperature oxidation resistance of (W,Mo)$Si_2$ was worse than that of $MoSi_2$, and they showed great changes in mass, volume and colour. Especialy at $500^{\circ}C$, the amount of volume expansion of (W,Mo)$Si_2$ was as high as about $7\sim8$ times and color changed from black to yellow after 4.0h with $MoO_3$, $WO_3$, (W,Mo)$O_3$ and amorphous $SiO_2$ as main reaction products. The mass gain and oxidation rate were relatively slower at $400^{\circ}C$ and $600^{\circ}C$ than that at $500^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.2
• /
• pp.110-118
• /
• 1995

The effect of reductants (Ti, Si, Al, Mn, Fe) addition into molten Borax has been studied on oxidation resistance and the growth of boronized layer formed during electro-boronizing on the substrate such as carbon steel and STS 430. Experiments have been carried out at the current density of 0.5 A/$\cm^2$ and in temperature range of 600~$1000^{\circ}C$ for 1~5 hours. The penetrated depth of the boron increased with addition of reductants (Ti, Si, Al) and decreased with addition of Mn and Fe. But excessive addition of reductants inhibited the boronizing due to an increase in viscosity of electrolyte. Oxidation resistance of the boronized carbon steel was improved but that of the boronized STS 430 decreased.

• Journal of Korea Foundry Society
• /
• v.26 no.2
• /
• pp.92-97
• /
• 2006

Contact material is widely used as electrical parts. Ag-Cd alloy has a good wear resistance and stable contact resistance. But the disadvantages of Ag-Cd alloy are coarse Cd oxides and harmful metal, Cd. To solve the disadvantages of that, Ag-Sn alloy that has stable and fine Sn oxide at high temperature has been developed. In order to optimize Sn amount that affects the formation of the oxide layer on the surface, we worked for the microstructures and properties of Ag-Sn material fabricated by rapid solidification process. The experimental procedure were melting using high frequency induction, melt spinning, and internal oxidation. We have shown that the optimized Sn amount for high hardness is 7.09 wt%Sn. Surface oxide layer forms when Sn amount is over 9.45 wt%. The size of Sn oxide is 20 nm.

• Journal of the Korean Ceramic Society
• /
• v.23 no.2
• /
• pp.31-37
• /
• 1986

The effect of dehydration temperature on the reduction process of silica-coated hematite was invest-igated The particle shape and magnetic properties of the products reduced from hematite at various conditions and the oxidation resistance of silica-coated iron powder were examined. It was revealed that single phase iron powder obtained over 45$0^{\circ}C$ had good magnetic properties. The iron powder manufactured between 45$0^{\circ}C$ and 50$0^{\circ}C$ displayed the maximum coercive force as a result of maintaining its acicular shaped. However the coercive force of iron powder reduced over 50$0^{\circ}C$ was decreased. The oxidation resistance of silica-coated iron powder in air was very good up to 11$0^{\circ}C$ and for 12 days.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.373-382
• /
• 1999

Nucleation and growth process of sticking particle in ferritic stainless steels was investigated using a two disk type hot rolling simulator. The sticking behavior was strongly dependent on the surface roughness of a high speed steel roll(HSS) and the oxidation resistance of the ferritic stainless steels. A hot rolling condition with the lower oxidation resistance of the stainless steel and the higher surface roughness of HSS roll was more sensitive to sticking occurrence. It was also illucidated that the initial sticking particles were nucleated at the scratches formed on the roll surface and were served as the sticking growth sites. As rolling proceeded, the sticking particles grew sites. As rolling proceeded, the sticking particles grew by the process that the previous sticking particles provided the sticking growth sites.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.171-173
• /
• 2005

Inconel 617 is a solid solution, nickel-chromium-cobalt-molybdenum alloy with an exceptional combination of high temperature strength and oxidation resistance. The combination of high strenth and oxidation resistance at temperatures over $1800^{\circ}F$ makes Inconel 617 an attractive material for such components as ducting, transition liners in both aircraft and gas turbine. In this study, the weldability and weldment characteristics of Inconel 617 are considered in GTAW associated with the two welding current and with back shielding gas using or not. After GTAW with 120A and 150A current, microstructures and hardness test, bending test, tensile test on room and elevated temperature for the determination of optical welding condition.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.4
• /
• pp.173-178
• /
• 2006

Incoloy alloy 909 is an Fe-Ni-Co based superalloy that is attractive for gas turbine engine applications. The absence of chromium, however, makes the alloy more susceptible to oxidation in high temperature. To improve the oxidation resistance aluminizing was performed by high activity low temperature pack cementation process. Aluminizing condition was examined with different times and temperatures. Optimum aluminizing conditions were at the temperature of $552^{\circ}C$ for 20 hrs. In the optimized condition, the thickness of the aluminized layer was about $20{\mu}m$. Also, the aluminized layer made the alloy to increase the resistance to the corrosion.

• Nuclear Engineering and Technology
• /
• v.53 no.7
• /
• pp.2295-2303
• /
• 2021

To investigate wall-thinning impact on axial load resistance of Zircaloy-4 cladding rods after a LOCA transient, axial tensile samples have been machined on as-received tubes with reduced thicknesses between 370 and 580 ㎛. After high temperature oxidation under steam at 1200 ℃ with measured ECR ranging from 10 to 18% and water quenching, machined samples were axially loaded until fracture. These tests were modeled using a fracture mechanics approach developed in a previous study. Fracture stresses are rather well predicted. However, the slightly lower fracture stress observed for wall-thinned samples is not anticipated by this modeling approach. The results from this study confirm that characterizing the axial load resistance using semi-integral tests including the creep and burst phases was the best option to obtain accurate axial strengths describing accurately the influence of wall-thinning at burst region.

• Tribology and Lubricants
• /
• v.25 no.6
• /
• pp.432-437
• /
• 2009

The effect of oxidation in SAE 5W30 engine oils on friction and wear characteristics was investigated using reciprocating bench tester and shell 4-ball tester. Commercial engine oils were collected and oxidized using the KS M 2021 method modifying the oxidation time. Kinematic viscosity, total acid number(TAN), FT-IR spectrum and total base number(TBN) also measured to examine the chemical change of oils with oxidation. The results showed that TAN was slightly changed and Kinematic viscosity was suddenly increased during the oxidation stage. however, TBN results keep a constant slope after TBN linearly decreased with oxidation time. Spectroscopy results showed that spectrums were orderly increased at $1710cm^{-1}$ during the oxidation time. Friction test results showed that oxidation of oils formed unstable friction layers causing higher fluctuating friction. however, the wear resistance was independent of oxidized time due to the different friction characteristics by oxidation. We found several factors in relation to lubrication properties with oxidation time. This factors were Viscosity, TBN, change of FT-IR spectrum, friction coefficient using reciprocating bench tester and wear scar.