• 열처리공학회지
• /
• 제27권5호
• /
• pp.225-229
• /
• 2014

The influence of electron irradiation energy(eV) on the structural, electrical and optical properties of ITO/ZnO bi-layered films prepared with RF magnetron sputtering has been investigated. The ITO/ZnO show the lowest resistivity of $2.8{\times}10^{-4}{\Omega}cm$. The optical transmittance in a visible wave length region also increased with the electron irradiation energy. The film irradiated at 900 eV shows 82---- of optical transmittance in this study. By comparison of figure of merit, it was observed the optical transmittance and electrical resistivity of the films were dependent on the electron irradiation energy and optoelectrical performance of ITO/ZnO film is improved with electron irradiation.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2015년도 제49회 하계 정기학술대회 초록집
• /
• pp.178.1-178.1
• /
• 2015

In and Ga doped ZnO (IGZO) thin films were prepared by radio frequency magnetron sputtering without intentional substrate heating on glass substrate and TiO2-deposited glass substrates to consider the effect of a thin TiO2 buffer layer on the optical and electrical properties of the films. The thicknesses of the TiO2 buffer layer and IGZO films were kept constant at 5 and 100 nm, respectively. Since the IGZO/TiO2 bi-layered films show the higher FOM value than that of the IGZO single layer films, it is supposed that the IGZO/TiO2 bi-layered films will likely perform better in TCO applications than IGZO single layer films.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1996년도 하계학술대회 논문집 C
• /
• pp.1569-1571
• /
• 1996

The role of ESR spectroscopy in the characterization of functional LB films is discussed. Optical absorption were performed on LB films of binary mixtures of three kinds of merocyanine dyes where DS and 6Me-DS form J-like aggregates but not DO in single component films. The observed optical absorption spectra of mixed films were markedly dependant on the combination of dyes. We found the formation of J-aggregates in a mixed merocyanine dyes containing a non J-aggregate forming dye DO, in a single component case. In structural studios, ESR is of particular important in the analysis of molecular orientation of LB films. Development of new functional LB films may provide more cases where ESR spectroscopy will clarify the nature of such films.

• 한국표면공학회지
• /
• 제38권5호
• /
• pp.179-182
• /
• 2005

Indium Tin Oxide (ITO) thin films were deposited from various target densities ($98.7\%\~99.6\%$) using RF magnetron sputtering. Effect of the sputtering target densities on the structural, electrical and optical properties of deposited ITO thin films was investigated. The preferable (400) crystalline orientation peak was observed on the films deposited from > $99.0\%$ target density. Higher target density produced films with higher roughness but lower resistivity. All of the deposited films showed optical transmittance more than $85\%$ in the visible wavelength region. It is necessary to use the highest target density for sputtering deposition of ITO thin films.

• 한국결정성장학회지
• /
• 제14권4호
• /
• pp.145-150
• /
• 2004

We have investigated the structural, electrical and optical properties of Al-doped ZnO (AZO) thin films grown on glass substrate by pulsed DC magnetron sputtering as functions of pulse frequency and substrate temperature. A highly c-axis oriented AZO thin film is grown in perpendicular to the substrate when pulse frequency of 30 kHz and substrate temperature of $400^{\circ}C$ was applied. Under this optimized growth condition, the resistivity of AZO thin films exhibited $7.40\times 10^{-4}\Omega \textrm{cm}$. This indicated that the decrease of film resistivity resulted from the improvement of film crystallinity. The optical transmittance spectra of the films showed a very high transmittance of 85∼90 % in the visible wavelength region and exhibited the absorption edge of about 350 nm. The results show the potential application for transparent conductivity oxide (TCO) thin films.

• 한국표면공학회지
• /
• 제41권4호
• /
• pp.129-133
• /
• 2008

Nitrogen and aluminum codoped ZnO(NAZO) thin films were grown on glass substrates with changing the nitrogen flow ratio by radio-frequency magnetron sputtering. The structural, optical, and electrical properties of the NAZO films were investigated. The surface morphologies and the structural properties of the thin films were analyzed by using the X-ray diffraction and scanning electron microscopy. The NAZO thin film, deposited at nitrogen flow ratio of 0%, showed a strongly c-axis preferred orientation and the lowest resistivity of $3.2{\times}10^{-3}{\Omega}cm$. The intensity of ZnO(002) diffraction peak was decreased gradually with increasing the nitrogen flow ratio. The optical properties of the films were measured by UV-VIS spectrophotometer and the optical transmittances for all the samples were found to be an average 90% in the visible range. Based on the transmittance value, the optical bandgap energy for the NAZO thin film deposited at nitrogen flow ratio of 0% was determined to be 3.46 eV. As for the electrical properties, the carrier concentration and the hall mobility were decreased, but the electrical resistivity was increased as the nitrogen flow ratio was increased.

• 반도체디스플레이기술학회지
• /
• 제9권4호
• /
• pp.83-86
• /
• 2010

The transparent electrode properties of ITO films deposited by RF magnetron sputtering with process pressure were investigated. The ITO thin films was deposited on a glass substrate using a target with 3in diameter sintered at a ratio of $In_2O_3$ : $SnO_2$ (9 : 1). 200-nm-thick ITO thin films were manufactured by various process pressures ($2.0{\times}10^{-2}$, $7.0{\times}10^{-3}$ and $2.0{\times}10^{-3}$ Torr). The optical transmittance and resistivity of the deposited ITO thin films showed a relatively satisfactory result under $10^{-2}$ Torr. For high process pressure, the optical transmittance was below 80%, while for low process pressure, the optical transmittance was above 85%. As a result of of mobility, resistivity and carrier concentration by Hall measurement, we obtained satisfactory properties to apply into a transparent conducting thin film.

• 한국전기전자재료학회논문지
• /
• 제24권9호
• /
• pp.739-743
• /
• 2011

Ga doped ZnO (GZO)/Cu bi-layer films were deposited with RF and DC magnetron sputtering on glass substrate and then the effect of post deposition annealing temperature on the structural, optical and electrical properties of the films was investigated. The post deposition annealing process was conducted for 30 minutes in gas pressure of $1{\times}10^{-3}$ Torr and the annealing temperatures were 150 and $300^{\circ}C$. With increasing annealing temperature, GZO/Cu films showed an increment in the prefer orientation of ZnO (002) diffraction peak in the XRD pattern and the optical transmittance in a visible wave region was also increased, while the electrical sheet resistance was decreased. The GZO/Cu films annealed at $300^{\circ}C$ showed the highest optical transmittance of 70% and also showed the lowest electrical resistance of $85\;{\Omega}/{\Box}$ in this study.

• 대한금속재료학회지
• /
• 제50권7호
• /
• pp.545-548
• /
• 2012

The optical and electronic properties of Indium Tin Oxide (ITO) thin films deposited on a RF-plasma treated glass substrate were investigated by X-Ray Photoelectron Spectroscopy (XPS), Ultra-violet Photoelectron Spectroscopy (UPS), Reflected Electron Energy Loss Spectroscopy (REELS). The modification of glass substrates was carried out by varying the time of the plasma surface treatment in an oxygen atmosphere. The focus of this research was to examine how the optical and electronic properties of ITO thin films change with the plasma treatment time. The surface energy increased since the carbon bonds were removed from the surface after the glass substrate received the surface treatment. The ITO thin films produced on the glass substrate with surface treatment showed that the high optical transmittance was approximately 85%. The measured band gap energy was as high as 3.23 eV when the plasma treatment time was 60 s and the work function after the treatment was increased by 0.5 eV in comparison to that before the treatment of 60 s. The ITO thin film exhibited an excellent sheet resistance of $2.79{\Omega}/{\Box}$. We found that the optical and electronic properties of ITO thin films can be improved by RF-plasma surface treatment.

• 한국재료학회지
• /
• 제32권5호
• /
• pp.249-257
• /
• 2022

Transparent thin films of pure and nickel-doped ZrO₂ are grown successfully by sol-gel dip-coating technique. The structural and optical properties according to the different annealing temperatures (300 ℃, 400 ℃ and 500 ℃) are investigated. Analysis of crystallographic properties through X-ray diffraction pattern reveals an increase in crystallite size due to increase in crystallinity with temperature. All fabricated thin films are highly-oriented along (101) planes, which enhances the increase in nickel doping. Scanning electron microscopy and energy dispersive spectroscopy are employed to confirm the homogeneity in surface morphology as well as the doping configuration of films. The extinction coefficient is found to be on the order of 10^-2, showing the surface smoothness of deposited thin films. UV-visible spectroscopy reveals a decrease in the optical band gap with the increase in annealing temperature due to the increase in crystallite size. The variation in Urbach energy and defect density with doping and the change in annealing temperature are also studied.