• Journal of the Korean Wood Science and Technology
• /
• 제22권3호
• /
• pp.17-25
• /
• 1994

This study was carried out to compare the properties of Com-Ply Boards with those of OSBs. These two kinds of boards were made of same flakes. Com-Ply Boards were covered with three different thickness veneers, such as 4mm, 3mm, and 2.5mm. All manufactured Com-Ply Boards and OSBs were 12mm thick. In MOR, all Com-Ply Boards were higher than OSB, and especially 3mm-veneer and 2.5mm-veneer Com-Ply Board were highest. But OSB showed 420kg/$cm^2$. 3mm-veneer Com-Ply Board showed the highest internal bonding 7.0kg/$cm^2$ and then 2.5mm-veneer showed 6.8kg/$cm^2$, and OSB showed 6.6kg/$cm^2$. Screw holding strength showed the high value 23.9kg/$cm^2$, 25.5kg/$cm^2$, and 29.3kg/$cm^2$ respectively at 3mm-veneer, 2.5mm-veneer Com-Ply Board and OSB. Thickness swelling of Com-Ply Boards was lower than that of OSB, but Water absorption of OSB was lower. Finally it was very encouraging that all properties of OSB without veneer, whose cost is higher than flake and whose properties is better, were not worse than those of Com-Ply Board with veneer. It seems That more researches on OSB will be required.

• Journal of the Korean Wood Science and Technology
• /
• 제40권4호
• /
• pp.287-293
• /
• 2012

본 연구에서는 현재 국내 목조건축에서 벽구성 재료로 많이 사용되고 있는 수입 OSB(배향성 스트랜드보드)를 국산 합판으로 대체하기 위해 OSB와 국산 합판의 못 접합부 전단성능을 비교 검토하였다. 주부재(잣나무)와 측면부재(OSB 합판)의 섬유 방향성(평행 직각)에 따른 전단성능은 합판에서 현저하였다. 결과, OSB와 합판 모두 현행 국내 기준인 못 접합부 기준 허용전단내력을 만족하는 것으로 나타났다. 그리고, 표면층에 MLH(열대산 활잡목)를 사용하고 7ply 구성한 합판(P-4 type)은 OSB보다 섬유방향에 관계없이 큰 전단성능을 나타냈다. 전반적으로 측면부재로서 합판을 사용할 경우 주부재에 대하여 섬유방향을 직교되도록 구성할 경우, 평행방향 구성보다 큰 전단성능을 발휘할 수 있음이 확인되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권2호
• /
• pp.163-171
• /
• 2014

Environmental issues about indoor air quality have been increased and focused on volatile organic compounds (VOCs) caused cancer, asthma, and skin disease. Reducing VOCs has been attempted in many different methods such as using environmentally friendly materials and air cleaner or purifier. Charcoal is well known material for absorbing VOCs. Therefore, carbonized board from medium density fiberboard has been developed. We assumed that the source of carbonized boards can be any type of wood-based panels. In this study, carbonized boards were manufactured from oriented strand board (OSB) at 400, 600, 800, and $1000^{\circ}C$. Each carbonized OSB (c-OSB) was evaluated and determined physiomechanical characteristics such as exterior defects, dimensional shrinkage, modulus of elasticity, and bending strength. No external defects were observed on c-OSBs at all carbonizing conditions. As carbonizing temperature increased, less porosity between carbonized wood fibers was observed by SEM analysis. The higher rate of dimensional shrinkage was observed on c-OSB at $1000^{\circ}C$ (66%) than c-OSB at 400, 600, and $800^{\circ}C$ (47%, 58%, and 63%, respectively). The densities of c-OSBs were lower than original OSB, but there was no significant different among the c-OSBs. The bending strength of c-OSB increased 1.58 MPa (c-OSB at $400^{\circ}C$) to 8.03 MPa (c-OSB at $1000^{\circ}C$) as carbonization temperature increased. Carbonization temperature above $800^{\circ}C$ yielded higher bonding strength than that of gypsum board (4.6 MPa). In conclusion, c-OSB may be used in sealing and wall for decorating purpose without additional artwork compare to c-MDF which has smooth surface.

• Journal of the Korean Wood Science and Technology
• /
• 제36권2호
• /
• pp.56-62
• /
• 2008

The surface and edge structure of OSB is defined by surface strand orientation and strand mat thickness variation parallel to the length of the panel using video-microscope. The bending strength of OSB was correlated with surface strand orientation and decreased with increasing the orientation angle in the direction parallel to length of the panel. Average strand mat thickness variation parallel to the length of the panel did not influence the bending strength, but the bonding characteristics among the outermost strands affects the bending strength of OSB. Hankinson formula can be used to predicts the MOE according to strand orientation in the surface of OSB, and more precise strand alignment and reducing thickness variation should be important in the structural performance of OSB panels.

• 한국항만경제학회지
• /
• 제32권4호
• /
• pp.57-71
• /
• 2016

삼면이 바다로 둘러싸인 한국의 경우 해양산업의 육성은 필연적인 당면 과제이다. 그러나 해양산업의 경우 육상과 비교해 가혹한 물리적 조건하에서 이뤄지기 때문에 시간과 비용 측면에서 경쟁력을 확보하기 위한 다양한 노력들이 요구된다. 이러한 노력 중 하나로 해양보급기지(Offshore Supply Base, OSB)의 운영을 들 수 있다. 이러한 이유로 인해 한국에서 OSB 운영 및 구축에 관한 중요성이 주목받기 시작하였다. 그럼에도 불구하고 관련 국내 연구는 거의 없는 상태로 이를 언급한 문헌으로는 국내 연구기관에서 발표한 보고서가 전부이다. 이들 보고서는 직접적인 OSB에 대한 연구라기보다는 OSB와 관련된 산업인 해양플랜트산업의 육성방안 중 하나로 OSB 구축 및 운영에 대한 필요성만을 언급하였다. 반면 이 연구는 OSB을 중심으로 한국 실정에 맞는 OSB 구축에 대한 다양한 논의를 수행한다는 점에서 차별성을 지니고 있으며 이를 바탕으로 정책적 제언을 수행하였다. 이를 위해 대표적인 해외 OSB 구축 지역인 휴스턴과 싱가포르의 문헌조사를 통해 국내 OSB 구축 여건을 분석하였다. 그리고 OSB의 주요 기능 중 국내 OSB 구축시 우선적으로 요구되는 기능과 관련 문제점을 도출하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제35권5호
• /
• pp.46-57
• /
• 2007

The leachability of boron in zinc borate (ZB)-modified oriented strandboard (OSB) from southern wood species was investigated in this study. The leaching experiments were conducted by exposing edge-sealed OSB samples under running water at $31^{\circ}C$ for 8, 24, 72, and 216 h. The results from leached samples were compared with those from the unleached controls. Boron leaching of the modified OSB occurred upon the initial water exposure, and the leaching rate decreased as the leaching time increased. Initial boric acid equivalent (BAE) level, wood species, and sample thickness swelling significantly influenced the leachability. There was no consistent effect of polyethylene glycol (PEG) on zinc borate leaching. The glue-line washing within OSB due to thickness swelling of the test samples under water and decomposition of the borate to form water-soluble boric acid were thought to be two possible causes for the observed leaching. The relationship between assayed BAE and leaching time followed a decaying exponential function for zinc borate treated OSB. From the boron/zinc ratio after each leaching period, boron element in ZB was more or less leachable. The material constant of the regression models allowed comparing the leachability of the modified OSB for various wood species. An unified leaching method for treated wood composite materials is needed.

• 한국가구학회지
• /
• 제10권2호
• /
• pp.1-8
• /
• 1999

The use of structural wood based panels like plywood, OSB in many applications involves the use of nails, and data on the performance of panel-nail connection are needed for design and comparative purpose. This study was carried out to develop basic information on nail performance(withdrawal, embedding, nailhead push through) with water absorption in plywood and OSB. In withdrawal resistance test, initial stiffness of plywood performed better than OSB in 24hr soaked condition. The soaked condition reduced average nail withdrawal resistance value about 46% (12d mail), 53%(8d nail) in OSB, 17%(12d mail), 24%(8d mail) in plywood. The nail embedding strength of plywood also performed better than that of OSB and retention value(wet strength/dry strength) yielded similar in each nail types. The nail head push through capacity of OSB was higher than that of plywood in dry condition, but equal or lower in soaked condition. Therefore, critical consideration about structural panels is required in moist applications. The average values of nail withdrawal, nail embedding strength and nail head push through resistance of tested materials meet the minimum requirement of various specification and standards.

• Journal of the Korean Wood Science and Technology
• /
• 제37권2호
• /
• pp.121-127
• /
• 2009

Acacia wood (Acacia mangium Willd.) is the most popular fast growing tree species planted in timber estate in Indonesia and is considered to be very valuable raw materials for structural composite products. The objective of the research was to evaluate the properties of OSB prepared from A. Mangium wood with or without immersing the strands to hot water at $80^{\circ}C$ for 2 hours. MDI adhesive was used in 3 levels i.e., 3%, 5%, and 7%. The moisture content of strand was 7%. The results indicated that immersing strands in hot water for 2 hours at $80^{\circ}C$ prior to manufacture OSB improved significantly the mechanical peoperties (i.e., MOR and MOE) of OSB. The higher the adhesive content resulted in the better the dimensional stabilisation (i.e., water absorption and thickness swelling) and the mechanical properties (i.e., MOR, MOE and IB) of OSB. OSB prepared from hot-water immersed strands with 5% adhesive content has met all parameters requirement on the JIS A 5908 (2003) standard.

• 한국화재소방학회논문지
• /
• 제30권6호
• /
• pp.57-63
• /
• 2016

본 연구에서는 목재 기반 소재(MDF, OSB)의 연소생성물의 독성을 동물실험 기법을 사용하여 분석하였다. 실험용 쥐의 평균행동정지시간은 MDF가 OSB에 비해 짧았다. 이는 MDF 연소생성물의 독성이 OBS보다 높음을 의미한다. 해당 결과의 요인을 정량적으로 분석하기 위해 FT-IR을 통한 가스상 물질 분석을 수행하였다. 정성분석 결과 CO와 $CO_2$가 발생됨을 확인하였으며, 정량분석 결과 가스발생량은 OSB가 MDF보다 높음을 확인하였다. 또한 실험 후 실험용 쥐의 혈액분석 결과 OSB가 MDF에 비해 COHb 농도가 높음으로써, 가스상 물질의 발생량과 COHb 농도가 상관성이 있음을 확인하였다. 현재 재료의 연소생성물 독성 분석은 독성지수 Fractional Effective Dose (FED)를 통해 이루어지고 있다. FED는 독성가스 발생량을 기반으로 하고 있으며, 노출 물질의 독성이 높을수록 평균행동정지시간은 짧아진다. 하지만 본 연구 결과에서는 OSB가 MDF에 비하여 CO 발생량은 186.5%, COHb는 > 129.6% 임에도 불구하고 평균행동 정지시간이 51초가량 길게 나타남을 확인함으로써, 연소생성물 중 가스상 물질 이외의 추가적인 독성 요인에 대한 연구가 요구됨을 확인하였다.

• 한국작물학회:학술대회논문집
• /
• 한국작물학회 2017년도 9th Asian Crop Science Association conference
• /
• pp.160-160
• /
• 2017

Drought stress is a major constraint of crop development and productivity. Plants have evolutionally developed several mechanisms at the molecular, cellular, and physiological levels to overcome drought stress. The basic Leucine zipper (bZIP) transcription factor (TF) family members are starting to be concerned about their roles in drought stress responses. In this study, we functionally characterized OsbZIP66, a rice group-E bZIP TF, to be associated with rice drought tolerance mechanisms. Expression of OsbZIP66 was significantly induced upon treatments of rice plants with drought, high salinity, and ABA. These observations and the fact that the OsbZIP66 promoter contains ten ABA-responsive elements suggest that OsbZIP66 is up-regulated by drought stress in an ABA-dependent manner. Overexpression of both OsbZIP66 in a whole plant body and specifically in roots enhanced drought tolerance of rice plants, indicating that the rice drought tolerance positively correlates with the expression levels of OsbZIP66. Thus, our results demonstrated that OsbZIP66 has a potential for use in biotechnological development of high-yielding rice plants under drought conditions.