• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.2
• /
• pp.134-140
• /
• 2019

Oxide ($SnO_2$)/metal alloy (Cu(Ni))/oxide ($SnO_2$) multilayer films were fabricated using the magnetron sputtering technique. The oxide and metal alloy were $SnO_2$ and Ni-doped Cu, respectively. The structural, optical, and electrical properties of the multilayer films were investigated using X-ray diffraction (XRD), ultraviolet-visible (UV-vis) spectrophotometry, and 4-point probe measurements, respectively. The properties of the $SnO_2/Cu(Ni)/SnO_2$ multilayer films were dependent on the thickness and Ni doping of the mid-layer film. Since Ni atoms inhibit the diffusion and aggregation of Cu atoms, the grain growth of Cu is delayed upon Ni addition. For $250^{\circ}C$, the Haccke's figure of merit (FOM) of the $SnO_2$ (30 nm)/Cu(Ni) (8 nm)/$SnO_2$ (30 nm) multilayer film was evaluated to be $0.17{\times}10^{-3}{\Omega}^{-1}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.1
• /
• pp.25-30
• /
• 2020

Oxide (SiO₂)/Metal(Ag)/Oxide(SiO₂, ITO, ZnO) multilayer films were fabricated using a magnetron sputtering technique at room temperature on Si (p-type, 100) and a glass substrate. The electrical and optical properties of the asymmetric multilayer films depended on the thickness of the mid-layer film and the type of oxide in the bottom layer. As the metal layer becomes thicker, the sheet resistance decreases. However, the transmittance decreases when the metal layer exceeds a threshold thickness of approximately 10~12 nm. In addition, the sheet resistance and transmittance change according to the type of oxide in the bottom layer. If the oxide has a large resistivity, the overall sheet resistance increases. In addition, the anti-reflection effect changes according to the refractive index of the oxide material. The optical and electrical properties of multilayer films were investigated using an ultraviolet visible (UV-Vis) spectrophotometer and a 4-point probe, respectively. The optimum structure is SiO₂ (30 nm)/Ag (10 nm)/ZnO (30 nm) multilayer, with the highest FOM value of 7.7×10^-3 Ω^-1.