• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.1
• /
• pp.59-66
• /
• 2000

To investigate the optimum brazing condition, variation of bonded structure and mechanical properties of novel brazed pure Al with bonding condition (brazing temperature, time and Si/flux ratio) was studied. A basic study of the bonding mechanism was also examined. The optimum brazing condition was obtained at $590^{\circ}$ for 2 minutes and the bonded structure showed that it is composed of almost entirely eutectic Al-Si with near eutectic composition. At higher brazing temperature $630^{\circ}$, hypoeutectic Al-Si structure was observed in the bonded area and resulted in erosion of base metal. The thickness of eutectic layer formed in optimum brazing temperature increased linearly with the square root of time, showing a general diffusion controlled process. The ultimate tensile strength of bonded joint brazed at an optimum brazing condition was about 60% of base metal and its fracture surface showed a brittle mode.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.545-550
• /
• 2002

In order to ensure the signal could be transported cocrrectly, the microwave devices made of Aluminmn alloys must be assembled and brazed flaw-freely. In this paper, a new approach of using contact reactive brazing (CRB) process to realize the compact brazing of Aluminum alloys was put forward. The reason for this is that CRB, which realizes bonding depending on the liquid alloy produced by metallurgy reaction between the materials to be joined, overcomes the limitation of traditional brazing that the macroscopically disorganized filling flow of liquid filler metal would result in defects in brazed seam. Joint ofLF21 (AA3003) with the compactness of over 95% was brazed by the method of CRB using Si powder as an interlayer. At last, the influence of the physical parameter related to the Si powder interlayer on the compactness of the joints was investigated in detail.