• Journal of the korean Society of Automotive Engineers
• /
• v.11 no.1
• /
• pp.51-56
• /
• 1989

This study was performed to investigate the effect of defect on fatigue strength under the stress of rotary bending. The specimens were made of low carbon steel having artificial microholes, namely, single micro-hole and two adjacent micro-holes as natural defects, and the effects of the diameter of hole and the distance between the holes on fatigue strength have been investigated. The obtained result can be summarized as follows: 1, The critical defect means the largest size of defect that does not affect fatigue limit, and correspondes to the size of defect leading to final fracture under fatigue limit of smooth specimen. The size of defect which has an effect on fatigue limit is larger than that of critical defect. 2, The defect larger than the critical defect affects fatigue strength for as a kind of size effect, and the physical meaning of size effect of defect is considered same as the one of notch effect.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.8
• /
• pp.693-701
• /
• 2016

In this study, notch defects are evaluated using fracture mechanics. To understand the effects of notch defects, FE analysis is conducted to predict the limit load and J-integral for middle-cracked and single-edge cracked plates with various sizes of notch under tension and bending. As the radius of the notch increases, the energy release rate also increases, although the limit load remains constant. The values of fracture toughness($J_{IC}$) of SM490A are determined for various notch radii through FE simulation instead of conducting an experiment. As the radius of the notch increases, the energy release rate also increases, together with a more significant increase in fracture toughness. To conclude, as the notch radius increases, the resistance to crack propagation also increases.

• Proceedings of the KOR-BRONCHOESO Conference
• /
• 1981.05a
• /
• pp.39.3-40
• /
• 1981

Concerning the pathogenesis of acquired cholesteatoma in attic, there has been postulated theories by immigration from the Shrapnell's portion of the tympanic membrane, posterosuperior quardrant of the deep meatal skin and invagination of the margin of the central perforation. Otherwise, squamous metaplasia of the epithelium lining the middle ear cleft has been supported as a possible cause of cholesteatoma. Clinically, there has been known of the facts that cholesteatoma is formed in the attic but the pathogenesis concerning the acquired cholesteatoma is not still exactly reported. Recently, authors analyzed 170 cases of cholesteatomatous middle ear performed the operation to the middle ear cleft. On the operation finding, when the primary focus of the cholesteatoma was in the attic, we observed two types of perforation, marginal and central perforation in the Shrapnell's portion, and retraction to the Prussak's space, bony defect on the Rivinus notch. Among 36 cases of the cholesteatoma, the perforation of the Shrapnell's portion are 5 cases. Bony defect on the Rivinus notch and marginal perforation on the posterosuperior quadrant of the Shrapnell's portion are 21 cases. Among these cases, 3 cases are combined with central perforation of the Shrapnell's portion. Conclusively, the reasons that cholesteatoma is favorable site in the attic: 1) Excretion of the inflammatory discharge in the attic is difficult because of the distance of the E-tube. 2) The Shrapnell's portion has less collagen fiber than the pars tensa and it is thin because the elastic fibers are rich in it. It is easy to retract within the Prussak's space to the cases of keratinizing hyperplasia. 3) The epidermis attached at the Rivinus notch of the superior portion on the Shrapnell's portion is invaginated through the destructed bony wall of the Rivinus notch and the margin of the tympanic membrane in the response to the keratinizing hyperplasia.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.3 s.258
• /
• pp.344-354
• /
• 2007

The objective of this study is to investigate the effect of arbitrarily located defect around the circular hole in the aircraft structural material such as Al/GFRP laminates and monolithic Al alloy sheet under cyclic bending moment. The fatigue behavior of these materials may be different due to the defect location. Material flaws in the from of pre-existing defects can severely affect the fatigue crack initiation and propagation behavior. The aim of this study is to evaluate effects of relative location of defects around the circular hole in monolithic Al alloy and Al/GFRP laminates under cyclic bending moment. The fatigue behavior i.e., the stress concentration factor($K_t$), the crack initiation life($N_i$), the relationship between crack length(a) and cycles(N), the relationship between crack growth rate(da/dN) and stress intensity factor range(${\Dalta}K$) near a circular hole are considered. Especially, the defects location at ${\theta}_1=0^{\circ}\;and\;{\theta}_2=30^{\circ}$ was strongly effective in stress concentration factor($K_t$) and crack initiation life($N_i$). The test results indicated the features of different fatigue crack propagation behavior and the different growing delamination shape according to each location of defect around the circular hole in Al/GFRP laminates.

• Structural Engineering and Mechanics
• /
• v.32 no.5
• /
• pp.609-620
• /
• 2009

In this paper the results of a series of experimental tests upon three-point bending specimens made of polystyrene and containing re-entrant corners are firstly described. Tests involved different notch angles, different notch depths and finally different sizes of the samples. All the specimens broke at the defect, as expected because of the material brittleness and, hence, the generalized stress intensity factor was expected to be the governing failure parameter. Recorded failure loads are then compared with the predictions provided by a fracture criterion recently introduced in the framework of Finite Fracture Mechanics: fracture is assumed to propagate by finite steps, whose length is determined by the contemporaneous fulfilment of energy balance and stress requirements. This fracture criterion allows us to achieve the expression of the generalized fracture toughness as a function of the tensile strength, the fracture toughness and the notch opening angle. Comparison between theoretical predictions and experimental data turns out to be more than satisfactory.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.929-933
• /
• 2003

Internal defects of thin pressure vessel used in the power plants or the chemical plants may be created and grow due to corrosion or creep fatigue to reduce the strength and cause critical failure during operation. Therefore it is very important to detect this defect at the early stage. For this purpose, non-destructive, non-contact and highly sensitive method should be considered for on-line application. In this paper, a laser shearographic interferometer is applied to inspect circular defects and notch defects existed inside of thin pressure vessel under the presence of pressure up to 3 times of atmospheric pressure. The influences of the defect shape and size as well as the internal pressure to the characteristic pattern in the shearography fringe are investigated, and the quantitative evaluation of the defect size is tried. Also the experimental results are compared with the destructive test results to show the applicability of this method to the quantitative evaluation of internal defects in the thin pressure vessel.

• Journal of Power System Engineering
• /
• v.14 no.3
• /
• pp.46-51
• /
• 2010

A torsional guided wave was applied to detect a defect in petrochemical pipes. Phase and group velocity dispersion curves for the longitudinal and torsional modes of the inspected pipe were presented for the theoretical analysis. It was found through mode shape analysis that there was mode conversion when torsional wave is incident at an asymmetric defect. An artificial notch was fabricated in the pipe and the detectability was examined from the distance 2m of the end of the pipe by using magnetostrictive sensors. The relativities between the amplitude of the reflected signal and the size of the defect was examined. It was shown that the T(0,1) mode could be used for the long range inspection for the petrochemical pipes.

• Journal of Periodontal and Implant Science
• /
• v.29 no.3
• /
• pp.507-519
• /
• 1999

The ultimate objective of periodontal treatment is to stop disease progression and to regenerate destroyed periodontal tissues and thereby regain normal function. Growth factors are naturally found polypetides which stimulate many cellular activities pertaining to wound healing by acting as signal molecule in controlling cell movement, proliferation, and matrix production. Platelet derived growth factor (PDGF) is 28,000-35,000 Da molecular weight dimeric protein with 2 long positively charged polypeptide chains connected by sulfide bonds. The purpose of this study is to evaluate histologically the initial guided tissue regeneration in a periodontal defect f a beagle dog treated with a biodegradable membrane formed with polylactic acid (poly-L-lactic acid) and polyglycolic acid loaded with 200ng/$cm^2$ platelet derived growth factor. 2 beagle dogs were used in he experiment. $5mm{\times}6mm$ alveolar bone defect was formed in upper and lower canines and third premolars and a reference notch was placed. PDGF-BB non-containing membrane was used as control. Each defect was randomly assigned to the test roup or the control group. The dogs were sacrificed 3 weeks after membrane placement. Toluidine blue and multiple staining was done for histological analysis. In the 3 week specimen in the control group, no new one formation could be seen. Small amount f bone resorption below the notch could be seen. In the notch, loose connective tissue with infiltration of inflammatory cells could be seen. Also thin discontinuous new cementum could be seen and the membrane still retained its structure. Where PDGF-BB containing membrane was used, new bone formation could be seen in the notch at weeks and also continuous thin cementum could be seen. PDL cells were observed between new bone and new cementum and some were attached to bone and cementum. These results suggest that new bone and cementum formation seen when PDGF-BB loaded membrane was used was due to inhibition of downgrowth of epithelial cells and also due to continuous release of the growth factor. Further study on the resorption characteristics of the membrane nd the release characteristics of the PDGF-BB is necessary. Also, development of a membrane easier to use clinically is necessary.

• The korean journal of orthodontics
• /
• v.28 no.3 s.68
• /
• pp.431-440
• /
• 1998

While periodontal disease results in the extrusion of upper incisors with interdental spacing in adult patient, the intrusive movement should be executed for the rehabilitation in terms of esthetics and function. The present study was peformed to investigate the periodontal response following orthodontic intrusion of teeth with infrabony pocket. Bone defect and periodontal disease were produced adjacent to the both maxillary second lateral incisors in four adult dogs. Four weeks later, a flap operation was performed to eliminate inflammation and a reference notch was made on the root surface at the level of bottom of each defect. Two weeks after periodontal surgery, 4 weeks of intrusion and subsequent another 4 weeks of retention was executed on the right side of incisors while left incisors served as the control. Through the histologic analysis, following results were obtained. 1. Histologic section of control side showed the reduction of pocket depth after flap operation. However, the status of long junctional epithelium was observed while new connective tissue attachment occurred in a small area adjacent newly formed cementum 2. Epithelial attachment was less around the intruded incisor while new connective tissue attachment was much more compared to the control side. 3. Plenty of cells were observed in the connective tissue around the reference notch of the intruded incisor and the degree of the new cementum formation was higher in the intruded incisor than the control. The results of the present study suggested that an orthodontic intrusion of periodontally involved and extruded incisors could be carried out with a desirable periodontal response, provided that inflammation is under control.

• Journal of the Korean Institute of Gas
• /
• v.8 no.3 s.24
• /
• pp.1-7
• /
• 2004

The polyethylene pipe can use semi-permanent because of the high corrosion resistance with chemical stability. In addition to, there is the merit that is an easy to establish and to maintain. However, as the reason that it is simply degraded when the polyethylene pipe was exposed to the outside, mainly it is used to lay under the ground with low-pressure gas transportation pipe. In this study, the nondestructive evaluation method was used to maintain the integrity of the polyethylene pipe. We simulated the various defects on the polyethylene pipes, and then the AE signal occurred according to the impact test of steel ball was evaluated by the acoustic emission method. From the results, the waveform and dominant frequency could be distinguishing from the defect shapes of polyethylene pipe. Especially, in the case of notch defect, the AE signals occur different by the angle and depth of the notch.