Microcracks can rapidly grow and develop in high-strength steels used in offshore structures. It is important to render these microcracks harmless to ensure the safety and reliability of offshore structures. Here, the dependence of the aspect ratio (As) of the maximum depth of harmless crack (a_hlm) was evaluated under three different conditions considering the threshold stress intensity factor (Δk_th) and residual stress of offshore structural steel F690. The threshold stress intensity factor and fatigue limit of fatigue crack propagation, dependent on crack dimensions, were evaluated using Ando's equation, which considers the plastic behavior of fatigue and the stress ratio. a_hlm by peening was analyzed using the relationship between Δk_th obtained by Ando's equation and Δk_th obtained by the sum of applied stress and residual stress. The plate specimen had a width 2W = 12 mm and thickness t = 20 mm, and four value of As were considered: 1.0, 0.6, 0.3, and 0.1. The a_hlm was larger as the compressive residual stress distribution increased. Additionally, an increase in the values of As and Δk_th(l) led to a larger a_hlm. With a safety factor (N) of 2.0, the long-term safety and reliability of structures constructed using F690 can be secured with needle peening. It is necessary to apply a more sensitive non-destructive inspection technique as a non-destructive inspection method for crack detection could not be used to observe fatigue cracks that reduced the fatigue limit of smooth specimens by 50% in the three types of residual stresses considered. The usefulness of non-destructive inspection and non-damaging techniques was reviewed based on the relationship between a_hlm, a_NDI (minimum crack depth detectable in non-destructive inspection), a_{cr N} (crack depth that reduces the fatigue limit to 1/N), and As.

• Journal of the Korean Society of Industry Convergence
• /
• v.25 no.5
• /
• pp.791-797
• /
• 2022

Using the fatigue limit (△σ_unsm) and residual stress (σ_r) of the UNSM smooth specimen, the harmless maximum crack depth (α_hml) according to the crack aspect ratio (As) was evaluated. α_hml evaluated the reliability in the relationship between the minimum crack depth (α_NDI1, α_NDI2) detectable by nondestructive inspection(NDI) and the crack depth (α₂₅, α₅₀) that reduces the fatigue limit by 25% and 50%. All α_hml was determined by the crack depth. The α_hml of 80N UNSM with high σ_r and high △σ_unsm was found to be large. σ_r in the depth direction had a much effect on α_hml. Since α_hml>α₅₀(As=0.6-0.1) and α_hml>α₂₅, α₂₅ and α₅₀(some range) can secure the safety and reliability. Since α_hml<α₅₀ (As=1. 0-0. 6), it cannot be made harmless by UNSM. So safety and reliability cannot be secured. α_NDI1 and α_NDI2 are larger than α₂₅, α₂₅ cannot be detected by NDI. α_NDI1 and α_NDI2 are smaller than α₅₀, α₂₅ can detected by NDI.