• Journal of the Korean Electrochemical Society
• /
• v.3 no.1
• /
• pp.49-56
• /
• 2000

In the present we.k, temperature dependence of oxygen diffusivity in the polyvinyl chloride (PVC) film $D_f$ formed on gold electrode was investigated using steady-state rotating disk electrode (RDE) technique and modulated electrohydrodynamic (EHD) impedance technique. Both the diffusion rate defined as the ratio of oxygen diffusivity in the PVC film to the film thickness $D_f/\delta_f$ and the time constant $\delta_f^2/D_f$ for oxygen diffusion through the PVC film were obtained from plot of the limiting current versus disk rotation speed and from filing the EHD impedance spectra experimentally measured to those theoretically calculated on the basis of the diffusion equation for mass transport through the non-conductive and porous film, respectively. By combining measured $D_f/\delta_f$ with $\delta_f^2/D_f$, we determined $\delta_f\;and\;D_f$ at room temperature separately. As temperature increased, it appeared that the $D_f$ value measured for the PVC film-covered gold RDE was enhanced more rapidly than that $D_s$ value in the solution measured for the PVC film-free gold RDE. This means that the pores glowing with increasing temperature act as effective diffusion paths within the film. The present in-situ steady-state and modulated EHD measurements prove to be effective for determining $\delta_f\;and\;D_f$, separately and at the same time the porosity of the PVC film at temperatures below glass temperature $T_g$ of the film.

• Membrane Journal
• /
• v.27 no.4
• /
• pp.344-349
• /
• 2017

Alkaline fuel cells using polymer electrolyte membranes are expected to replace proton exchange membrane fuel cells, which have similar system configurations. In particular, in alkaline fuel cells, a low-cost non-platinium catalyst can be used. In this study, to fabricate high performance and high durability anion exchange membranes for alkaline fuel cell systems, two kinds of supports, polybenzoxazole and polyethylene supports, were impregnated with Fumion FAA ionomer, by which we tried to fabricate the support-impregnated membrane which has higher mechanical strength and higher ion conductivity than the Fumion series. Finally, the Pore-filling membranes were successfully fabricated and ionic conductivity and mechanical properties were different depending on the properties of the supports. In the pore-filling membranes with Fumion ionomer on the PE support, excellent mechanical properties were obtained, but ionic conductivity decreased. On the other hand, when the PBO support was impregnated with Fumion ionomer, high ionic conductivity was shown after impregnation due to high basicity of PBO, but the mechanical strength was relatively low as compared with Fumion-PE membrane. As a result, it was concluded that it is necessary to consider the characteristics of the support according to the operating conditions of the alkaline fuel cell during the preparation of the pore-filling membranes.