• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.3
• /
• pp.88-94
• /
• 2006

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, the effect of shot peening in corrosion environment was not known. In this study, investigated is the effect of shot peening on corrosion fatigue crack growth of SAE 5155 steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of SAE 5155 are as follows; the fatigue crack growth rate of the shot peening material was lower than that of the non-peening material. And fatigue life shows more improvement in the shot peening material than in non-peening material. This is due to the compressive residual stress of surface increases resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Journal of Advanced Marine Engineering and Technology
• /
• v.33 no.4
• /
• pp.533-538
• /
• 2009

The magnitude of constraint effect $A_2$ values on the non-linear elastic plastic fracture toughness was experimentally estimated by using displacement at various measuring positions near crack tip. Constraint effect $A_2$ value was dependent on specimen configuration and on the measured displacement near crack front. The crack tip opening displacement in the vicinity of the crack tip front should be estimated within plastic region when appropriately constraint effect was calculated. It was found that the magnitude of constrain effect |$A_2$| is below 8.0 at the crack tip. But an appropriate location to measure the effective constraint effects $A_2$ at the critical value of J that crack initiation is characterizable by is r = 2mm and ${\theta}=90^{\circ}$ away from original crack tip, and the constraint effect |$A_2$| estimated is 5.3.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.6 no.1
• /
• pp.9-22
• /
• 1986

Acoustic Emission is not only expected as a non-destructive evaluation technique in practice but also noted as a new powerful means of evaluation of materials. AE occurs with plastic deformation and propagation of crack, and this patterns of occurence of AE vary with materials. AE which comes from propagation of crack depends oil the shapes and properties of materials. Like this AE has characteristic of material. The present work is an attempt to evaluate characteristics of carbon steel (SM55C) and Die steel(SKD11) by means of dynamic response of AE method.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.601-601
• /
• 1989

The behavior of fatigue was studied by using low carbon steel bar with microhole(artificial small defect) under the condition of rotary bending stress which is made artificially at smooth surface and round notch root. The results obtained can be summerized; The behavior of non-propagating cracks which are produced at both tips of small defect occurred to dissymmetry, and it is found to be double size of small defect. For the range of l>lc, threshold stress intensity is constant. However, for the range of l

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.101-107
• /
• 1989

The behavior of fatigue was studied by using low carbon steel bar with microhole(artificial small defect) under the condition of rotary bending stress which is made artificially at smooth surface and round notch root. The results obtained can be summerized; The behavior of non-propagating cracks which are produced at both tips of small defect occurred to dissymmetry, and it is found to be double size of small defect. For the range of l>lc, threshold stress intensity is constant. However, for the range of l

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.8
• /
• pp.1277-1286
• /
• 2001

Aluminum 5052/Aramid Fiber Reinforced Plastic(Al5052/AFRP) laminates are applied to the fuselage-wing intersection. The Al5052/AFRP laminates suffer from the cyclic bending moment of variable amplitude during the service. Therefore, the influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in Al5052/AFRP laminate was investigated in this study. Al5052/AFRP laminate composite consists of three thin sheets of Al5052 and two layers of unidirectional aramid fibers. The cyclic bending moment fatigue tests were performed with five different levels of bending moment. The shape and size of the delamination zone formed along the fatigue crack between Al5052 sheet and aramid fiber-adhesive layer were measured by an ultrasonic C-scan. The relationships between da/dN and ΔK, between the cyclic bending moment and the delamination zone size, and between the fiber bridging mechanism and the delamination zone were studied. Fiber failures were not observed in the delamination zone in this study. It represents that the fiber bridging modification factor should turn out to increase and that the fatigue crack growth rate should decrease. The shape of delamination zone turns out to be semi-elliptic with the contour decreased non-linearly toward the crack tip.

• Journal of the Korean Society of Safety
• /
• v.28 no.6
• /
• pp.57-63
• /
• 2013

This paper discusses 2D models of beams for simulating the fracture of brittle materials. A simulation of an experiment on a concrete beam subjected to bending, in which two overlapping cracks occur, is used to study the effect of individual beam characteristics and different arrangements of the beams in the overall network mesh. It was found that any regular orientation of the beams influences the resulting crack patterns. Methods to implement a wide range of poisson's ratios are also developed, the use of the mesh to study arbitrary micro-structures is outlined. The crack pattern that are obtained with mesh are in good agreement with the experimental results. Also, numerical simulations of the tests were performed by means of a model, and non-integer dimensions were measured on the predicted mesh damage patterns.

• Computers and Concrete
• /
• v.2 no.2
• /
• pp.165-176
• /
• 2005

This paper discusses 2D lattice models of beams for simulating the fracture of brittle materials. A simulation of an experiment on a concrete beam subjected to bending, in which two overlapping cracks occur, is used to study the effect of individual beam characteristics and different arrangements of the beams in the overall lattice. It was found that any regular orientation of the beams influences the resulting crack patterns. Methods to implement a wide range of Poisson's ratios are also developed, and the use of the lattice to study arbitrary micro-structures is outlined. The crack patterns that are obtained with lattice are in good agreement with the experimental results. Also, numerical simulations of the tests were performed by means of a lattice model, and non-integer dimensions were measured on the predicted lattice damage patterns.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.5
• /
• pp.34-41
• /
• 2001

More accurate and fast inspection method for mechanical parts and structure is required to guarantee the safety. Conventional methods using compliance method, eddy current method, ultrasonic wave, acoustic emission for non-destructive testing in mechanical parts and structure have been performed as the method of contact with objects to be inspected. With this reason these methods have been taken relatively much time, money, and manpower. In this study, in order to overcome these shortcomings, we used In-plane Electronic Speckle pattern Interferometry(In-plane ESPI) that was full-field measurement and noncontact method. We detected the cracks of the specimen at a real time and measured the length of the crack by using In-place ESPI system. Finally, we compared this results with conventional microscope method.

• Steel and Composite Structures
• /
• v.19 no.3
• /
• pp.601-614
• /
• 2015

The Metal Magnetic Memory (MMM) method is a non-destructive testing method based on an analysis of the self-magnetic leakage field distribution on the surface of a component. It is used for determining the stress concentration zones or any irregularities on the surface or inside the components fabricated from ferrous-based materials. Thus, this paper presents the MMM signal behaviour due to the application of fatigue loading. A series of MMM data measurements were performed to obtain the magnetic leakage signal characteristics at the elastic, pre-crack and crack propagation regions that might be caused by residual stresses when cyclic loadings were applied onto the A283 Grade C steel specimens. It was found that the MMM method was able to detect the defects that occurred in the specimens. In addition, a justification of the Self Magnetic Flux Leakage patterns is discussed for demonstrating the effectiveness of this method in assessing the A283 Grade C steel under cyclic loadings.