• Journal of Electrochemical Science and Technology
• /
• 제14권3호
• /
• pp.262-271
• /
• 2023

For electrode stability and the electrochemical performance of the Li-ion cell, it is essential that the active ingredients and unique additives in the polymer binder be well dispersed with the solvent-based slurry. The efficient procedure used to create the slurry affects the rheological characteristics of the electrode slurry. When successively adding different steps of Nmethyl-2-pyrrolidone (NMP) solvent to the cathode composition, it is evenly disseminated. The electrochemical performance of the Li-ion cells and the electrodes made with slurry formed by single step and multiple steps of addition of NMP solvent are examined. To preform rheological properties of cathode electrode slurry on Ni-rich Lithium Nickel-Cobalt-Aluminum Oxide (LiNi_0.80Co_0.15Al_0.05) (NCA). Also, we investigate different step addition of electrode formation and mechanical strength characterization like peel strength. According to the EIS study, a multi-step electrode slurry has lower internal resistance than a single-step electrode slurry, which results in better electrical characteristics and efficiency. Further, microstructure of electrodes is obtained electrochemical performance in the 18650 cylindrical cells with targeted capacity of 1.5 Ah. The slurry of electrodes prepared by single step and multiple steps of addition of NMP solvent and its effect on the fabrication of 1.5 Ah cells. A three-step solvent addition on slurry has been found to be a lower internal resistance than a single-step electrode slurry as confirmed by the EIS analysis, yielding improved electrical properties and efficiency.

• 전기화학회지
• /
• 제24권4호
• /
• pp.120-132
• /
• 2021

기존 LiCoO₂의 고전압 사용의 제약에 따른 용량적 한계와 코발트 원료의 높은 가격을 해결하기 위하여 high-Nickel에 대한 개발이 활발히 진행되고 있지만 Ni 함량의 증가에 따른 구조적 안정성의 저하에 의한 전지 특성의 저하는 상용화를 지연시키는 중요한 원인이 되고 있다. 이에 Ni-rich 삼성분계 양극소재 LiNi_0.6Co_0.2Mn_0.2O₂의 고안정성을 높이고자 전구체에 균일한 이종원소 Ti를 치환을 위해서 나노크기의 TiO₂ 서스펜젼 형태 소스를 사용하여 전구체 Ni_0.6Co_0.2Mn_0.2-x(OH)₂/xTiO₂를 제조하였다. Li₂CO₃와 혼합하고, 열처리 후 양극활물질 LiNi_0.6Co_0.2Mn_0.2-xTi_xO₂ 합성하여 Ti 함량에 따른 물리적 특성을 비교하였다. Field Emission Scanning electron Microscope(FE-SEM) 및 Energy Dispersive Spectroscopy (EDS) mapping 분석을 통해 Ti 치환된 구형의 전구체와 입자 크기 측정을 통해 균일한 입자크기를 가지는 양극 활물질 제조를 확인하였고, 내부치밀도와 강도가 증가함을 확인 하고, X-ray Diffractometry (XRD) 구조 분석과 Inductively Coupled Plasma Mass Spectrometry (ICP-MS) 정량분석을 통해 Ti 치환된 양극활물질 제조 및 고온, 고전압에서 충·방전을 지속하더라도 효과적으로 용량이 유지됨을 확인하였다.