• 한국세라믹학회지
• /
• 제34권10호
• /
• pp.1074-1082
• /
• 1997

Microstructure and permeability as a function of sintering temperature and composition were studied on the Ni$\delta$Cu0.4-$\delta$Zn0.6Fe2O4 ($\delta$=0, 0.1, 0.2, 0.3, 0.4) which was prepared by Cu2+ substitution for Ni2+ in Ni.0.4Zn0.6Fe2O4, then followed by 8 wt% CuO and 1wt% Bi2O3 as sintering aids. It was found that NiCuZn ferrite in which Cu2+ is substituted for Ni2+ is more effective in reduction of sintering temperature than Ni.0.4Zn0.6Fe2O4, containing CuO as a sintering aid. The specimen $\delta$=0.2 sintered at 90$0^{\circ}C$ for 2hr exhibited the highest initial permeability value ($\mu$o=280 at 1Mhz), but the real permeability decreased at the frequency under 10 MHz. EPMA analysis showed that Ni$\delta$Cu0.4-$\delta$Zn0.6Fe2O4 ($\delta$=0.4), sintered at 95$0^{\circ}C$ for 2hrs consisted of three phase regions of Ni.0.3Cu0.1Zn0.6Fe2O4 region, Cu and Bi liquid existed at the 3-point boundary, although the stabilization energy of Ni2+ is higher than that of Cu2+ in B site.

• 한국자기학회지
• /
• 제20권5호
• /
• pp.182-186
• /
• 2010

Cobalt가 치환된 NiZnCu ferrite의 소결 및 자기적 성질에 미치는 영향에 대해 연구 하였다. 칩인덕터용 $Ni_{0.36-x}Co_xZn_{0.44}Cu_{0.22}Fe_{1.98}O_4(0{\leq}x{\leq}0.04)$를 고상반응법으로 제조하였다. 소결조제를 사용하지 않고 $880{\sim}920^{\circ}C$에서 공기중 2시간 열처리 하였으며 초투자율, 품질계수 Q, 밀도, 수축율, 포화자화, 및 보자력을 측정하였다. Cobalt가 치환된 NiZnCu ferrite는 품질계수 Q를 증가시켰으며 칩인덕터용으로 사용 가능함을 알 수 있었다. 품질계수 Q는 치환량이 x = 0.01까지 증가한 후 x = 0.01 이후로 급격히 감소하였다. Cobalt의 치환량이 증가함에 따라 초투자율 및 밀도값은 감소하였다. $900^{\circ}C$에서 소성된 $Ni_{0.35}Co_{0.01}Zn_{0.44}Cu_{0.22}Fe_{1.98}O_4$ 토로이달 core 샘플의 경우 1 MHz에서 측정 시 초투자율값은 130이었고 품질계수 Q값은 230으로 나타났다.

• 한국자기학회지
• /
• 제17권6호
• /
• pp.238-241
• /
• 2007

복합 전파흡수체로 사용할 Ni-Cu-Zn ferrite는 공침법을 사용하여 제조 하였고,제조 시편의 물리적 특성 및 전파흡수특성은 소결온도 변화에 따라 고찰하였다. Ni-Cu-Zn ferrite의 스피넬 구조는 XRD pattern을 통하며 확인하였다. 소결온도가 $1100^{\circ}C$에서 흡수 능력도 좋아짐을 알 수 있었으며, 소결된 페라이트의 초투자율은 평균 50 정도로 나타났다. $Ni_{0.7}Cu_{0.2}Zn_{0.1}Fe_2O_4$ 조성에서 소결 온도가 $1100^{\circ}C$ 일 때가 복합 전파흡수체로 사용할 조성임을 확인할 수 있었으며, 그 결과 복합 전파흡수체에서 사용할 수 있다고 사료된다.

• 한국세라믹학회지
• /
• 제39권12호
• /
• pp.1119-1123
• /
• 2002

Nanostructured spinel NiZn ferrites were prepared by the sol-gel method from metal nitrate raw materials. Analyses by X-ray diffraction and scanning electron microscopy showed the average particle size of NiZn ferrite was under 50 nm. The single phase of NiZn ferrites was obtained by firing at 250${\circ}C$, resulting in nanoparticles exhibiting normal ferrimagnetic behavior. The nanostructured $Ni_{1-X}Zn_XFe_2O_4$ (x=0.0∼1.0) were found to have the cubic spinel structure of which the lattice constants ${\alpha}_2$ increases linearly from 8.339 to 8.427 ${\AA}$ with increasing Zn content x, following Vegard's law, approximately. The saturation magnetization $M_s$ was 48 emu/g for x=0.4 and decreased to 8.0 emu/g for higher Zn contents suggesting the typical ferrimagnetism in mixed spinel ferrites. Pure NiZn ferrite phase substituted by Cu was observed before using the additive but hematite phase was partially appeared at $Ni_{0.2}Zn_{0.2}Cu_{0.6}Fe_2O_4$. On the other hand, the hematite phase in this NiZn Cu ferrite was disappeared after using the additive of acethyl aceton with small amount. The saturation magnetization Ms of $Ni_{0.2}Zn_{0.8-y}Cu_yFe_2O_4$(y=0.2∼0.6) as measured was about 51 emu/g at 77K and 19 emu/g at room temperature, respectively.

• 한국자기학회지
• /
• 제15권5호
• /
• pp.282-286
• /
• 2005

공침법으로 제조한 Ni-Cu-Zn ferrite를 사용하여 전파흡수체로 사용할 저온소결용 ferrite를 연구하였다. Ni 첨가량에 따른 조성비 및 가소온도와 소결온도 변화를 시켜 전파흡수특성 및 물리적 특성을 고찰하였다. XRD pattern을 통하여 spinel구조를 가짐을 확인하였고, 공침법으로 제조된 Ni-Cu-Zn ferrite 미분말이 나노입자 크기를 보였다 소결온도가 $1100^{\circ}C$이고 Ni 함량이 많을 수록 투자율이 낮고 손실계수도 높게 측정되어 흡수 능력도 좋아짐을 알 수 있고, MHz 영역에서 사용할 수 있다고 사료된다. 그리고 소결온도 $1100^{\circ}C$이고 $(Ni_{0.7}Cu_{0.2}Zn_{0.1}O)_{1.02}(Fe_{2}O_3)_{0.98}$ 조성일 때가 가장 손실이 크므로 전파흡수체로 사용할 조성임을 확인 할 수 있었다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.548-551
• /
• 1995

The effect of Cu substitution on the properties of NiZn ferrites sintered at low temperature with composition is investigated. The densification of NiCuZn ferrite in dependent upon Cu content in the composition of (N/sub 0.5-x/Cu/sub x/ Zn/sub 0.5/O)(Fe/sub 2/O/sub 3/)/sub 0.98/. Electrical resistivity is maximum at x=0.2. Dispersion characteristics of complex permeability of (Ni/sub 0.5-x/ Cu/sub x/Zn/sub 0.5/O)(Fe/sub 2/O/sub 3)/sub 0.98/ is observed above x=0.3 and relaxation frequency increases with higher temperature. The magnetic loss of NiCuZn ferrite is occurred above the Cu content x=0.3 at a low frequency.

• 한국정보통신학회논문지
• /
• 제5권5호
• /
• pp.994-1000
• /
• 2001

정보통신기술의 발달과 전자기기의 사용량 증가에 따른 전자파장애의 발생이 점차 사회 문제화되면서 그 대책이 요구됨에 따라 전자파 흡수체에 대한 관심도 증가되고 있는데 본 연구에서는 전자파 흡수체로 알려진 NiCuZn 페라이트의 조성비 및 소결온도 변화에 따른 복소유전율과 복소투자율의 주파수 의존 특성을 알아보고 전자파 흡수성능에 대한 영향을 조사하였다. NiCuZn 페라이트의 조성 중 $Fe_2O_3$및 ZnO를 각각 49.0, 34.0mol%로 고정하고 NiO 및 CuO의 구성비를 변화시켜 측정한 결과 NiO의 구성비가 8.5~9.5 mol%의 범위에서, 소결온도는 $1080^{\circ}C$에서 초투자율 및 유전율이 크고 $loss tangent(=\mur"/\mur')$가 약 2 MHz~9.5 GHz 주파수 대역에서 1 이상을 보이며 전파흡수 성능이 가장 우수하게 나타났다.나타났다.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1992년도 춘계연구발표회 논문개요집
• /
• pp.48-49
• /
• 1992

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1994년도 춘계연구발표회 논문개요집
• /
• pp.46-47
• /
• 1994

• 한국자기학회지
• /
• 제17권6호
• /
• pp.232-237
• /
• 2007

기본조성 $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$에서 $Fe_2O_3$가 약간 부족한 비화학양론적인 조성비를 택하여 Ni-Zn-Cu 페라이트의 입계에 높은 저항층을 형성하고 소결을 촉진시켜 낮은 손실, 높은 투자율 및 자기유도 와 주성분을 치환해서 스피넬 격자를 고용시킬 목적으로 $TiO_2$ 및 $Li_2CO_3$를 소량 첨가하였다. 이들 원료들을 혼합한 후 가소 후 소결온도 $875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C$ 및 $950^{\circ}C$에서 소결하였다. 각 시편들에 대한 소결밀도는 $4.85\sim5.32g/cm^3$으로 나타났고, 각 시편들의 고유저항은 $10^8\sim10^{12}\Omega-cm$으로 측정되었다. 시편들의 자기유도 특성 값은 대략 $800\sim1300G$ 부근이었으며, $TiO_2$를 첨가한 경우보다 $Li_2CO_3$를 첨가한 경우가 약간 높게 측정되었다. 각각 시편들의 보자력은 $2.5\sim4.5$ Oe로 연자성 재료의 범위로 나타났다. 초투자율 및 품질계수는 각각 $125\sim275$ 및 $65\sim83$으로 나타나 Ni-Zn-Cu 페라미트에서 측정되는 값들과 대동소이했다. 물리적인 특성값(고유저항, 자기유도, 초투자율, 품질계수 등)으로 미루어 보마 각종 고주파영역(microwave영역까지 포함) 통신기기 코어 및 편향 요크 코어 등으로 응용이 가능하다.