• 한국자기학회지
• /
• 제5권5호
• /
• pp.548-551
• /
• 1995

The effect of Cu substitution on the properties of NiZn ferrites sintered at low temperature with composition is investigated. The densification of NiCuZn ferrite in dependent upon Cu content in the composition of (N/sub 0.5-x/Cu/sub x/ Zn/sub 0.5/O)(Fe/sub 2/O/sub 3/)/sub 0.98/. Electrical resistivity is maximum at x=0.2. Dispersion characteristics of complex permeability of (Ni/sub 0.5-x/ Cu/sub x/Zn/sub 0.5/O)(Fe/sub 2/O/sub 3)/sub 0.98/ is observed above x=0.3 and relaxation frequency increases with higher temperature. The magnetic loss of NiCuZn ferrite is occurred above the Cu content x=0.3 at a low frequency.

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1162-1166
• /
• 2001

석유화학 공정 중 Styrene(SM) 공정에서 발생되는 산화철 폐촉매는 산업 폐기물로서 전량 매립되고 있는데, 이를 출발 원료로 사용하여 NiZn-페라이트를 합성하였고 그 자기적 특성을 조사하였다. 산화철 폐축매 펠렛을 분쇄한 후 NiO 및 ZnO를 혼합하여 90$0^{\circ}C$에서 하소하고 123$0^{\circ}C$에서 5시간 소결하여 스핀넬형 페라이트 소결체를 얻었다. N $i_{x}$ Z $n_{1-x}$F $e_2$ $O_4$(x=0.36, 0.50, 0.66)조성에 대하여 초투자율을 측정하였고, S-parameter를 측정하여 반사 감쇄량을 계산하였다. 산화철 폐촉매를 이용하여 X-band 주파수 영역에서 높은 전자파 흡수능을 갖는 전파흡수체를 제조할 수 있음을 확인하였다.다.

• 한국정보통신학회논문지
• /
• 제5권5호
• /
• pp.994-1000
• /
• 2001

정보통신기술의 발달과 전자기기의 사용량 증가에 따른 전자파장애의 발생이 점차 사회 문제화되면서 그 대책이 요구됨에 따라 전자파 흡수체에 대한 관심도 증가되고 있는데 본 연구에서는 전자파 흡수체로 알려진 NiCuZn 페라이트의 조성비 및 소결온도 변화에 따른 복소유전율과 복소투자율의 주파수 의존 특성을 알아보고 전자파 흡수성능에 대한 영향을 조사하였다. NiCuZn 페라이트의 조성 중 $Fe_2O_3$및 ZnO를 각각 49.0, 34.0mol%로 고정하고 NiO 및 CuO의 구성비를 변화시켜 측정한 결과 NiO의 구성비가 8.5~9.5 mol%의 범위에서, 소결온도는 $1080^{\circ}C$에서 초투자율 및 유전율이 크고 $loss tangent(=\mur"/\mur')$가 약 2 MHz~9.5 GHz 주파수 대역에서 1 이상을 보이며 전파흡수 성능이 가장 우수하게 나타났다.나타났다.

• 한국세라믹학회지
• /
• 제50권3호
• /
• pp.231-237
• /
• 2013

Thermodynamic modeling of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite system has been adopted as a rational approach to establish routes to better synthesis conditions for pure phase $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ complex ferrite. Quantitative analysis of the different reaction equilibria involved in the precipitation of $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ from aqueous solutions has been used to determine the optimum synthesis conditions. The spinel ferrites, such as magnetite and substitutes for magnetite, with the general formula $MFe_2O_4$, where M= $Fe^{2+}$, $Co^{2+}$, and $Ni^{2+}$ are prepared by coprecipitation of $Fe^{3+}$ and $M^{2+}$ ions with a stoichiometry of $M^{2+}/Fe^{3+}$= 0.5. The average particle size of the as synthesized $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$, measured by transmission electron microscopy (TEM), is 14.2 nm, with a standard deviation of 3.5 nm the size when calculated using X-ray diffraction (XRD) is 16 nm. When $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite is annealed at elevated temperature, larger grains are formed by the necking and mass transport between the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ ferrite nanoparticles. Thus, the grain sizes of the $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ gradually increase as heat treatment temperature increases. Based on the results of Thermogravimetric Analysis (TGA) and Differential Scanning Calorimeter (DSC) analysis, it is found that the hydroxyl groups on the surface of the as synthesized ferrite nanoparticles finally decompose to $Ni_{0.5}Zn_{0.4}Cu_{0.1}Fe_2O_4$ crystal with heat treatment. The results of XRD and TEM confirmed the nanoscale dimensions and spinel structure of the samples.

• 한국자기학회지
• /
• 제17권6호
• /
• pp.232-237
• /
• 2007

기본조성 $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$에서 $Fe_2O_3$가 약간 부족한 비화학양론적인 조성비를 택하여 Ni-Zn-Cu 페라이트의 입계에 높은 저항층을 형성하고 소결을 촉진시켜 낮은 손실, 높은 투자율 및 자기유도 와 주성분을 치환해서 스피넬 격자를 고용시킬 목적으로 $TiO_2$ 및 $Li_2CO_3$를 소량 첨가하였다. 이들 원료들을 혼합한 후 가소 후 소결온도 $875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C$ 및 $950^{\circ}C$에서 소결하였다. 각 시편들에 대한 소결밀도는 $4.85\sim5.32g/cm^3$으로 나타났고, 각 시편들의 고유저항은 $10^8\sim10^{12}\Omega-cm$으로 측정되었다. 시편들의 자기유도 특성 값은 대략 $800\sim1300G$ 부근이었으며, $TiO_2$를 첨가한 경우보다 $Li_2CO_3$를 첨가한 경우가 약간 높게 측정되었다. 각각 시편들의 보자력은 $2.5\sim4.5$ Oe로 연자성 재료의 범위로 나타났다. 초투자율 및 품질계수는 각각 $125\sim275$ 및 $65\sim83$으로 나타나 Ni-Zn-Cu 페라미트에서 측정되는 값들과 대동소이했다. 물리적인 특성값(고유저항, 자기유도, 초투자율, 품질계수 등)으로 미루어 보마 각종 고주파영역(microwave영역까지 포함) 통신기기 코어 및 편향 요크 코어 등으로 응용이 가능하다.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.383-390
• /
• 1992

We investigated the effect of substrate on the properties of the Ni-Zn-Cu ferrite thin films deposited on SiO2 (1000∼3000${\AA}$) / Si (100) substrate at various conditions by rf magnetron sputtering. A disktype Ni-Zn-Cu ferrite sintered by conventional ceramic process and argon gas were used as a target and a sputtering gas, repectively. The compositions of the thin films measured by EPMA were similar to target composition (Fe: 65.8 at%, Ni: 12.7 at%, Cu: 6.7 at%, Zn: 14.8 at%) irrespective of substrate temperature. Amorphous thin films were deposited when substrate was not intentionally heated, but the films came to crystallize with increasing substrate temperature, and crystalline thin films were deposited at substrate temperature above 200$^{\circ}C$. Below 250$^{\circ}C$ saturation magnetization (Ms), remanence (Mr) and coercivity (Hc) of the ferrite thin film increased with the substrate temperature due to the increase of grain size and the improvement of crystallinity. And above 250$^{\circ}C$, Ms, Mr increased slightly, but Hc of the amorphous thin films increased due to crystallization, whereas that of the crystalline thin films decreased because of grain growth and stress release.

• 한국전기전자재료학회논문지
• /
• 제20권10호
• /
• pp.873-877
• /
• 2007

In order to apply a complex multilayer chip LC filter, this study has estimated the interfacial reaction and coupling properties of dielectric materials $Pb(Fe_{1/2}Nb_{1/2})O_3$ and Ni-Zn-Cu ferrite materials through low-temperature co-sintering (LTCS). PFN powders were fabricated using double calcinated at $700^{\circ}C$ and then $850^{\circ}C$. While the perovskite phase rate was found to be 91 %, after heat treatment at $900^{\circ}C$ for 6h, the perovskite phase rate and density exhibited a value of 100 % and 7.46$g/cm^3$, respectively. The PFN/Ni-Zn-Cu ferrite, PFN/CUO (or $Pb_2Fe_2O_5$) and ferrite/CuO (or $Pb_2Fe_2O_5$) were mechanically coupled through interfacial reactions after the specimen was co-sintered at $900^{\circ}C$ for 6 h. No intermediate layer exists for the mutual coupling reaction. This result indicates the possibility of low-temperature co-sintering without any interfacial reaction layer for a multilayer chip LC filter.

• 한국자기학회지
• /
• 제15권3호
• /
• pp.202-206
• /
• 2005

무전해 도금법에 의해 제조된 은 피복 Ni-Zn 페라이트 분말의 전파흡수특성을 조사하였다. 분무건조법 및 소결 고정에 의해 평균입경이 $50{\mu}m$ 정도인 페라이트 구형 분말을 제조하고, 이 분말 위에 은 피막을 무전해 도금법에 의해 코팅하였다. 페라이트 표면에 형성되는 은 피막의 미세조직은 도금욕의 $AgNO_3$의 농도에 따라 민감히 변화하였다. 균일한 은 피막을 얻기 위해 페라이트 분말 20g당 10g/L $AgNO_3$가 필요하였다. 페라이트 분말 표면에 은 피막이 형성됨에 따라 전기저항은 $10^{-2}\~10^{-3}\;\Omega$ 정도까지 감소하였다. 도금 처리되지 않은 순수 페라이트 분말은 400 MHz에서 자기공명을 나타내는 전형적인 자성재료의 특성을 나타내었고, 복소유전율은 실수 항이 35, 허수 항은 거의 0에 가까운 값을 나타내었다. 반면 균일한 은 도금이 이루어진 페라이트 분말은 투자율의 큰 변화 없이 복소유전율 실수항이 35, 허수항이 8 이상으로 매우 크게 증가하였다. 이에 따라 전파흡수체의 두께를 현저히 줄일 수 있었다. 임피던스 정합두께는 C-band대역에서 도금되지 않은 페라이트 분말의 경우 5mm로부터 도금 후 2mm 수준으로 감소하였다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1991년도 하계학술대회 논문집
• /
• pp.217-220
• /
• 1991

Ni-Zn ferrite powders in the few hundred angstrum size range and up have been synthesized by a wet direct method. The coprecipitate were prepared by adding alkaline solution into the constituent metal ions solution. and subsequent calcined at various temperature. At 95, the particles were ultrafine spherical shaped particles of about 500(A) in diameter.

• 한국결정학회지
• /
• 제12권1호
• /
• pp.20-24
• /
• 2001

NiZn-ferrite was synthesized usign waste iron oxide catalysts which were produced from styrene monomer process and buried underground as an industrial wastes. The spinel type ferrite was obtained by calcination and sintering of the mixture of finely ground waste catalysts, nickel oxide and zinc oxide powders. The sintered body of Ni/sub 0.5/Zn/sub 0.5/Fe₂O₄ composition at 1230℃ for 5 hours showed the density of 5.38g/㎤, and initial permeability of 59 at 1 kHz. Not only cerium oxide, which existed as a major component in the catalyst, but also unicorporated NiO and ZnO into spinel structure remained as second phases after sintering.