• 한국재료학회지
• /
• 제8권6호
• /
• pp.505-512
• /
• 1998

플라즈마 용사법을이용하여 AISI 316 스테인레스 금속모재에 0.1mm 두께의 $NiCrAlCoY_{2}O_{3}$금속 결합층과 0.3mm 두께의 $ZrO_{2}(8wt%Y_{2}O_3$) 세라믹층으로 구성된 이층 단열코팅층을 제조하였다. 코팅층의 미세조직, 금속결합층의 산화를 고찰하였으며, $900^{\circ}C$에서 등은 시험과 열반복시험 후, 접합강도시험을 통하여 코팅층의 단사정 상은 열처리시간이 길어질수록 약간 증가하였다. 또한 비변태성 t'의 c/a는 용사상태에서 1.0099이였으며, 100시간 열처리 후에는 1.0115로 약간 증가하였다. 그리고 용사층의 접합강도는 열처리 시간이 길어질수록 감소하였다. 등온열처리 후에는 1.0115로 약간 증가하였다. 그리고 용사층 의 접합강도는 열처리 시간이 길어질수록 감소하였다. 등온열처리 후, 파괴는 주로 세라믹층에서 일어났으며, 반복 열처리되 시편에서는 10회 이후 대부분 금속결합층/세라믹층의 계면에서 일어났다.

• Corrosion Science and Technology
• /
• 제2권1호
• /
• pp.53-57
• /
• 2003

The MarM247 based superalloy (8wt.%Cr- 9wt.%Co- 3wt.%Ta- 1.5wt.%Hf- 5.6%wt.Al- 9.5wt.%W- Bal. Ni) specimens were diffusion aluminized by for types of pack cementation methods, and their coating structure and their high temperature oxidation resistance were investigated. The coated specimens treated at 973K in high aluminum concentration pack had a coating layer containing large hafunium rich precipitates, which were originally included in substrate alloy. After the high temperature oxidation test in air containing 30 vol.% $H_2O$ at 1273K ~ 323K, the deep localized corrosion which reached to the substrate were observed along with these hafnium rich precipitates. On the other hand, the coated specimens treated at 1323K using low aluminum concentration pack showed the coating layer without the large hafunium rich precipitates, and after the high temperature oxidation test at 1273K for 1800 ksec, it did not show the deep localized corrosion. The nickel electroplating before the aluminizing forms thick hafnium free area, and its high temperature oxidation resistance were comparable to platinum modified aluminizing coatings at 1273K.

• 비파괴검사학회지
• /
• 제29권5호
• /
• pp.450-457
• /
• 2009

열차폐 코팅 시편에 대하여 열충격을 주기적으로 가한 후 발생하는 결함을 관찰하였다. 실험에 사용 된 열차폐 코팅 시편은 인코넬-738로 제작된 모재 위에 CoNiCrAlY 본드 코팅층과 $ZrO_2-8wt%Y_2O_3$ 세라믹탑 코팅층이 플라즈마 용사 방법으로 올려진 형태로 되어있다. 열충격 시험은 $1000^{\circ}C$의 고온으로 가열했다가 상온으로 급격하게 냉각시키는 가혹한 조건으로 실행되었고, 사이클 수가 증가함에 따라 열충격의 피로도 또한 증가하였다. 시험후 시편 내부의 미세 조직 변화와 결함을 전자현미경으로 관찰하고, 시편의 기계적인 특성을 측정하여 그 변화 양상을 살펴보았다. 열충격 주기실험후 본드 코팅층과 세라믹 탑 코팅층 사이에 발생하는 TGO 산화물층에 대한 변화 양상과 이에 대한 와전류 신호를 측정하여 TGO층 성장 거동의 비파괴적인 평가를 위한 실험을 진행하였다. 본 연구를 통하여 마이크로 단위의 TGO층에 대한 와전류검사의 적용 가능성을 확인하고 열차폐 코팅의 수명을 예측할 수 있는 가능성을 제시하였다.

• 대한금속재료학회지
• /
• 제47권11호
• /
• pp.728-733
• /
• 2009

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_{6}$) powders were deposited onto Al 6061 substrates by cold spray process with different powder preheating temperatures (below glass transition temperature: $350^{\circ}C$, near glass transition temperature: $430^{\circ}C$ and near crystallization temperature: $500^{\circ}C$). The microstructure and macroscopic properties (hardness, wear and corrosion) of Cu based amorphous coating layers were also investigated. X-ray diffraction results showed that cold sprayed Cu based amorphous coating layers of $300{\sim}350{\mu}m$ thickness could be well manufactured regardless of powder preheating temperature. Porosity measurements revealed that the coating layers of $430^{\circ}C$ and $500^{\circ}C$ preheating temperature conditions had lower porosity contents (0.88%, 0.93%) than that of the $350^{\circ}C$ preheating condition (4.87%). Hardness was measured as 374.8 Hv ($350^{\circ}C$), 436.3 Hv ($430^{\circ}C$) and 455.4 Hv ($500^{\circ}C$) for the Cu based amorphous coating layers, respectively. The results of the suga test for the wear resistance property also corresponded well to the hardness results. The critical anodic current density ($i_{c}$) according to powder preheating temperature conditions of $430^{\circ}C$, $500^{\circ}C$ was lower than that of the sample preheated at $350^{\circ}C$, respectively. The higher hardness, wear and corrosion resistances of the preheating conditions of near $T_{g}$ and $T_{x}$, compared to the properties of below $T_{g}$, could be well explained by the lower porosity of coating layer.

• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.321-327
• /
• 2008

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_6$) coating was produced by cold spraying as a new fabrication process. The microstructure and macroscopic properties of amorphous coating layer was investigated and compared with those of cold sprayed pure Cu coating. Amorphous powders were prepared by gas atomization and Al 6061 was used as the substrate plate. X-ray diffraction results showed that Cu based amorphous powder could be successfully deposited by cold spraying without any crystallization. The Cu based amorphous coating layer ($300{\sim}400{\mu}m$ thickness) contained 4.87% porosity. The hardness of Cu based amorphous coating represented $412.8H_v$, which was correspond to 68% of the hardness of injection casted bulk amorphous material. The wear resistance of Cu based amorphous coating was found to be three times higher than that of pure Cu coating. The 3-point bending test results showed that the adhesion strength of Cu based amorphous coating layer was higher than that pure Cu coating. It was also observed that hard Cu base amorphous particle could easily deform soft substrate by particle collisions and thus generated strong adhesion between coating and substrate. However, the amorphous coating layer unexpectedly represented lower corrosion resistance than pure Cu coating, which might be resulted from the higher content of porosity in the cold sprayed amorphous coating.

• 한국광학회지
• /
• 제11권5호
• /
• pp.323-329
• /
• 2000

[공기 $ISiO_2ITiNI$ 유리]설계의 반사율이 가시광선 영역에서 0이 되는 TiN의 이상적인 복소수 굴절률을 계산하였다. TiN과 $SiO_2$의 각 층의 두께 변화에 따른 2층 무반사 코팅의 반사율을 전사모의하였으며, 그 결과 TiN의 두께를 조절함으로써 최저 반사율 영역의 폭과 반사율을 변화시킬 수 있었고, $SiO_2$층의 두께를 조절함으로써 반사율이 최저가 되는 중심을 이동시킬 수 있었다. RF 마크네트론 스퍼터링 방법으로 증착한 TiN 박막의 화학적, 구조적, 전기적 특성은 각각 Rutherford backscattering spectroscopy (RBS), atomic force microscope(AFM), 4점 탐침 측정기를 이용하였다. 또한 TiN 박막과 2층 무반사 코팅의 광학적 특성은 분광광도계와 variable angle spectroscopic ellipsometer(VASE)를 이용하여 조사하였다. AFM 측정 결과 TiN 박막의 rms 거칠기는 $9~10\AA$으로 비교적 박막의 표면은 균일하고, 높은 기판온도에서 증착한 TiN 박막의 비저항은 4점 탐침측정 결과 $360~730\mu$\Omega $ cm로 매우 낮으며, RBS측정 결과 Ti:O:N=1:0.65:0.95 비율로 산소가 포함되어 있음을 알았다. 이러한 TiN 박막의 특성과 전산모의 바탕으로 증착한 TiN층을 이용한 2층 무반사 무정전 코팅[공기 $ISiO_2ITiNI$ 유리]의 반사율은 440~650 nm영역에서 0.5% 미만이었다.

• 청정기술
• /
• 제25권3호
• /
• pp.256-262
• /
• 2019

Hydroxylammonium nitrate (HAN) 기반 액상 추진제는 발암물질이 아니며 연소가스 또한 독성이 거의 없어서 환경 친화적인 추진제로 주목을 받고 있다. 추력기에서 HAN 기반 액체추진제를 분해하는데 사용되는 촉매는 저온 활성 및 고내열성을 동시에 보유하고 있어야 한다. 본 연구의 목적은 metal foam 표면에 alumina slurry를 wash coating 방법으로 담지한 후, 루테늄(ruthenium) 전구체를 그 위에 담지하여 Ru/alumina/metal foam 촉매를 제조하고, 이 촉매의 HAN 수용액 분해 활성을 평가하는 것이다. Wash coating 방법으로 metal foam 지지체에 알루미나를 담지시키는 과정에서 wash coating 반복 횟수가 alumina/metal foam의 물리적 특성에 미치는 영향을 분석하였다. 알루미나 wash coating 횟수가 증가할수록 약 7 nm의 직경을 갖는 메조기공이 지속적으로 발달하여 표면적과 기공 부피가 증가하는데, metal foam에 알루미나를 코팅하는 과정을 12 회 반복하는 것이 최적이라고 판단하였다. 이 지지체에 Ru을 담지한 Ru/alumina/metal foam 촉매의 표면에도 메조기공이 잘 발달하였다. 활성금속과 알루미나를 담지하지 않은 metal foam 자체만으로도 HAN 수용액의 분해반응을 촉진할 수 있음을 알 수 있었다. Ru/alumina/metal foam-550촉매의 경우는 열분해 반응에 비해서 분해개시온도를 큰 폭으로 낮추었고, ${\Delta}P$를 크게 증가시킬 수 있어서, HAN 수용액 분해 반응에서 우수한 활성을 보였다. 그러나 이 촉매를 $1,200^{\circ}C$에서 소성하면 반응 활성이 저하되는데 이는 촉매의 표면적과 기공 부피가 급격하게 감소하고 Ru이 소결되기 때문이다. 추가적인 연구를 통해서 Ru/alumina/metal foam의 내열성을 개선할 필요성이 있다.