The Mar-M-247 alloy is one of the most widely used materials for gas turbine components in aerospace filed and it shows excellent high temperature strength properties. Hot section parts, such as turbine nozzle and blade, are difficult to manufacture because of their complicated shape. So, the joining process usually applies to them. In this study, the high-temperature behavior of Mar-M-247 alloy at liquid diffusion bonding was investigated. Thus, we performed the diffusion bonding at $1,121^{\circ}C$ for 7 minutes, and observed changes in high temperature strength. As a result, the strength of the bonded specimens decreased by about 70% at $649^{\circ}C$, 60% at $825^{\circ}C$, and 45% at $1,000^{\circ}C$ compared to the base metal. As a result of observing the strength change with bonding time, the specimen bonded for 720 minutes showed a similar strength with the base metal at $649^{\circ}C$. Inferring this result, the joint is considered to be the one-body part.

• Korean Journal of Materials Research
• /
• v.32 no.4
• /
• pp.200-209
• /
• 2022

In this study, defects generated in the YSZ coating layer of the IN738LC turbine blade are investigated using an optical microscope and SEM/EDS. The blade YSZ coating layer is composed of a Y-Zr component top coat layer and a Co component bond coat layer. A large amount of Cr/Ni component that diffused from the base is also measured in the bond coat. The blade hot corrosion is concentrated on the surface of the concave part, accompanied by separation of the coating layer due to the concentration of combustion gas collisions here. In the top coating layer of the blade, cracks occur in the vertical and horizontal directions, along with pits in the top coating layer. Combustion gas components such as Na and S are contained inside the pits and cracks, so it is considered that the pits/cracks are caused by the corrosion of the combustion gases. Also, a thermally grown oxide (TGO) layer of several ㎛ thick composed of Al oxide is observed between the top coat and the bond coat, and a similar inner TGO with a thickness of several ㎛ is also observed between the bond coat and the matrix. A PFZ (precipitate free zone) deficient in γ' (Ni₃Al) forms as a band around the TGO, in which the Al component is integrated. Although TGO can resist high temperature corrosion of the top coat, it should also be considered that if its shape is irregular and contains pore defects, it may degrade the blade high temperature creep properties. Compositional and microstructural analysis results for high-temperature corrosion and TGO defects in the blade coating layer used at high temperatures are expected to be applied to sound YSZ coating and blade design technology.