• Journal of Magnetics
• /
• 제4권4호
• /
• pp.128-130
• /
• 1999

We have measured the magnetization of Ni/Ag(Ni at %)/Ni (50$\AA$/30 $\AA$/50 $\AA$) trilayered films including Ni atoms inserted in non-magnetic Ag spacer. The magnetization as a function of applied field at 5 K and as a function of temperature at 100 Oe were investigated respectively using SQUID magnetometer. In these measurements peaks of magnetization at some critical temperatures were observed in all the samples. The antiferromagnetic coupling energy between neighboring Ni layers showed oscillatory behaviors according to the amounts of the Ni atoms inserted in Ag spacer. Loose spin model suggested by slonczews야 was used to explain such results.

• Journal of Magnetics
• /
• 제16권2호
• /
• pp.97-100
• /
• 2011

Bilayers of soft NiFe (150 nm-420 nm) on hard Ni (150 nm) were prepared by electrodeposition. The process of magnetization reversal in the NiFe/Ni bilayers was then investigated. The hysteresis loop generated by a magnetization reversal of soft NiFe under a positive saturation state of a hard Ni layer shows a shift along the negative field axis, which is clear evidence for the exchange spring effect in the NiFe/Ni bilayers. The dependence of the coercive field $H_c$ and exchange bias field Hex on the thickness of the NiFe layer was also investigated. As the NiFe thickness increases from 150 nm to 420 nm, both $H_c$ and $H_{ex}$ decrease rapidly from $H_c$= 51.7 Oe and $H_{ex}$ = 12.2 Oe, and saturate to $H_c$ = 5.8 Oe and $H_{ex}$ = 3.5 Oe.

• 한국수소및신에너지학회논문집
• /
• 제13권1호
• /
• pp.74-82
• /
• 2002

Ni nanoparticles이 표면에 분산된 mutiwall carbon nanotubes (MWNTs)의 수소저장 특성을 분석하였다. Metal nanoparticles의 분산 방법은 incipient wetness impregnation procedure을 사용하였는데, 이러한 Ni catalysts의 역할은 기존에 알려진 Li, K doping과 같은 개념으로 기상의 수소를 분해하여 carbon 표면에 chemical adsorption 시키는 역할을 하게 된다. 실제로 Ni nanoparticles이 6wt% loading된 경우에는 thermal desorption spectra를 분석한 결과 ~2.8wt% hydrogen이 ~340-520K의 온도범위에서 방출되는 것을 관찰할 수 있었다. Kissingers plot을 통해서 MWNTs와 hydrogen과 interaction energy를 구한 결과 ${\sim}31kJ/molH_2$를 얻을 수 있었으며 이 값은 기존의 SWNTs에 hydrogen이 physi-sorption에서 실험적으로 얻을 수 있었던 값보다 1.5배 큰 값이라고 할 수 있다. 자세한 수소저장 기구를 분석하기 위해서 FT-IR분석을 한 결과 C-Hn stretching vibrations이 관찰되었으며 mono-hydride와 weak di-hydride $sp^3$가 형성된 것으로 해석 될 수 있었다. 이와 같은 결과는 Ni nanoparticle들이 예상과 같이 hydrogen molecules을 dissociation하는 역할을 하는 것을 의미한다. 연속적인 thermal desorption 실험을 통해 가역성도 평가하였다.

• 원예과학기술지
• /
• 제32권4호
• /
• pp.434-439
• /
• 2014

이 연구는 야파 처리 시간대가 살비아 'Salsa'의 영양생장 및 개화에 미치는 영향을 조사하고, 저광도 야파 처리가 광합성을 증가시킬 수 있는지 알아보고자 수행되었다. 살비아는 9시간의 단일조건 또는 9시간 일장에 $3-5{\mu}mol{\cdot}m^{-2}{\cdot}s^{-1}$의 광도의 야파를 추가한 조건의 식물 생육상에서 재배되었고, 야파 처리는 18시-22시(NI18), 22시-02시(NI22), 02시-06시(NI02)의 세 구간으로 나누어 적용되었다. NI18, NI22, NI02 처리구에서 광합성은 야파 처리 시간 동안에 각각 0.33, 0.16, $0.13{\mu}mol{\cdot}CO_2{\cdot}m^{-2}{\cdot}s^{-1}$만큼 증가하였다. 하지만 엽폭, 엽장 등의 영양생장은 단일 조건하의 식물들과 유의성 있는 차이를 나타내지 못하였다. 야파 처리 시 개화까지 걸리는 시간은 9.8일 단축되었고, 17주간 야파 처리 시 꽃의 수는 단일 조건의 36.4개에 비해 NI02 처리구에서 138.7개로 증가하였다. 이러한 결과는 02시부터 06시까지의 야파 처리가 개화를 촉진하는 데에 가장 효과적이라는 것을 보여준다. 그러나 야파 처리 시간 동안에 증가한 광합성량은 살비아의 영양생장 증가에는 효과를 보이지 못하였다. 비록 야파 처리 동안의 미미한 광합성의 증가가 살비아의 영양생장을 증가시키지는 못하였지만, 개화에는 크게 영향을 미쳤다. 단일 조건에서는 44.4%만이 개화하였지만 8주간 야파 처리시 NI18, NI22, NI02 처리구에서는 각각 77.8, 88.9, 100.0% 개화하였다.

• Journal of Magnetics
• /
• 제6권3호
• /
• pp.83-85
• /
• 2001

The magnetoresistance properties of NiO/NiFe/Cu/NiFe spin valve film deposited on MgO(100) substrate with YBa$_2$$Cu_3O_7$(YBCO) film were investigated at room temperature and at 77 K. The magnetoresistance (MR) curves of the hybrid superconductor-magnetoresistor film structure showed an exchange coupling field of 300 Oe and an inverse magnetoresistance ratio of -6.5%. The magnetization configurations of the two magnetic layers in the NiO spin valve were antiparallel due to an increment in the conduction electron flow to superconductor YBCO film. This sample showed an inverse MR ratio.

• 대한화학회지
• /
• 제45권3호
• /
• pp.242-246
• /
• 2001

사성분계 thiophosphates, $A_2NiP_2S_6>(A=Rb$, Cs)를 halide fluxes 법으로 합성하였으며 단결정 X-ray 회절방법으로 결정 구조를 해석하였다. 이 화합물들을 $C_{2h}^5-P2_1/n$ 의 공간군을 가지며, $Rb_2NiP_2S_6$의 경우 a=5.960(2), b=12.323(4), $c=7.491(3)\AA$, $\beta=97.05(3)^{\circ}$, $V=546.0(3)\AA^3$이고$Cs_2NiP_2S_6$의 경우 a=5.957(4),b=12.696(7), $c=7.679(4)\AA$, $\beta=93.60(5)^{\circ}$, $V=579.7(5)\AA^3$인 격자상수를 갖는다. 이 두화합물은 동일한 결정 구조를 갖는다. 이들의 구조는 결정학적인 a축을 따라 성장한 1차원적인 무한사슬 $_{\infty}^1[NiP_2S_6^{2-}]$로 구성되어 있으며 이 사슬들은 알칼리 금속과의 정전기적 인력을 통하여 안정화 되어있다. Ni원자는 6개의 S원자에 의해 팔면체 배위를 하고 있고, Ni$S_6$팔면체는 $[P_2S_6^{4-}]$ 음이온 3개의 $\mu-S$ 원자들에 의해 연결되어 무한 1차원적인 사슬을 형성한다. $Cs_2NiP_2S_6$에 대한 자화율 측정결과 Neel temperature($T_N$)에 상응하는 8K 이하에서 superexchange를 통한 반자기성 magnetic coupling을 발견하였다. $T_N$이상의 온도에서는 Curie-Weiss법칙을 따른다. 자기 모멘트, C(Curie), 그리고 $\theta$(Weiss Constant)는 각각 2.77 B.M., 0.9593K, 그리고 -19.02K 이다. 측정 결과로부터 얻은 유효 자기 모멘트는 spin-only $Ni^{2+}d^8$(2.83 B.M.)계의 결과와 일치한다.

• 한국수소및신에너지학회논문집
• /
• 제20권5호
• /
• pp.361-370
• /
• 2009

Ni-PTFE composite plated on graphite (C/Ni-PTFE) and PTFE (PTFE/Ni-PTFE) particles were prepared uniformly by electroless composite plating. The conductivity of C/Ni-PTFE particles was 280 S/m higher than 95 S/m of PTFE/Ni-PTFE particles at same composite plating condition (Ni:35~36 wt%, PTFE:8 wt%). The C/Ni-PTFE particles were formed into the C/Ni-PTFE plate using heat treatment at $350^{\circ}C$ under 10~$1000\;kg/cm^2$. The C/Ni-PTFE plate showed 1) high conductivity of $5.7\;{\times}\;10^4\;S/m$ due to the existence of graphite as conducting aid and the formation of 3-dimensional Ni network 2) good gas diffusion caused by various pore volumes (0.01~$100\;{\mu}m$) in the plate. The plate could be useful for an electrode in an alkaline fuel cell (AFC). The current density of C/Ni-PTFE electrode indicated $84\;mA/cm^2$ at 0.3V and it was 3.0 times higher than that of PTFE/Ni-PTFE electrode.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2002년도 동계연구발표회 논문개요집
• /
• pp.190-191
• /
• 2002

Granular feromagnets는 non-magnetic maxtrix 안에 nanometer-sized의 ferromagnetic grain들 구성된다. Co-Cu,Co-Ag, Fe-Ag, NiFe-Ag $^1$을 포함하는 이미 알려진 다른 Granular 금속 합금들의 giant magnetoresistance 에 관계하여 Granular feromagnets 에 대해 조사하였다. Bulk상태의 NiFe와 Mn 혼화되기 쉽다.$^2$ 그리고 Mn은 열처리된 다층박막의 NiFe의 lattice에 쉽게 수용되어진다.$^3$ 이번 실험에서는 metastable한 fcc solid solution NiFe-Mn 박막이 열처리 하에서 NiFe과 Mn으로 분리되었다. (중략)

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.381-387
• /
• 2000

Si3N4/stainless steel 316 joints with Ni buffer layer were fabricated by direct active brazing method (DIB) using Ag-Cu-Ti brazing alloy only and double brazing method (DOB) using Ag-Cu brazing alloy with Si3N4 pretreated with Ag-Cu-Ti brazing alloy. For the joint brazed by DIB method, Ti was segregated at the Si3N4/brazing alloy interface, but was not enough to form a stable joint interface. In addition, large amounts of Ni-Ti inter-metallic compounds were formed in tehbrazing alloy near the joint interface, which could deplete the contents of Ti involved in the interfacial reaction. However, for the joint brazed by DOB method, segregation of Ti at the joint interface were enough to enhance the formation of stable interfacial reaction products such as TiN and Ti-Si-Ni-N-(Cu) multicompounds, which restricted the formation of Ni-Tio inter-metallic compounds in the brazing alloy during brazing with Ni buffer layer. Fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was much improved by using DOB method rather than DIB method. It could be deduced that the differences of fracture strength of the joint with Ni buffer layer depending on brazing process adapted were directly affected by the formation of stable joint interface and the change in microstructure of the brazing alloy near the joint interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of Ni buffer layer in the joint was increased from 0.1 mm to 10 mm. It seems to due to the increased residual stress in the joint as the thickness of Ni buffer layer is increased. The maximum fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was 386 MPa, and the fracture of joint was originated at Si3N4/brazing alloy joint interface and propagated into Si3N4 matrix.

• 분석과학
• /
• 제13권2호
• /
• pp.194-199
• /
• 2000

본 연구에서는 Ni가 처리된 PAN계 ACFs에 대하여 흡착, 표면특성 및 항균효과를 통하여 물리 화학적인 특성과 생물학적인 특성을 제시하였다. Ni가 처리된 PAN계 ACFs의 흡착에 관한 연구로부터 N1-N3에 대하여 Type I의 흡착등온곡선과 N4-N6에 대하여 Type II와 III의 흡착등온곡선을 각각 얻었다. 이들 시료에 대하여 흡착된 부피는 Ni의 몰농도의 증가와 함께 천천히 감소함을 알 수 있었다. BET식을 사용하여 계산된 $S_{BET}$값은 $692.58-895.24m^2/g$의 범위에 분포하였다. 또한 common-t값을 사용하여 ${\alpha}_s$-법으로부터 구한 단위 질량 당 미세 동공 부피는 $0.19-0.56cm^3/g$이었다. SEM 모폴로지의 결과로부터 PAN계 ACFs의 표면은 Ni를 처리함에 따라 부분적으로 피복됨을 관찰 할 수 있었다. 최종적으로 Shake flask법을 사용한 대장균(E. coli)에 대한 항균 효과를 측정한 결과, 각각의 시료들은 92.5-100%의 효과를 나타내었다. 이러한 항균 효과는 역시 Ni의 몰농도의 증가와 함께 향상됨을 알 수 있었다.