넓은 과냉각 액체영역을 가지는 Ni-Nb-Ti-Zr계 비정질 합금의 제조 (Fabrication of Ni-Nb-Ti-Zr Amorphous Alloys with Wide Supercooled Liquid Region)

  • 김성규
    • 한국주조공학회지
    • /
    • 제22권5호
    • /
    • pp.252-256
    • /
    • 2002
  • Ni-Nb-Ti-Zr amorphous alloys were manufactured using melt-spinning methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The value of the reduced glass transition temperature and the supercooled liquid region of $Ni_{62}Nb_{10}Ti_{13}Zr_{15}$ alloy were relatively high and were 0.612 and 76 K respectively. However, amorphous bulk alloy rod was not formed using the Cu-mold die casting. The mechanical properties were in the range of $800{\sim}900DPN$ of hardness and $2.5{\sim}2.8$ GPa of tensile strength in the whole composition range.

Ni기 비정질 벌크합금의 제조와 기계적 성질 (Fabrication and Mechanical Properties of Ni-based Amorphous Bulk Alloys)

  • 김성규
    • 한국주조공학회지
    • /
    • 제22권6호
    • /
    • pp.288-292
    • /
    • 2002
  • Ni-base amorphous alloys were manufactured using melt-spinning and Cu-mold die casting methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The reduced glass transition temperature and the supercooled liquid region of $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$alloy were 0.621 and 46 K respectively. $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$ alloy was produced in the rod shape 3mm diameter using the Cu-mold die casting. Hardness, compression strength, elongation and elastic modulus of the alloy were 850 DPN, 2.75 GPa, 1.8% and 150 GPa respectively. Moreover, compression strength of 2.75 GPa was the highest value in the amorphous bulk alloy produced up to now.

비정질 분말의 열간 성형법에 의한 벌크 비정질합금의 제조 (Fabrication of Bulk Metallic Glass Alloys by Warm Processing of Amorphous Powders)

  • 이민하;김도향
    • 한국분말재료학회지
    • /
    • 제11권3호
    • /
    • pp.193-201
    • /
    • 2004
  • 1960년 Au-Si계 합금에서 처음으로 비정질상이 급속 응고법에 의해 보고된 이래/sup 1)/ 지난 40년 간 많은 합금계에서 비정질상이 보고되어졌다. 대표적으로 Fe-, Ni-, Co기 합금 등 많은 합금계에서 비정질상이 보고되었으나, 비정질상의 형성을 위해서는 약 105 K/s이상의 높은 냉각속도를 필요로 하였다. 1980년대 수백 K/s의 낮은 냉각속도 하에서도 비정질상이 형성될 수 있는 다원계 합금(multi-component alloy)이 Mg-Ln-(Ni, Cu, Zn), Ln-Al-TM 합금에서 보고되어 졌으나 많은 관심을 받지 못하다가 1993년 Zr-Ti-Ni-Cu-Be 합금에서 수 ㎝ 크기의 비정질합금 제조가 보고되면서 전 세계적으로 많은 관심을 받게 되었다. Zr-Ti-Ni-Cu-Be계 벌크 비정질 합금이 보고된 후 Zr-(Nb,Pd)-Al-TM, Pd-Cu-Ni-P, Fe-Co-Zr-Mo-W-B, Ti-Zr-Ni-Cu-Sn등 여러 합금계에서 벌크 비정질 합금이 보고되었다. (중략)

Zr계 비정질 복상 합금의 과냉 액상 영역에서의 유동 음력과 변형거동 (Flow Stress and Deformation Behavior of Zr-based Bulk Metallic Glass Composite in Supercooled Liquid Region)

  • 전현준;이광석;장영원
    • 한국소성가공학회:학술대회논문집
    • /
    • 한국소성가공학회 2006년도 춘계학술대회 논문집
    • /
    • pp.417-420
    • /
    • 2006
  • The composition and structure of dendrite phase within $Zr_{76.11}Ti_{4.20}Cu_{4.51}Ni_{3.16}Be_{1.49}Nb_{10.53}$ bulk metallic glass (BMG) were confirmed by using an EPMA, XRD and TEM, respectively. The chief elements of dendrite phase were Zr-Ti-Nb and had a BCC structure. The thermal properties of this BMG have been then subsequently investigated by using a differential scanning calorimeter (DSC). The glass transition and crystallization onset temperatures were determined as $339.7^{\circ}C$ and $375.8^{\circ}C$ for this alloy, respectively. Mechanical properties have also been examined by conducting a series of uniaxial compression tests at various temperatures within supercooled liquid region under the strain rates between $10^{-4}/s$ and $3{\times}10^{-2}/s$. The deformation behavior of BMG composite within supercooled liquid region is similar to one of Vit-1 exhibiting amorphous single phase alloy. The flow stresses of BMG composite, however, are entirely higher than those of Vit-1 because dendrite phases are interfere with moving of atoms.

  • PDF

$\textrm{Fe}_{80-x}\textrm{P}_{10}\textrm{C}_{6}\textrm{B}_{4}\textrm{M}_{x}$(M=Transition Metal) 비정질합금의 열적안정성 (Thermal Stability of $\textrm{Fe}_{80-x}\textrm{P}_{10}\textrm{C}_{6}\textrm{B}_{4}\textrm{M}_{x}$(M=Transition Metal) Amorphous Alloys)

  • 국진선;전우용;진영철;김상협
    • 한국재료학회지
    • /
    • 제7권3호
    • /
    • pp.218-223
    • /
    • 1997
  • 과냉각액체구역(${\Delta}T_{x}=T_{x}-T_{g}$)을 갖는 $Fe_{80}P_{10}C_{6}B_{4}$ 조성에 천이금속(Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Co, Ni, Pd, Pt및 Cu)를 첨가하여 이들 원소가 유리화온도($T_{g}$), 결정화온도($T_{x}$) 및 과냉액체구역 (${\Delta}T_{x}$)에 미치는 영향에 \ulcorner여 조사하였다. $Fe_{80}P_{10}C_{6}B_{4}$ 합금의 ${\Delta}T_{x}$ 값은 27K였으나 이 합금에 Hf, Ta 및 Mo을 각각 4at%첨가하면 그 값이 40k 이상으로 증가하였다. 이같은 ${\Delta}T_{x}$ 값의 증가는 유리화온도($T_{g}$의 상승보다 결정화온도($T_{x}$)의 상승폭이 크기 때문이다. $T_{g}$$T_{x}$는 외각전자밀도(e/a)가 약 7.38에서 7.05로 감소할수록 상승하였다. e/a의 감소는 천이금속과 다른 구성원소(반금속)사이의 상호결합상태를 의미한다. 즉 $T_{g}$$T_{x}$의 상승은 강한 상호결합력에 기인하는 것으로 사료된다.

  • PDF