• Journal of Korea Foundry Society
• /
• v.11 no.6
• /
• pp.475-481
• /
• 1991

In this study the fabrication technology and mechanical properties of AC8A/$Al_2O_3$ Composites by squeeze casting process were investigated to develope for application as the piston materials that require good friction, wear resistance, and thermal stability. AC8A/$Al_2O_3$ composistes without a porosity and the break of preform were fabricated at the melt temperature of $740^{\circ}C$, the preform temperature of $500^{\circ}C$, and mold temperature of $400^{\circ}C$ under the applied pressure of $1200kg/cm^2$ as the results of the observation of microstructures. As the results of this study, the tensile strength of AC8A/$Al_2O_3$ composites was not increased linearly with $Al_2O_3$ volume fraction and so it seemed not to agree with the rule of mixture, which had been used often in metal matrix composite. Also the tensile strength after thermal fatigue test was little different from that before the test. Consequently it was thought that AC8A/$Al_2O_3$ composites fabricated under our experimental conditions had a good thermal stability and subsequently a good interface bonding. Wear rate(i.e., volume loss per unit sliding distance) of AC8A/$Al_2O_3$ composites was decreased with $Al_2O_3$ volume fraction and the sliding speed at both room temperature and $250^{\circ}C$ and so there was a good correlation between wear rate and hardness. Also the wear rate of AC/8A20% $Al_2O_3$ composities was obtained the value of $1.65cm^3/cm$ at sliding speed of 1.14m/sec as compared with about $3.0\;{\times}10^{-8}cm^3/cm$ hyereutectie Al-Si alloy(Al-16%Si-2%Cu-1%Fe-1%Ni), which applied presently for piston materials. The wear behavior of $Al_2O_3$ composites was observed to a type of abrasive wear by the SEM view of wear surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.241-241
• /
• 2007

We fabricated SmBCO coated conductors(CCs) on IBAD-MgO templates using co-evaporation method. IBAD-MgO templates consist of PLD-LMO/epi-MgO/IBAD-MgO/Ni-alloy and showed good in-plane texture of below FWHM 7 degree. Evaporation rates of Sm, Ba, and Cu were precisely controlled to get the optimum composition ratio after deposition process. To optimize the oxygen partial pressure of reaction region, wide range of the partial pressure was investigated from 1 mTorr to 15 mTorr. By reducing the oxygen partial pressure to 5mTorr, (103)grains in SmBCO layer have been increased. On the other hand, there were only (001)grains in SmBCO layer deposited at 15 mTorr $O_2$. Deposition temperature was also investigated from $600^{\circ}C\;to\;800^{\circ}C$ to make high Ic SmBCO CCs. SmBCO on IBAD MgO template showed that the Ic increased gradually at higher growth temperature to $800^{\circ}C$, which the highest Jc and Ic is $2.6\;MA/cm^2$ and 500 A/cm-w., respectively.