• Journal of Power System Engineering
• /
• v.1 no.1
• /
• pp.70-79
• /
• 1997

Ni-base self-fluxing alloy powder particles were flame sprayed onto the SS400 mild steel substrate surface. The effects of both substrate temperature and spraying distance on the splat behavior of sprayed particles were examined. The results obtained are summarized as follows: 1) In the splat behavior of Ni-base self-fulxing alloy particles sprayed onto the SS400 mild steel substrate, splashing was observed under the room temperature condition. On the contrary, it showed circular plate pattern in the substrate temperature range over 373K. 2) It was cleared that there was close relationship between mechanical properties of coating layer and splat behavior of sprayed particles. 3) From the experimental results, optimum spraying conditions showed excellent mechanical properties in the case of Ni-base self fluxing alloy sprayed onto the SS400 mild substrate were 473K of substrate temperature and 250mm of spraying distance.

• Journal of Power System Engineering
• /
• v.2 no.2
• /
• pp.35-40
• /
• 1998

In this study, the author investigated the effects of strengthening treatments on the mechanical properties of plasma sprayed Ni-base self fluxing alloy. Strengthening treatments for sprayed specimens were carried out in 4 different temperature conditions in vacuum furnace. The mechanical properties, such as microhardness, thermal shock resistance and erosion resistance were tested for the sprayed specimens after strengthening treatments. And it was proved that the mechanical properties of coating layer were much improved by strengthening treatments.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.19 no.5
• /
• pp.538-544
• /
• 2013

In this study, cavitation characteristics of a thermal spray coating were evaluated in order to improve durability and cavitation resistance. For a coating material, a Ni-based self-fluxing alloy was thermal-sprayed over a ALBC3 alloy substrate and subsequently modified by heat treatment.The resulted self-fluxing coating layer had relatively high hardness compared to the base material, and thus would be expected to exhibit good durability. However, the cavitation characteristics were deteriorated due to the intrinsic porous structure of the coating. Therefore, it is essential to optimize heat treatment condition during thermal spraying coating process for self-fluxing alloy, and in this research the increase in heat treatment temperature is thought to increase the fluidity of B and Si in the self-fluxing alloy and to remove pores or defects, leading to the characteristics enhancement.

• Journal of the Korean institute of surface engineering
• /
• v.22 no.1
• /
• pp.26-42
• /
• 1989

It has between investigated that the optimum spaying conditions, such as, spraying distance, fusing temperature and fusing time, ect, in a Ni-cr base self fluxing alloy sprayed on the mild steel substrate by oxygen-acetylenc flame spraying. Sprayed specimens on various conditions were fuused in a vacuum furnace and the results were as follows. The optimum spraying condition for excellent coating layer are obtained under spraying distances, fusing temperature and fusing and time ; 180~240mm,1050~110$0^{\circ}C$and 15~30min, respectively. The adhesive strength and surface hurface hardness of the as sprayed specimens were very low by mechanical bonding becaus of the diffusion layer during process. The carbides and borides and formed in the sprayed coating layer and densification of the layer was resulted from the elimination of pores and oxides. The hardness of sprayed coating layer, particularly in the high temperature, was superior to ordinary tool steels.