• 한국표면공학회지
• /
• 제47권6호
• /
• pp.323-329
• /
• 2014

Effects of sealant and sealing procedure on corrosion resistance of high velocity oxy-fuel (HVOF) sprayed coatings were studied. HVOF-sprayed CrC-20NiCr coatings were sealed using three commercial sealants based on phenolics and epoxy. Penetration depth of sealants, measured by fluorescent microscope technique, was between $19{\mu}m$ and $340{\mu}m$ depending on sealant, sealing condition or sealing procedure. It was found that sealing on rotation status was more effective than that on stationary specimen due to the Coriolis effect of fluid in pores of the coating. From the CASS results, corrosion resistance of properly sealed CrC-20NiCr coatings was equal to that of hexa-valent chromium plating.

• 반도체디스플레이기술학회지
• /
• 제13권3호
• /
• pp.51-55
• /
• 2014

Ni-CNT(Carbon Nanotubes) composite coating is often used for the surface treatment of mechanical/electronic devices to improve the properties of the Ni coating. For the Ni-CNT coating, the dispersion of CNT fibers is a critical process. In this study, ultrasonic treatment instead of the conventional ball milling was attempted as a dispersion method for the electroless Ni-CNT coating. SEM-EDX analysis was performed and contact angle, sheet resistance, and micro-hardness were measured. Results showed that the ultrasonic treatment was comparable to the ball milling, as a dispersion method, but the difference was negligible. However, combined ball milling and ultrasonic treatment(double treatment) showed much improved micro-hardness value, above 350Hv(close to the value obtained by the Ni-CNT electroplating). In addition, electroless Ni-CNT(double-treated) coatings formed on the thin Ni film deposited by the electroless plating(double coating) showed better mechanical properties. Thus, double treatment and double coating are suggested as an improved electroless Ni-CNT coating method.

• 공업화학
• /
• 제8권5호
• /
• pp.742-748
• /
• 1997

초경공구(WC-Co)의 성능 향상을 목적으로 고경도, 높은 열전도도의 특성 등을 가진 다이아몬드 막을 코팅하고 있으나 WC-Co 기판표면의 특성상 문제점으로 인하여 코팅의 어려움이 있다. 이 문제의 해결을 위하여 WC-Co기판위에 중간층을 도입한 후 다이아몬드 막을 증착시키는 새로운 방법을 고려하였으며 중간층의 제조에 무전해 Ni-P도금법을 사용하였다. 무전해도금을 위한 WC-Co기판의 전처리, 무전해도금 및 열처리, 다이아몬드 막 증착의 공정에 대하여 조사하였다. 형성되는 계면의 구조와 성분, 계면간의 밀착력 등을 Scratch Tester, Roughness Tester, SEM/EDS, XRD, Raman Spectroscopy를 사용하여 분석하였다. 무전해도금의 전처리로서 산에 의한 방법과 다이아몬드 분말에 의한 방법을 사용하였으며 두 경우에 모두 WC-Co기판의 표면조도의 감소, 표면 Co성분의 감소, 그리고 밀착력 저하가 관찰되었다. 무전해도금층의 열처리시 영향을 조사하였으며 온도 증가에 따라 Ni 결정이 형성되며 이로 인하여 도금의 밀착력이 증가되며 Ni 결정이 성장함을 관찰하였다. 또한 열처리된 Ni-P도금 위에서 다이아몬드막 증착 실험을 실시하였으며 증착온도를 증가시킴에 따라 다이아몬드 형성이 증가되어 $800^{\circ}C$일때 양호한 다이아몬드 막을 얻을 수 있었다. 본 연구의 방법 및 실험조건은 WC-Co를 비롯하여 다이아몬드 막 형성이 어려운 소재들의 코팅에 효과적으로 이용될 수 있다.

• 마이크로전자및패키징학회지
• /
• 제27권2호
• /
• pp.39-44
• /
• 2020

최근 웨어러블 장치에 적용하기 위한 유연성 기판에 대한 연구가 활발히 진행되고 있다. 특히, 유연성 기판 중 의복에 웨어러블 장치를 적용하기 위한 전도성 섬유기판에 대한 연구가 진행되고 있다. 본 연구에서는, 면섬유 기판 표면에 CNT와 Pd복합 용액을 스프레이 법을 이용하여 형성하였고, 무전해 도금법을 이용하여 금속층을 도금하였다. 도금된 섬유기판의 형상을 분석하기 위하여 SEM 장비를 이용하였고, CNT를 증착한 섬유기판의 표면에 Ni 레이어가 형성된 것을 확인하였다. EDS 분석을 통하여 섬유기판의 표면에 형성된 물질이 Ni임을 알 수 있었다. 전기적 특성을 확인하기 위하여 4-point probe로 무전해 도금을 진행한 섬유기판의 표면저항 및 저항 분포를 확인하기 위한 맵핑을 진행하였다. 무전해 도금의 진행 시간이 길어질수록 전도성이 향상되었음을 확인할 수 있었고, 표면 위치 별 저항의 분포가 균일함을 알 수 있었다. 인장력, 굽힘, 뒤틀림 시험을 통하여 기계적 스트레스로 인한 저항변화를 측정하였다. 그 결과 도금 시간이 길어질수록 유연성 기판의 저항변화가 점점 사라지는 것을 확인하였다. UTM(Universal testing machine)을 이용하여 도금시간 변화에 대한 무전해 도금 기판의 기계적 특성 향상 여부에 대하여 분석하였다. 인장강도는 무전해 도금을 2 시간 동안 진행한 전도성 섬유기판의 경우, 면섬유 기판보다 약 16 MPa 증가하였다. 이러한 결과들을 토대로 Ni-CNT-Fabric 유연기판은 의류 일체형 전도성 기판으로 이용되기에 충분함을 확인하였고, 이러한 연구 결과는 유연기판, 웨어러블 디바이스뿐만 아니라 유연성이 필요한 배터리, 촉매, 태양전지 등에 적용되어 발전에 기여할 수 있을 것으로 기대한다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.434-435
• /
• 2009

The crystalline silicon solar cell where the solar cell market grows rapidly is occupying of about 85% or more. high-efficiency and low cost endeavors many crystalline silicon solar cells. the fabrication processes of high-efficiency crystalline silicon solar cells necessitate complicated fabrication processes and Ti/Pd/Ag contact, however, this contact formation processed by expensive materials. Ni/Cu contact formation is good alternative. in this paper, according to temperature Ni silicide makes, produced Ni/Cu contact solar cell and measured conversion efficiency.

• 한국표면공학회지
• /
• 제45권4호
• /
• pp.162-167
• /
• 2012

Ni-P/C multi-layer was synthesized by electroless plating and paste coating for better corrosion and surface conductance as a metallic bipolar plate. The Ni-P layer could be synthesized with the range of 2.6~22.4 at.% P contents and it's surface morphology and corrosion resistance depend on content of P. Corrosion resistance of the Ni-P layer in sulfuric acid by electrochemical test is similar with pure Ni. Surface resistance of pure Ni after corrosion was increased about 8% compared to pure Ni. On the other hand, that of the Ni-P/C composite with 20% carbon content was increased only 1%.

• Journal of Advanced Marine Engineering and Technology
• /
• 제19권3호
• /
• pp.50-61
• /
• 1995

In recent years, many ceramic researchers have discoved various methods of joining ceramic to metal. However, most of these joining methods are perfomed under vacuum and pressured circumstances. So, when we join ceramic to metal,the proceedings are very complicated and require a very high cost. The purpose of this study is to develop a new joining method of an alumina ceramic to an aluminum metal in air atmosphere. The joining condition, such as copper metallizing, nickel plating, brazing, etc. was investigated through the shear strength test of the trial joint. The results obtained from the above experimenta are summarized as follows : 1) In the case of the $Al_2O_3$/$Al_2O_3$joint, the shear strength of the joint was affected by the various foctor such as kaolin content, copper metallizing thickness, firing temperature, firing time. 2) The better shear strength of the $Al_2O_3$/Al joint was obtained when Ni plating was conducted under higher current density than existing plating condition. 3) The shear strength of the $Al_2O_3$/Al joint increases with the Ni plating thickness is confined to the range of this paper. 4) The shear strength of the thermal-shocked specimen($Al_2O_3$/Al joint) was far more deteriorated than that of the as-bonded specimen.

• 폴리머
• /
• 제31권5호
• /
• pp.410-416
• /
• 2007

무유화제중합으로 제조된 폴리(메틸 메타크릴레이트) (PMMA) 시드 고분자 미립자에 가교단량체인 HDDA (1,6-hexanediol diacrylate), triEGDMA [tri(ethylene glycol) dimethacrylate] 또는 triEGDMA와 EGDMA (ethylene glycol dimethacrylate)의 혼합액을 흡수시키고, 이를 중합하여 단분산 가교고분자 미립자를 제조할 시 1) 흡수된 가교단량체와 시드 고분자 미립자의 중량비(흡수율) 변화, 2) 가교단량체의 변화, 3) 무전해 니켈도금 및 4) 무전해 (니켈/금)도금에 따른 단분산 가교고분자 미립자의 기계적 물성인 탄성복원율, 압축탄성률, 파괴강도 및 파괴변형률의 변화를 MCT(micro compression test)를 사용하여 측정하였다. 이번 연구를 통해 가교단량체의 흡수율 증가는 가교고분자 미립자의 파괴강도에만 큰 영향을 미쳤으나, 가교고분자 미립자의 무전해 도금은 도금분체의 탄성복원율 및 파괴강도는 감소시키나, 파괴변형률의 경우에는 거의 영향을 미치지 않으며, 압축탄성률의 경우는 $K_{10}$ 및 $K_{20}$는 크게 증가시키나, $K_{30}$ 이후에는 거의 영향을 미치지 못함을 알 수 있었다.

• Corrosion Science and Technology
• /
• 제7권1호
• /
• pp.61-67
• /
• 2008

In this paper, electrochemical and microstructural characteristics of nickel-plated Alloy 600 were investigated in order to identify the performance of electroless Ni-plating on Alloy 600 in high-temperature aqueous condition with the comparison of electrolytic nickel-plating. For high temperature corrosion test of nickel-plated Alloy 600, specimens were exposed for 770 hours to typical PWR primary water condition. During the test, open circuit potentials (OCP's) of all specimens were measured using a reference electrode. Also, resistance to flow accelerated corrosion (FAC) test was examined in order to check the durability of plated layers in high-velocity flow environment at high temperature. After exposures to high flow rate aqueous condition, the integrity of surfaces was confirmed by using both scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). For the field application, a remote process for electroless nickel-plating was demonstrated using a plate specimen with narrow gap on a laboratory scale. Finally, a practical seal design was suggested for more convenient application.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 추계학술발표회초록집
• /
• pp.11-11
• /
• 2003

Electroplated hexavalent chromium coatings have been used in many technical applications since it was invented by G.J. Sargent in 1920. Because of the environmental problems and health risks associated with the use of hexavalent chromium, there has been an extensive search for alternative coatings with properties such as corrosion resistance and wear resistance, at a reasonable cost. However there is no single substitute that meets all the desirable performance characteristics of chromium. Advanced techniques, such as alloy plating, electroless plating, trivalent chromium plating, plasma and thermal spray coating, PVD and ion implantation, have been applied for replacing hexavalent chromium plating.