• Resources Recycling
• /
• v.12 no.1
• /
• pp.18-24
• /
• 2003

Reusing of electroless Ni-Cu-B waste solution was investigated in the plating time, plating rate, solution composition and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 40% waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 6 times over than that of batch type. Plating time of 40% waste solution additive at continuous type took longer 2 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by deposited inferiority and larger decreased plating rate.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.393-397
• /
• 2003

The effects of the composition and additives on the blackening and deposition rate of electroless Ni-Zn plating have been examined. Hydrazine resulted in lower sheet resistance of the deposit than sodium hypophosphite. Zinc concentration more than 15 wt% and small amount of ammonium sulfate in the deposits were needed in obtaining Ni-Zn deposit with a black color. An optimum condition was obtained for the black Ni-Zn deposit at an appreciable deposition rate.

• Journal of the Korean institute of surface engineering
• /
• v.15 no.2
• /
• pp.57-67
• /
• 1982

Electroless Ni-plating is often utilized in industries due to its physical and mechanical characteristics in contrast to conventional electroplatings. Thus, electroless Ni-plating will be broadly applicated in many fields. However, The physial and mechanical properties of this depositss depend largely on the structure and P content of film and heat treatment. And here discused about the important results of those past research.

• Corrosion Science and Technology
• /
• v.23 no.1
• /
• pp.64-71
• /
• 2024

The objective of this study was to investigate corrosion and cavitation-erosion characteristics of the electroless nickel plating layer with heat treatment. The crystallization temperature of the electroless nickel plating layer was about 410 ℃. The phase transformation energy was confirmed to be 12.66 J/g. With increasing heat treatment temperature, the amorphous electroless nickel plating layer gradually changed to crystalline Ni and Ni₃P. At the same time, the crystal grain size was also increased. Additionally, when heat treatment was performed at a temperature above 400 ℃, NiO phase was observed due to oxidation phenomenon. As a result of the electrochemical polarization experiment, the corrosion resistance of the heat-treated electroless nickel plating layers was superior to that of the as-deposited plating layer. This was because crystal grains became larger and grain boundaries decreased during heat treatment. The cavitation-erosion resistance of heat-treated plating layers tended to be superior to that of as-deposited plating layers due to increased microhardness.

• Korean Journal of Materials Research
• /
• v.27 no.8
• /
• pp.409-415
• /
• 2017

For enhanced cavitation erosion resistance of vessel propellers, an electroless Ni-P plating method was introduced to form a coating layer with high hardness on the surface of Cu alloy (CAC703C) used as vessel propeller material. An electroless Ni-P plating reaction generated by Fe atoms in the Cu alloy occurred, forming a uniform amorphous layer with P content of ~10 wt%. The amorphous layer transformed to (Ni3P+Ni) two phase structure after heat treatment. Cavitation erosion tests following the ASTM G-32 standard were carried out to relate the microstructural changes by heat treatment and the cavitation erosion resistance in distilled water and 3.5 wt% NaCl solutions. It was possible to obtain excellent cavitation erosion resistance through careful microstructural control of the coating layer, demonstrating that this electroless Ni-P plating process is a viable coating process for the enhancement of the cavitation erosion resistance of vessel propellers.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.4
• /
• pp.328-332
• /
• 2011

The formation of front metal contact silicon solar cells is required for low cost, low contact resistance to silicon surface. One of the front metal contacts is Ni/Cu plating that it is available to simply and inexpensive production to apply mass production. Ni is shown to be a suitable barrier to Cu diffusion into the silicon. The process of Ni electroless plating on front silicon surface is performed using a chemical bath. Additives and buffer agents such as ammonium chloride is added to maintain the stability and pH control of the bath. Ni deposition rate is found to vary with temperature, time, utilization of bath. The experimental result shown that Ni layer by SEM (scanning electron microscopy) and EDX analysis. Finally, plated Ni/Cu contact solar cell result in an efficiency of 17.69% on $2{\times}2\;cm^2$, Cz wafer.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.3
• /
• pp.131-137
• /
• 2007

The typical MCFC (molten carbonate fuel cell) anode is made of Ni-10%Cr alloy. The work of this paper is focused concerning long life of anode because Ni-10% Cr anode is suffering from sintering and creep behavior during cell operation. Therefore, Ni-coated Alumina powder($20{\mu}m$) was developed by electroless nickel plating. Optimum condition of electroless nickel coation on $20{\mu}m$ alumina is as follows: pH 11.7, temperature $65{\sim}80^{\circ}C$, powder amount $100cm^2/l$. The deposition rate for Ni-electroless plating was as a function of temperature and activation energy was evaluated by Arrhenius Equation thereby activation energy calculated slope of experimental data as 117.6 kJ/mol, frequency factor(A) was $6.28{\times}10^{18}hr^{-1}$, respectively.

• Corrosion Science and Technology
• /
• v.13 no.3
• /
• pp.107-111
• /
• 2014

Electroless plated Ni-Co-P films have been used to suppress the electromagnetic waves from magnetic recording media, and the suppression is known to be achieved with films made with optimized plating composition and plating condition. Effects of complexing agents on the deposition rate and bath stability of Ni-Co-P film were studied using sodium citrate, sodium tartrate and multi-complex agents containing both of them. Deposition of electroless Ni-Co-P platings was dependent upon the complexing agents. Deposition rate was twice when using sodium tartrate compared to that using sodium citrate. And it was slightly slower with multi-complex agents than with sodium tartrate, bath stability being declined in the former. Deposition rate increased with increasing pH until pH 11. Excellent bath stability and good deposition rate were obtained using multi-complex agent as sodium citrate 0.10 mol/L and sodium tartrate 0.15 mol/L in the electroless Ni-Co-P plating films.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.250-253
• /
• 2007

An evaporated Ti/Pd/Ag contact system is most widely used to make high-efficiency silicon solar cells, however, the system is not cost effective due to expensive materials and vacuum techniques. Commercial solar cells with screen-printed contacts formed by using Ag paste suffer from a low fill factor and a high shading loss because of high contact resistance and low aspect ratio. Low-cost Ni and Cu metal contacts have been formed by using electroless plating and electroplating techniques to replace the Ti/Pd/Ag and screen-printed Ag contacts. Ni/Cu alloy is plated on a silicon substrate by electro-deposition of the alloy from an acetate electrolyte solution, and nickel-silicide formation at the interface between the silicon and the nickel enhances stability and reduces the contact resistance. It was, therefore, found that nickel-silicide was suitable for high-efficiency solar cell applications. The Ni contact was formed on the front grid pattern by electroless plating followed by anneal ing at $380{\sim}400^{\circ}C$ for $15{\sim}30$ min at $N_{2}$ gas to allow formation of a nickel-silicide in a tube furnace or a rapid thermal processing(RTP) chamber because nickel is transformed to NiSi at $380{\sim}400^{\circ}C$. The Ni plating solution is composed of a mixture of $NiCl_{2}$ as a main nickel source. Cu was electroplated on the Ni layer by using a light induced plating method. The Cu electroplating solution was made up of a commercially available acid sulfate bath and additives to reduce the stress of the copper layer. The Ni/Cu contact was found to be well suited for high-efficiency solar cells and was successfully formed by using electroless plating and electroplating, which are more cost effective than vacuum evaporation. In this paper, we investigated low-cost Ni/Cu contact formation by electroless and electroplating for crystalline silicon solar cells.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.2
• /
• pp.121-126
• /
• 2000

The effect of electroless Ni and Cu plating on $LaNi_5$, $AB_5$ type hydrogen storage alloy was investigated by the various electrochemical techniques such as constant current charge-discharge test, cyclic voltammeoy, and a.c. impedance spectroscopy. Scanning electron microscopy and X-ray diffraction test were conducted for phenomenological logical analyses. Cyclic Voltammetry results show that activation characteristics, cycle life and reaction ,rate were improved through electroless Ni and Cu plating. Compared with bare $LaNi_5$ the charge transfer resistance of electrode was greatly reduced as charge-discharge cycle increases. Therefore, electroless Ni and Cu plating on $LaNi_5$ alloy tends to accelerate the early activation, increasing the cyclic lift of electrode.