• Journal of Power System Engineering
• /
• v.17 no.4
• /
• pp.79-85
• /
• 2013

This study aims at investigating the effect of a fusing treatments on anti-corrosion characteristics of Ni-based self-flux alloy coating. Ni-based coatings were fabricated by flame spray process on steel substrates, and fusing treatments were performed using a vacuum furnace at $800^{\circ}C$ $900^{\circ}C$, $1000^{\circ}C$ and $1100^{\circ}C$. After fusing treatments, corrosion tests were carried out using potentiostat/galvanostat at solution with pH 2 and pH 6. Corrosion potential(Ecorr) and corrosion current density(Icorr) could be analyzed from polarization curve. Fusing-treated coating at $1100^{\circ}C$ showed more favorable anti-corrosion characteristics than as-sprayed coating. Anticorrosive effect of fusing-treated coating at solution with pH 2 was relatively greater than at solution with pH 6. Fusing-treated coating at $1100^{\circ}C$ showed the most excellent anti-corrosion characteristics.

• Korean Journal of Materials Research
• /
• v.27 no.8
• /
• pp.409-415
• /
• 2017

For enhanced cavitation erosion resistance of vessel propellers, an electroless Ni-P plating method was introduced to form a coating layer with high hardness on the surface of Cu alloy (CAC703C) used as vessel propeller material. An electroless Ni-P plating reaction generated by Fe atoms in the Cu alloy occurred, forming a uniform amorphous layer with P content of ~10 wt%. The amorphous layer transformed to (Ni3P+Ni) two phase structure after heat treatment. Cavitation erosion tests following the ASTM G-32 standard were carried out to relate the microstructural changes by heat treatment and the cavitation erosion resistance in distilled water and 3.5 wt% NaCl solutions. It was possible to obtain excellent cavitation erosion resistance through careful microstructural control of the coating layer, demonstrating that this electroless Ni-P plating process is a viable coating process for the enhancement of the cavitation erosion resistance of vessel propellers.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.857-863
• /
• 2017

In this paper, the process of electro Ni and electro Cr plating is studied for the purpose of thermal barrier to protect the inner wall combustion chamber. The chamber is under the environment of very high temperature and high pressure when propellants burn in there. As one of the thermal barrier coatings, Zr-based thermal spray coating has been applied to the chamber. However, peeling of coating layer can occur under such a hard condition because of the difference of thermal expansion coefficients between the ceramic and the metallic wall. We study the characteristics of Ni-Cr coating and establish its process. It is found that the thickness of over $100{\mu}m$ of Ni and Cr coating layers with the uniformity of ${\pm}10%$ can be obtained with the used of as-developed plating bath.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.14 no.5
• /
• pp.45-50
• /
• 2010

Thermal analyses have been performed to study the effect of location of fuel ring and thermal barrier coatings in regenerative cooling channels in a full-scale combustor. For the effective cooling, the fuel ring has better be installed near axial location of the low expansion ratio and low heat flux, and branching of cooling channels is preferable. Also, the radiative cooled nozzle extension is thought to be reasonable for the cooling of combustor walls. Among the possible coatings, $Y_2O_3$ stabilized $ZrO_2$ coating and Ni/Cr coating have been adopted. Compared with Ni/Cr coating which has high oxidation resistance, $Y_2O_3$ stabilized $ZrO_2$ coating, one of ceramic coatings is found to be much effective to sustain the thermal survivability of combustion walls.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2010.05a
• /
• pp.145-149
• /
• 2010

Thermal analyses have been performed to study the effect of location of fuel ring and thermal barrier coatings in regenerative cooling channels in a full-scale combustor. For the effective cooling, the fuel ring has better be installed near axial location of the low expansion ratio and low heat flux, and branching of cooling channels is preferable. Also, the radiative cooled nozzle extension is thought to be reasonable for the cooling of combustion walls. Among the possible coatings, $Y_2O_3$ stabilized $ZrO_2$ coating and Ni/Cr coating have been adopted. Compared with Ni/Cr coating which has high oxidation resistance, $Y_2O_3$ stabilized $ZrO_2$ coating, one of ceramic coatings is found to be much effective to sustain the thermal survivability of combustion walls.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.4
• /
• pp.157-160
• /
• 2009

Many fundamental studies have been carried out regarding waste water and hazardous gas treatments technologies using the photolysis effect of $TiO_2$. However, a permanent use of $TiO_2$ particles immobilized using organic or organic-inorganic binders is impossible. In this study, Ni-$TiO_2$ composite coating was produced by electroless plating to trap $TiO_2$ particles in the Ni coating layer. The electroless plating was performed in the bath solutions with three different concentrations of $TiO_2$ particles : 10 g/l, 20 g/l, and 40 g/l. The surface and photolytic characteristics of the coating layer was investigated by the use of SEM, a scratch tester, and an UV-Visible spectrophotometer. The results showed that the amounts of immobilized $TiO_2$ particles and the photolytic rate of the coating increased with the initial content of $TiO_2$ particles in the electroless bath. In addition, the photolytic rate of the Ni-$TiO_2$ composite coating was remarkably promoted by etching process in 10% HCl solution.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.4
• /
• pp.171-177
• /
• 2021

This paper is concerned with the surface hardness measurement of NiP-coated AA7050 using different loads from 10 to 100 g. The surface hardness was observed to increase from 180 to 600 H_v with increasing NiP layer thickness, depending on the load applied for indentation. When NiP coating thickness is thinner than 2 ㎛, the surface hardness of NiP-coated AA7050 was mainly determined by AA7050 substrate, while it was significantly increased by NiP coating layer when NiP coating thickness is thicker than 2 ㎛. Hardness of AA7050 substrate itself was not dependent on the applied load but the hardness of NiP-coated AA7050 was largely influenced by the load applied for indentation. The largest difference of hardness between 10 g and 100g of applied loads, was obtained at the NiP thickness of about 8 ㎛ above which the measured hardness at 10 g reached a maximum value of about 600 H_v. It was also observed that indentation-induced plastic deformation next to the indented zone occurs when NiP layer is 5.64 times thicker than the depth of impression formed by indentation.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.278-281
• /
• 2009

Selective laser sintering(SLS), a kind of rapid prototyping technology, can provide a process to form many types of coatings. Coated layers by selective laser melting are highly influenced by substrate, powder and laser parameters such as laser power, scan rate, fill spacing and layer thickness. Therefore an attempt to fabricate Fe-Ni-Cr coating on AISI H13 tool steel has been performed by selective laser sintering. In this study, Fe-Ni-Cr coating was produced by experimental facilities consisting of a 200W fiber laser which can be focused to 0.08mm and atmospheric chamber which can control atmospheric pressure with Ar. With power increase or energy density decrease, line width was decreased and line surface quality was improved with energy density increase. Surface quality of coating layer was improved with fill spacing optimization or layer thickness decrease.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.2
• /
• pp.103-108
• /
• 2006

Microstructural evolution of Pt-aluminide coated Ni-based superalloy has been investigated with ductilization heat treatment. The Pt coat was prepared on the superalloy and then aluminide coating was conducted using a pack cementation process. Samples were heat-treated at $1050^{\circ}C$ for 2 hrs and the microstructure and element analysis were preformed. A various precipitated compounds were observed within the coating layer and the diffusion region in the Pt-aluminide coating and heat treatment, indicating that the bi-phase compounds of $PtAl_2$ and NiAl were performed during the Pt-aluminide coating, whereas $M_{23}C_6$, MC, $Ni_3Al$ and ${\sigma}$ phases were precipitated in the inter-diffusion region. The bi-phase compounds of $PtAl_2$ and NiAl were transformed into the single phase compound of $PtAl_2$ with the heat treatment, increasing the amount of carbide and ${\sigma}$ phase.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.692-693
• /
• 2006

Behavior of stoichiometric and near-stoichiometric NiAl at plasma spray deposition, without and with a bond coat, for coating layers realization on a low alloyed steel substrate, has been investigated. In all variants, NiAl particle melting and subsequent welding at the impact with substrate were observed, forming a relatively compact and adherent coating layer with the NiAl stability maintaining - all assuring the coating layer oxidation and corrosion resistance. Good results from these points of view, also validated through corrosion tests, were obtained for 45:55 Ni:Al composition without a bond coat but adopting an Ar protective surrounding of plasma jet.