This study examined the feasibility of the combining HDDR-process (hydrogenation, disproportionation, desorption and recombination) with mechanical milling to prepare single domain $Nd_2Fe_{14}B$ particles from a Nd-Fe-B alloy ingot. The $Nd_{15}Fe_{77}B_8$ alloy was HDDR-treated and then subjected to a roller-milling. In the HDDR-treated $Nd_{15}Fe_{77}B_8$ alloy, very small $Nd_2Fe_{14}B$ grains comparable to their critical single domain size(0.3 ${\mu}m$) were observed. These fine individual grains were separated successfully along the grain boundaries by a roller-milling. The separated $Nd_2Fe_{14}B$ grains were found to be single domain particles. These results suggest that single domain particles of the $Nd_2Fe_{14}B$ phase can be prepared from a Nd-Fe-B ingot alloy by combining a HDDR-process with mechanical milling.

• 한국자기학회지
• /
• 제22권3호
• /
• pp.85-90
• /
• 2012

$Nd_2Fe_{14}B$ 화합물 결정의 산화 및 미세 $Nd_2Fe_{14}B$ 결정입자의 보자력에 미치는 산화의 영향을 조사하였다. $Nd_2Fe_{14}B$ 화합물 결정의 산화속도는 $Nd_{15}Fe_{77}B_8$ 합금 잉곳 중의 과잉 성장시킨 $Nd_2Fe_{14}B$ 결정립을 이용하여 조사하였다. $Nd_2Fe_{14}B$ 화합물 결정의 산화는 이 결정상의 ${\alpha}$-Fe, $Fe_3B$, 및 Nd 산화물 복합상으로의 분해에 의해 일어 났다. $Nd_2Fe_{14}B$ 화합물 결정의 산화속도는 결정 방위와는 무관하였다. 산화반응 속도 식은 단순한 직선관계로 나타났다. $Nd_2Fe_{14}B$ 화합물 결정의 산화에 대한 활성화에너지는 약 26.8 kJ/mol로 계산되었다. HDDR 처리한 $Nd_{15}Fe_{77}B_8$ 합금을 볼밀링하여 임계단자구 크기에 유사한 미세한 $Nd_2Fe_{14}B$ 결정입자를 제조하고, 이 입자들을 이용하여 보자력에 미치는 산화의 영향을 조사하였다. 임계단자구 크기에 유사한 미세한 $Nd_2Fe_{14}B$ 결정입자(${\fallingdotseq}0.3\;{\mu}m$)는 9 kOe 이상의 높은 보자력을 가졌다. 그러나, 이 보자력은 공기 중에서 온도 상승에 따라 급격하게 저하하였다($200^{\circ}C$에서 2 kOe 이하). 이러한 급격한 보자력의 감소는 산화에 의해 미세 입자의 표면에 형성된 연자성 ${\alpha}$-Fe 및 $Fe_3B$ 상 때문으로 판단되었다.

• Journal of Magnetics
• /
• 제9권2호
• /
• pp.27-33
• /
• 2004

Magnetic properties of $Nd_4Fe_{77.5}B_{18.5}$ compound in term of exchange coupling between $Nd_2Fe_{14}B$ and $Fe_3B$ magnetic nano crystals in melt spun powders were characterized by varying the quenching speed in mass production line. The exchange coupled phenomenon was characterized as functions of nano crystal size and volume fraction of each magnetic phase which was possible by employing Henkel plot (${\delta}M$) and refined Mossbauer spectroscopy. The optimized magnetic properties obtained from the present volume production line were: $B_r= 11.73 kG,{_i}H_c/ = 3.082 kOe$, and $(BH)_{max} = 12.28 MGOe.$ The volume fraction of each magnetic phase for those conditions giving the grain size of 10 nm were ${\alpha}-Fe; 4.2%, Fe_3B; 60.1 %$, and $Nd_2Fe_{14}B; 35.7%$. The superior magnetic properties in the $Nd_2Fe_{14}Fe_3B$ based nanocomposites were confirmed to be dependant on the volume fraction of $Fe_3B$.