• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 하계학술대회 논문집 D
• /
• pp.1352-1354
• /
• 1998

$LiNbO_3$ transistor showed relatively stable characteristic, low interface trap density, and large remanent polarization. This paper reports ferroelectric $LiNbO_3$ thin films grown directly on p-type Si(100) substrates by 13.56 MHz rf magnetron sputtering system for FRAM applications. To take advantage of low temperature requirement for growing films, we deposited $LiNbO_3$ films lower than $300 ^{\circ}C$. RTA(Rapid Thermal Anneal) treatment was performed for as-deposited films in an oxygen atmosphere at $600^{\circ}C$ for 60 sec. We learned from X-ray diffraction that the RTA annealed films were changed from amorphous to poly-crystalline $LiNbO_3$ which exhibited (012), (015), and (022) orientations. The I-V characteristics of $LiNbO_3$ films before and after anneal treatment showed that RTA improved the leakage current of films. The leakage current density of films decreased from $10^{-5}$ to $10^{-7} A/cm^2$ at room temperature measurement. Breakdown electric field of the films exhibited higher than 500 kV/cm. The C-V curves showed the clockwise hysteresis represents ferroelectric switching characteristics. From C-V curves, we calculated dielectric constant of thin film $LiNbO_3$ as 27.5 which is close to that of bulk value.

• 한국재료학회지
• /
• 제11권10호
• /
• pp.879-888
• /
• 2001

The effects of final annealing temperature on the microstructure and creep characteristics were investigated for the Zr-lNb-0.2X (X=0, Mo, Cu) and Zr-lNb- 1Sn-0.3Fe-0.1X (X=0, Mo, Cu) alloys. The microstructures were observed by using TEM/EDS, and grain size and distributions of precipitates were analyzed using a image analyzer. The creep test was performed at $400^{\circ}C$ under applied stress of 150 MPa for 10 days. The $\beta$-Zr was observed at annealing temperature above $600^{\circ}C$. In the temperature above$ 600^{\circ}C$, the grain sizes of both alloy systems appeared to be increased with increasing the final annealing temperature. The creep strengths of Zr-1Nb-1Sn-0.3Fe-0.1X alloys were higher than those of Zr-1Nb-0.2X ones due to the effect of solid solution hardening by Sn in Zr-lNb-lSn-0.3Fe-0.1X alloy system. Also, Mo addition showed the strong effect of precipitate hardening in both alloy systems. The creep strength rapidly decreased with increasing the annealing temperature up to $600^{\circ}C$. However, a superior creep resistance was obtained in the sample that annealed to have a second phase of $\beta$-Zr. It was considered that the appearance of $\beta$-Zr would play an important role in the strengthening mechanism of creep deformation.

• 한국세라믹학회지
• /
• 제38권4호
• /
• pp.308-313
• /
• 2001

We report the effects of the V$_2$O$_{5}$ additive on the sintering behavior and microwave dielectric properties of ZnNb$_2$O$_{6}$ ceramics. Densification temperatures of V$_2$O$_{5}$-doped ZnNb$_2$O$_{6}$ samples are lowered to the range of 875-9$25^{\circ}C$ because of the liquid phase sintering. Doped samples are composed of a Zn(Nb,V)$_2$O$_{6}$ solid solution and second phases. Up to 5 wt% V$_2$O$_{5}$ is the only second phase, however, V$_2$O$_{5}$ also exists as the second phase for 10 wt% V$_2$O$_{5}$ addition. In comparison with reported values of undoped ZnNb$_2$O$_{6}$ ceramics, microwave properties of V$_2$O$_{5}$-doped ZnNb$_2$O$_{6}$ samples are seriously degraded, which is confirmed to originate from the second phases. The optimum microwave properties (Q$\times$f=13,800, $\varepsilon$$_{r}$=23, $\tau$$_{f}$=-66ppm/$^{\circ}C$) are obtained from ZnNb$_2$O$_{6}$ with the addition of 5 wt% V$_2$O$_{5}$ sintered at 90$0^{\circ}C$.90$0^{\circ}C$.EX>.

• 한국해양공학회지
• /
• 제25권4호
• /
• pp.66-71
• /
• 2011

The flexural strength of $MoSi_2$ based composites reinforced with Nb sheets has been investigated, based on the detailed examination of their microstructure and fractured surface. Both sintered density and porosity of Nb/$MoSi_2$ composites were also examined. Nb/$MoSi_2$ composites were fabricated by different conditions such as temperature, applied pressure and its holding time, using a hot-press device. The volume fraction of Nb sheet in this composite system was fixed as 10%. The characterization of Nb/$MoSi_2$ composites were investigated by means of optical microscopy, scanning electron microscope and three point bending test. Nb/$MoSi_2$ composites represented a dense morphology at the interfacial region, accompanying the creation of two types of reaction layer by the chemical reaction of Nb and $MoSi_2$. Nb/$MoSi_2$ composites possessed an excellent density at the fabricating temperature of $1350^{\circ}C$, corresponded to about 95% of theoretical density. The flexural strength of Nb/$MoSi_2$ romposites were greatly affected by the pressure holding time at the same fabricating temperature, owing to the large suppression of porosity in the microstructure. Especially, Nb/$MoSi_2$ composites represented a good flexural strength of about 310 MPa at the fabricating condition of $1350^{\circ}C$, 30MPa and 60min, accompanying the pseudo-ductile fracture behavior by the deformation of Nb sheet and the interfacial delamination.

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.116-121
• /
• 1999

MgO 단결성 (100) 기판 위에 0.5 wt% Nb 첨가된 전기전도성의 SrTiO3 (Nb:STO) 박막을 Pulsed Laser Deposition 법으로 제조하였다. 산소압력, 타겟과 기판거리, 기판온도, 박막증착시간 등의 박막형성 조건을 다양하게 변화시켜 Nb:STO박막의 격자상수와 박막두께의 변화를 조사하였다. $700^{\circ}C$에서 제작한 0.5 wt% Nb doped SrTiO3 박막의 배향성은 산소분압변화에 따라(100), (110)과 (111)배향이 관찰되었고, 박막제조시의 산소분압이 79.8 Pa로 증가됨에 따라 격자상수는 감소하여 벌크값인 0.390 nm에 근접하였다. 증착시간증가에 따른 박막의 두께는 증착시간에 비례하여 증가하였고, 격자상수의 변화는 거의 없었다. 타겟과 기판사이의 거리가 멀어짐에 따라 박막의 두께는 감소하였으나, 격자상수에는 큰 변화가 없었고 박막두께분포의 균일성이 향상되었다.

• 소성∙가공
• /
• 제17권5호
• /
• pp.364-372
• /
• 2008

In this study, the circumferential creep behaviors ofpilgered advanced Zirconium alloy tubes such as Zr-Nb-O and Zr-Nb-Sn-Fe were investigated in the temperature range of $400\sim500^{\circ}C$ and in the stress range of 80$\sim$150MPa. The test results indicate that the stress exponent for the steady-state creep rate of the Zr-Nb-Sn-Fe alloy decreases with the increase of stress(from 6$\sim$7 to 4), while that of the Zr-Nb-O alloy is nearly independent of stress(5$\sim$6). The activation energy of creep deformation is found to be nearly the same as the activation energy for Zr self diffusion. This indicates that the creep deformation may be controlled by dislocation climb mechanism in Zr-Nb-O. On the other hand, the transition of stress exponent(from 6-7 to 4) in Zr-Nb Sn-Fe strongly suggests the transition of the rate controlling mechanism at high stresses. The lower stress exponent at high stresses in Zr-Nb-Sn-Fe can be explained by the dynamic deformation aging effect caused by interaction of dislocations with Sn substitutional atoms.

• 공업화학
• /
• 제5권5호
• /
• pp.862-870
• /
• 1994

출발물질로 $Pb(NO_3)_2$, $Mg(NO_3)_2$, $NbCl_5$를 선정하여 이들을 수용액상으로 $Pb(Mg_{1/3}Nb_{2/3})O_3$조성에 맞도록 각 수용액을 정확히 취하여 $Pb(Mg_{1/3}Nb_{2/3})O_3$ 1M용액이 되도록 조제하였다. 이 혼합용액은 상온에서 $PbCl_2$를 형성하므로 $70^{\circ}C$로 가열하여 $PbCl_2$를 용해시킨 후, 침전제 oxine을 가하여 pH 8~10에서 공침물을 얻었다. 이 침전물을 여과, 건조의 공정을 거처 $700{\sim}1000^{\circ}C$로 5시간 하소하여 $Pb(Mg_{1/3}Nb_{2/3})O_3$을 합성하였으며 합성된 분말은 평균입경이 $0.3{{\mu}m}$ 정도이고 모양은 구형이었다. 그리고 합성된 분말을 $2000Kg/cm^2$의 압력으로 성형하고, $1100{\sim}1200^{\circ}C$로 소성하여 이론밀도의 97.4%인 소결체를 얻었고 이때의 유전율은 1kHz에서 17000이고 유전손실은 상온에서 0.02%이었다.

• 한국식품조리과학회지
• /
• 제32권1호
• /
• pp.50-57
• /
• 2016

본 연구는 김부각(KB), 쑥부쟁이 나물부각(SB), 쑥부쟁이 나물김부각(NB)을 제조하여 품질특성을 조사하였다. NB는 쑥부쟁이 나물을 잘게 썰어 들깨 양념하여 김에 부착시켜 찹쌀풀을 발라 부각으로 제조 한 후 동결 건조하였다. KB보다 SB와 NB의 기름 흡유율이 높아 나물의 기름 흡수가 많았다. SB의 DPPH radical 소거능이 가장 높게 측정되었으며 KB 보다는 NB가 높게 측정되어 나물이 김보다 항산화능이 높았다. 저장기간이 길어질수록 수분함량은 증가하는 반면 최대하중, 항복응력 및 경도는 감소하는 경향이었다. 전반적인 기호도는 NB>KB>SB 순이었고, NB와 SB 간 유의한 차이가 있었다. $25^{\circ}C$에서 40일 저장한 NB의 산가 및 과산화물가는 점차 증가하는 경향이었으나, 산패의 기준에는 못 미쳤다. 따라서, $25^{\circ}C$ 이하에서 40일까지는 저장 가능할 것으로 판단되며, 쑥부쟁이뿐만 아니라 기능성이 입증된 다양한 나물을 첨가한 부각을 제조한다면 다양한 소비자 기호도를 충족시킬 수 있는 부각제조가 가능할 수 있을 것으로 본다.

• 한국재료학회지
• /
• 제11권2호
• /
• pp.104-114
• /
• 2001

Zr-Sn-Nb 합금의 재결정에 미치는 Nb과 Sn의 첨가영향을 연구하기 위해 냉간압연한 시편을 $300^{\circ}C$~75$0^{\circ}C$의 온도구간에서 열처리한 후에 미소경도와 TEP (Thermoelectric Power)를 측정하여 재결정 거동을 조사하였으며 광학현미경, 주사전자 현미경 (SEM), 투과전자현미경 (TEM)으로 미세조직을 관찰하였다 미소경도 및 미세조직의 분석 결과에 따르면, Nb과 Sn의 첨가에 의해 재결정 활성화 에너지가 증가하여 재결정이 지연되었으며, 재결정 완료 이후의 결정립 성장도 억제되었음을 관찰하였다. Zr내의 고용도가 매우 낮은 Nb의 첨가는 석출물을 쉽게 형성하는 반면에 고용도가 비교적 큰 Sn은 기지상 내에 대부분 고용되어 석출물의 양이 매우 작았으나, Sn 첨가에 의한 재결정의 지연 효과가 더욱 컸다. Nb보다 Sn의 첨가가 Zr 합금의 재결정 거동을 효과적으로 지연시킨 것은 고용도가 높은 SR에 의한 치환형 고용체 형성과정에서 발생된 응력장이 전위의 이동을 효과적으로 억제했기 때문으로 생각된다. 한편, 회복과 재결정이 진행됨에 따라 전자 산란인자의 감소로 TEP는 증가하였으며, 재결정이 완료되면 TEP의 포화가 발생하였다. 석출물의 형성은 석출물 주변의 용질농도 감소로 인한 전자 산란인자의 감소에 기인하여 TEP의 증가를 가져왔다

• 한국가스학회지
• /
• 제24권5호
• /
• pp.39-46
• /
• 2020

본 논문에서는 파이프라인에서 사용되는 API 5L 철강의 중심선 편석에 대해 다루고자 한다. Mn/S와 Nb 그리고 C는 파이프 두께 방향으로의 중심선에서 편석되는 요소로 알려져 있다. Mn은 일반적으로 긴 점성상을 이루는 S를 동반한다. 중심선의 미세조직은 MnS와 산소를 포함한 Nb/Ti로 구성되어 있는데 이 중심선 지역의 편석효과를 OM, SEM/EDS 및 마이크로비커스 경도기로 분석하였다. Mn, Nb 및 C는 오스테나이트가 페라이트 또는 마르텐사이트로 변태하는 것을 억제시키는 원소이다. 이러한 원소들은 마르텐사이트의 한 종류인 베이나이트 미세조직을 만들 수 있는데 이는 용융 및 열처리에서 얻어지는 중심선과 매트릭스 간의 원소 편석과는 다르다.