• Journal of the Korean Ceramic Society
• /
• v.36 no.7
• /
• pp.742-750
• /
• 1999

Nanosized TiO2 powders were synthesized using the chemical vapor conduensation (CVC) process with various precursor feeding rates (0.37 and 0.752 ml/min) and oxygen flow rates(1-2slm) conditions and powder characteristics were investigated in terms of formation of nanosized powder varying with the above processing conditions. For this study the main thermodynamic and fluid dynamic factors -supersaturation ratio collision frequency and residence time-were theoretically established and compared to the characteristics of formed TiO2 powder. The loosely combined anatase phase powders (including less than 3%of rutile phase) having 20-30nm crystallite size were obtained at overall conditions. The particle size and th degree of agglomeration for a precursor flow rate of 0.376 ml/min turn out to be smaller than for a flow rate of 0.742ml/min. And the decreasing of particles size and particle size distribution were observed with increasing oxygen flow rate as the residence time and collision frequency were reduced by increasing oxygen flow rate,. It appears that further scrutiny is needed to elucidate the influence of the individual thermodynamic and kinetic parameters mdependently.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.251-255
• /
• 2009

Nanocomposites based on coupling $TiO_2$ matrix with nanosized noble metals (Pt,Au) particles exhibited promising photoelectrode properties. The $M/TiO_2$ (M=Pt,Au) nanocomposite thin films were deposited on quartz and ITO glass substrates using a co-sputtering method. $TiO_2$ in rutile form is the dominant crystalline phase for as-deposited nanocomposite films. Along with heat treatment up to $600^{\circ}C$, XRD peaks of the rutile phase as well as those of noble metal increased in intensity and decreased in width, indicating the growth of crystallites. The anodic photocurrents of $M/TiO_2$ (M=Au,Pt) thin films were observed not only in the UV range but also in the visible light range. The photocurrent of the nanocomnosite films extended to the visible light region by dispersion of nano-sized noble metal in the $TiO_2$ matrix.

• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.426-431
• /
• 2013

Nanosized $TiO_2$ particles were prepared from titanium (IV) sulfate solution using base solutions at low reaction temperature ($95^{\circ}C$) and atmospheric pressure by hydrothermal precipitation method without calcination. The effects of preparation conditions, such as kind of base solutions (NaOH, $NH_4OH$, Monoethanolamine, Diethanolamine, Triethanolamine) and surfactants (CTAB, Span 20, SDBS), concentration of surfactants, temperature and pH, on the physical properties of $TiO_2$ particles have been investigated by XRD, SEM and Zeta-potential meter. Absorption area was also investigated by DRS in order to confirm the photocatalytic activity of the nanosized $TiO_2$ particles. It was turned out that, among base solutions, NaOH provides the smallest $TiO_2$ particles with excellent crystallinity. And cationic surfactant (CTAB) prepared smaller $TiO_2$ particles than any other surfactants. When CTAB is added in the concentration ratio of $Ti(SO_4)_2$:CTAB=10:1, $TiO_2$ particles with particle diameter of 5.8 nm were prepared. This is approximately 1/10 of that prepared without CTAB.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.11a
• /
• pp.5.2-5.2
• /
• 2008

• Journal of Environmental Science International
• /
• v.14 no.9
• /
• pp.889-896
• /
• 2005

The nanosized $TiO_2$ photocatalysts were prepared by the hydrolysis of $TiCl_4$ and calcined at different temperatures. The resulting materials were characterized by TGA, DSC, XRD, and TEM testing techniques. XRD, TEM, and BET measurements indicated that the particle size of $TiO_2$ was increased with rise of calcination temperature and surface area was decreased with rise of it. The prepared $TiO_2$ photocatalysts were used for the photocatalytic degradation of congo red. The effects of calcination temperature, $TiO_2$ loading, the initial concentration of congo red, and usage frequencies were investigated and the rate constants were determined by regressing the experimental data. Calcination is an effective treatment to increase the photo activity of nanosized $TiO_2$ photocatalysts resulting from the improvement of crystallinity. The optimum calcination temperature of the catalyst for the efficient degradation of congo red was found to be $400^{\cric}C$. The rate constant was decreased with increase in the initial concentration of congo red and increased with increase in the $TiO_2$ loading. In the case of $TiO_2$ photocatalysts, the photocatalytic activity wasn't greatly affected by the usage frequencies.

• Journal of Electrochemical Science and Technology
• /
• v.10 no.2
• /
• pp.148-158
• /
• 2019

The corrosion protection of AA2024 PPy coated samples doping with nanosized metal oxides, including $TiO_2$ and $CeO_2$ nanoparticles and $Nd_2O_3$ nanorods, during exposure to the solutions of 0.1 M $H_2SO_4$ and 3.5% NaCl was evaluated by electrochemical impedance spectroscopy (EIS) and linear polarization resistance (LPR) techniques. The nanorods of $Nd_2O_3$ were synthesized by cathodic pulse electrochemical deposition technique. The barrier properties of the different PPy coatings containing nanosized metal oxides immersed in $H_2SO_4$ solution were ranked as follows: $Nd_2O_3$ > $TiO_2$ > $CeO_2$. Therefore, the $Nd_2O_3$ coating sample provided the highest corrosion protection at any time of immersion up to 72 hours after immersing in $H_2SO_4$ solution. On the other hand, the $CeO_2$ coating sample displayed the best anticorrosive properties among the other coating samples after immersion in NaCl solution up to 28 days. This is due to the inhibition effect of cerium ions on aluminum alloys at near-neutral solutions.

• Bulletin of the Korean Chemical Society
• /
• v.19 no.11
• /
• pp.1185-1188
• /
• 1998

Layered nanocomposite, SiO2/TiO2 sol pillared clay, has been prepared by the ion exchange reaction of Na' ion in montmorillonite with positively charged mixed SiO2/TiO2 sol. The nanosized sol particles were synthesized by mixing SiO2 sol solution with TiO2 one, which is obtained by acidic hydrolysis of TEOS and TiCl4, respectively. From powder XRD, the basal spacing (d001) of the sample calcined at 400 ℃ was found to be ca. 60 Å, due to the multistacking of nanosized SiO2 and TiO2 sol particles, which was confirmed by the pore size analysis from 129Xe NMR and micropore analysis calculated from nitrogen adsorption. The BET specific surface area shows the value of 684 m2g-1 (Langmuir 1115 m2g-1), which is the highest among various pillared clays ever reported previously, and the total porosity is found to be 0.51 mlg-1, and the pores are mainly composed of micropore with a size of ca. 11.8 Å. This result agrees with the adsorption capacity obtained from water adsorption. According to diffuse reflectance ultraviolet-visible spectroscopy, it is found that the TiO2 particles stabilized in the interlayer space of montmorillonite are quantum-sized of ca. 20 Å.

• Clean Technology
• /
• v.20 no.1
• /
• pp.28-34
• /
• 2014

In this study, we synthesized $TiO_2$ supports with nanosized crystalline structure by solvothermal method and prepared $TiO_2$ supported Pd-Cu catalysts. It was shown that the crystalline size of $TiO_2$ support in the catalyst influenced on the catalytic activity of nitrate reduction in water. The catalyst with the smaller crystalline size of $TiO_2$ support presented faster nitrate reduction rate, but had low nitrogen selectivity due to high pH environment of reaction medium during the reaction. Through injection of carbon dioxide as a pH buffer, the nitrogen selectivity increased by about 60%. Furthermore, we investigated that the relationships between the catalytic performance and the physicochemical properties of the prepared catalysts characterized by $N_2$ adsoprtion-desorption, X-ray diffraction (XRD), $H_2$-temperature programmed reduction (TPR), X-ray photoelectron spectroscopy (XPS).

• Journal of Powder Materials
• /
• v.29 no.3
• /
• pp.207-212
• /
• 2022

Nanosized rutile titanium dioxide (TiO₂) is used in inorganic pigments and cosmetics because of its high whiteness and duality. The high quality of the white pigments depends on their surface coating technique via the solgel process. SiO₂ coatings are required to improve the dispersibility, UV-blocking, and whiteness of TiO₂. Tetraethyl orthosilicate (TEOS) is an important coating precursor owing to its ability to control various thicknesses and densities. In addition, we use Na₂SiO₃ (sodium silicate) as a precursor because of its low cost. Compared to TEOS, which controls the pH using a basic catalyst, Na₂SiO₃ controls the pH using an acid catalyst, giving a uniform coating. The coating thickness of TiO₂ is controlled using a surface modifier, cetrimonium bromide, which is used in various applications. The shape and thickness of the nanosized coating layer on TiO₂ are analyzed using transmission electron microscopy, and the SiO₂ nanoparticle behavior in terms of the before-and-after size distribution is measured using a particle size analyzer. The color measurements of the SiO₂ pigment are performed using UV-visible spectroscopy.

• Korean Chemical Engineering Research
• /
• v.48 no.4
• /
• pp.417-422
• /
• 2010

Nanosized $TiO_2$ particles were prepared by hydrothermal method from the aqueous peroxotitanate solution using the different carboxylic acids as an additives. The physical properties of prepared nanosized $TiO_2$ particles were investigated and we also examined the activity of $TiO_2$ particles as a photocatalyst on the decomposition of methylene blue. The major phase of all the prepared $TiO_2$ particles was an anatase structure regardless of carboxylic acids and a rutile peak was observed above $700^{\circ}C$. The photocatalytic activity increased with an increase of hydrocarbon number of carboxylic compounds and the highest activity was shown on the catalysts which was prepared using succinic acid as an additive and calcined at $500^{\circ}C$.