• Applied Microscopy
• /
• v.27 no.4
• /
• pp.473-481
• /
• 1997

Disorder-order transformation of nanocrystalline FeAl have been investigated by a combination of electron and X-ray diffraction analysis including high resolution electron microscopy and differential scanning calorimetry. Fe-50at.%Al powders mechanically alloyed for 90 hours consist of $5\sim10$ nm size grains haying either disordered b.c.c. structure or amorphous structure. X-ray and electron diffraction of mechanically alloyed FeAl powders show that disorder-order transformation occurs at the temperature range of $300^{\circ}C\sim320^{\circ}C$. Such a low-temperature ordering behavior exhibiting an exothermic reaction is attributable to the nm-scale grain structure with a large amount of defects accumulated during mechanical alloying process.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.6
• /
• pp.266-270
• /
• 2010

The effect of an Ar plasma treatment on polycarbonate substrates was investigated using $TiO_2$ coatings produced by reactive ion-beam assisted sputtering. The typical pressure used during sputtering was about $10^{-4}$ Torr. After the Ar plasma treatment, the contact angle of a water droplet was reduced from $88^{\circ}$ to $52^{\circ}$ and then further decreased to $12^{\circ}$ with the addition of oxygen into the chamber. The surface of the polycarbonate substrate hanged from hydrophobic to hydrophilic with these treatments and revealed its changing nano-scale roughness. The $TiO_2$ films on the treated surface showed various colors and periodic ordering dependant on the film thickness due to optical interference.

• Korean Journal of Materials Research
• /
• v.23 no.3
• /
• pp.190-193
• /
• 2013

Spatial distributions of alloying elements of an Fe-based amorphous ribbon with a nominal composition of $Fe_{75}C_{11}Si_2B_8Cr_4$ were analyzed through the atom probe tomography method. The amorphous ribbon was prepared through the melt spinning method. The macroscopic amorphous natures were confirmed using an X-ray diffractometer (XRD) and a differential scanning calorimeter (DSC). Atom Probe (Cameca LEAP 3000X HR) analyses were carried out in pulsed voltage mode at a specimen base temperature of about 60 K, a pulse to base voltage ratio of 15 %, and a pulse frequency of 200 kHz. The target detection rate was set to 5 ions per 1000 pulses. Based on a statistical analyses of the data obtained from the volume of $59{\times}59{\times}33nm^3$, homogeneous distributions of alloying elements in nano-scales were concluded. Even with high carbon and strong carbide forming element contents, nano-scale segregation zones of alloying elements were not detected within the Fe-based amorphous ribbon. However, the existence of small sub-nanometer scale clusters due to short range ordering cannot be completely excluded.