• Elastomers and Composites
• /
• 제43권1호
• /
• pp.1-7
• /
• 2008

DSC 및 컴파운드 온도 측정을 통해 원적외선에 의한 EPDM의 가교 반응을 연구하였으며, 특히 동일 조건에서의 열풍에 의한 가교 시험을 통해 원적외선 가교시의 효율성을 평가하였다. 원적외선 및 열풍에 의한 EPDM 컴파운드의 가교도를 분석한 결과, 동일 조건에서 원적외선가교 시료의 가교도가 열풍가교에 비해 높게 나타남을 확인할 수 있었으며, 특히 3 mm 두께 시편의 경우 약 2배가량 높은 가교도를 나타내었다. EPDM 컴파운드의 열전도도의 증가는 원적외선에 의한 가교도를 크게 증가시켰으나, 열풍에 의한 가교도의 변화에는 거의 영향을 주지 못하였다.

• Advances in nano research
• /
• 제12권5호
• /
• pp.529-547
• /
• 2022

Graphene is one of the strongest, stiffest, and lightest nanoscale materials known to date, making it a potentially viable and attractive candidate for developing lightweight structural composites to prevent high-velocity ballistic impact, as commonly encountered in defense and space sectors. In-plane twist in bilayer graphene has recently revealed unprecedented electronic properties like superconductivity, which has now started attracting the attention for other multi-physical properties of such twisted structures. For example, the latest studies show that twisting can enhance the strength and stiffness of graphene by many folds, which in turn creates a strong rationale for their prospective exploitation in high-velocity impact. The present article investigates the ballistic performance of twisted bilayer graphene (tBLG) nanostructures. We have employed molecular dynamics (MD) simulations, augmented further by coupling gaussian process-based machine learning, for the nanoscale characterization of various tBLG structures with varying relative rotation angle (RRA). Spherical diamond impactors (with a diameter of 25Å) are enforced with high initial velocity (V_i) in the range of 1 km/s to 6.5 km/s to observe the ballistic performance of tBLG nanostructures. The specific penetration energy (E_p^*) of the impacted nanostructures and residual velocity (V_r) of the impactor are considered as the quantities of interest, wherein the effect of stochastic system parameters is computationally captured based on an efficient Gaussian process regression (GPR) based Monte Carlo simulation approach. A data-driven sensitivity analysis is carried out to quantify the relative importance of different critical system parameters. As an integral part of this study, we have deterministically investigated the resonant behaviour of graphene nanostructures, wherein the high-velocity impact is used as the initial actuation mechanism. The comprehensive dynamic investigation of bilayer graphene under the ballistic impact, as presented in this paper including the effect of twisting and random disorder for their prospective exploitation, would lead to the development of improved impact-resistant lightweight materials.

• Composites Research
• /
• 제20권5호
• /
• pp.43-48
• /
• 2007

전자기파의 흡수와 간섭 문제는 상업적, 군사적 용도에서 중요한 문제로 다루어져 왔다. 스텔스 기술은 전자기파 흡수 기술의 가장 전형적인 적용 방법 중에 하나이다. 본 연구는 유전성 및 자성 손실을 함유한 복합성의 필러를 개발하고자 시작되었다. 전도성 나노 소재인 탄소나노섬유 (CNFs)에 자성을 부여하기 위해 두 가지의 니켈-인과 니켈-철을 무전해 도금을 적용하여 각각 코팅하는 실험에 성공하였다. 제작된 복합 소재의 미세 구조를 SEM/TEM을 통해 관찰하였고, 이들의 성분 분석(EDS/ELLS)을 수행하였다. 코팅 층의 평균 두께는 약 $50\;{\sim}\;100\;nm$의 결과를 나타내었으며, 코팅 층의 성분은 Ni-6wt%P와 Ni-70wt%Fe의 결과를 각각 나타내었다.

• Composites Research
• /
• 제37권3호
• /
• pp.162-169
• /
• 2024

본 논문에서는 습식 방사 공정을 통한 PAN(polyacrylonitrile)계 전구체 섬유의 형태학적 제어 및 2종의 흑연화 촉진제(Ca, Ni)가 도입된 PAN계 탄소섬유의 흑연화 거동을 조사하였다. 흑연화 촉진제는 습식방사된 PAN 계 전구체 섬유의 열수 연신시 형성된 기공으로 도입되었으며, 결정구조 및 라만 분석을 통해 흑연화 촉진효과를 검토하였다. 1500℃의 상대적으로 낮은 온도에서는 흑연화에 큰 영향을 주지 않은 반면에, 2400℃의 고온에 서는 흑연화 촉진제 미처리 섬유와 비교하여 I_D/I_G 비율이 최대 2배까지 감소하는(GF-AS 0.54: GF-Ni100 0.28) 경향을 나타냈다. 흑연화도(degree of graphitization)는 Ca 흑연화 촉진제와 비교하여 Ni 흑연화 촉진제가 더 큰 영향을 끼침을 I_D/I_G 비율을 비교하여(GF-Ca100 0.42: GF-Ni100 0.28) 확인할 수 있었다. 또한, 2D band의 존재로부터 흑연평면구조가 다층으로 구성되어 있음을 알 수 있었다. 흑연결정의 결정면간거리(d₀₀₂)에 대한 흑연화 촉진제 효과는 미비하였으나, 특히 Ca 흑연화 촉진제 처리된 흑연섬유(GF-Ca100)의 경우 최대 ~5 nm 결정 크기가 증가함이 확인되었다.

• Composites Research
• /
• 제33권6호
• /
• pp.365-370
• /
• 2020

항공기에서의 결빙은 동체 전체의 무게증가로 인한 연료 효율 감소, 거칠기 생성으로 인한 항력 증가, 센서의 오작동 등과 같은 문제의 원인이다. 폴리우레탄 탑코트의 경화온도인 60℃에서의 경화시간에 따른 폴리우레탄 탑코트의 점도를 실시간으로 측정하였고 이 데이터를 통해 폴리우레탄 탑코트의 시간 별 점도에 대해 파악하였다. 실리카 나노입자는 초음파분산을 통해 에탄올 내에 분산을 진행하였고, 각기 다른 선경화 조건을 진행한 폴리우레탄 탑코트 위에 도포를 진행하였다. 실리카/폴리우레탄 탑코트 나노복합재료의 표면 거칠기는 표면 거칠기 테스터를 사용하여 측정하였고 표면 거칠기 데이터는 3차원 매핑을 사용하여 시각화 하였다. 선경화 시간에 따른 실리카와 폴리우레탄 탑코트 간의 접착력은 인발접착시험(Adhesion pull-off test)를 통하여 평가를 진행하였고, 표면 소수성은 증류수를 이용한 정적 접촉각을 통해 평가하였다. 최종적으로 소수성 표면을 위한 폴리우레탄 탑코트의 최적 선경화 시간을 파악할 수 있었다.

• 한국해양공학회지
• /
• 제20권5호
• /
• pp.77-81
• /
• 2006

In this study, monolithic liquid phase sintered SiC (LPS-SiC) was made by the hot pressing method with nano-SiC powder, whose particle size is 30 nm and less on the average. Alumina ($Al_{2}O_{3}$), yttria ($Y_{2}O_{3}$), and silica ($S_{i}O_{2}$) were used for sintering additives. To investigate the effects of $S_{i}O_{2}$, the $Al_{2}O_{3}/Y_{2}O_{3}$ composition was fixed and the ratio of $S_{i}O_{2}$ was changed, with seven different ratios tested. And to investigate the effects of the sintering temperature, the sintering temperature was changed, with $1760^{\circ}C,\;1780_{\circ}C$, and $1800_{\circ}C$ being used with a $S_{i}O_{2}$ ratio of 3 wt%. The materials were sintered for 1 hour at $1760^{\circ}C,\;1780^{\circ}C$ and $1800^{\circ}C$ under a pressure of 20 MPa. The effects on sintering from the sintering system used, as well as from the composition of the sintering additives, were investigated by density measurements. Mechanical properties, such as flexural strength, were investigated to ensure the optimum conditions for a matrix of SiCf/SiC composites. Sintered densityand the flexural strength of fabricated LPS-SiC increased with an increase in sintering temperature. Particularly, the relative density of a sintered body at $1800^{\circ}C$ with a non-content of $S_{i}O_{2}$, a specimen of AYSO-1800, was 95%. Also, flexural strength was about 750MPa.

• Composites Research
• /
• 제18권1호
• /
• pp.23-29
• /
• 2005

본 연구에서는 몬모릴로나이트(montmorillonite, MMT)의 오존처리가 몬모릴로나이트의 표면특성과 폴리프로필렌(polypropylene, PP) 나노복합재료의 열안정성에 미치는 영향에 대하여 살펴보았다. MMT의 표면 특성은 XRD, FT-IR 그리고 XPS를 통해 관찰하였고, 나노복합재료의 열안정성은 열중량 분석기(TGA)를 이용하여 조사하였다 실험 결과, 실리케이트의 층간 간격은 유기적으로 개질된 MMT(D-MMT)가 개질되지 않은 MMT에 비해 약 11${\AA}$ 증가한 것을 알 수 있었고, FT-IR 결과로부터 D-MMT의 경우 $2800\~2900\;cm^{-1}$ 부근에서 $CH_2$의 피크가 형성된 것을 확인할 수 있었다. 또한 오존처리는 MMT 표면에 Si-O와 $SiO_2$ 관능기를 증가시켰는데, 이는 산소를 포함하는 관능기들이 발달하기 때문으로 판단된다. 오존처리된 MMT가 도입된 나노복합재료에서 열안정성이 증가하는 것을 확인할 수 있었으며, 이는 PP와 MMT 사이의 산-염기 계면 상호작용으로부터 계면 결합력이 향상되었기 때문으로 판단된다.

• The Journal of Advanced Prosthodontics
• /
• 제10권2호
• /
• pp.101-112
• /
• 2018

PURPOSE. The purpose of this study was to investigate the effect of various surface treatments (ST) on the shear bond strength of resin composite to three bilayer dental ceramics made by CAD/CAM and two veneering ceramics. MATERIALS AND METHODS. Three different bilayer dental ceramics and two different veneering ceramics were used (Group A: IPS e.max CAD+IPS e.max Ceram; Group B: IPS e.max ZirCAD+IPS e.max Ceram, Group C: Vita Suprinity+Vita VM11; Group D: IPS e.max Ceram; Group E: Vita VM11). All groups were divided into eight subgroups according to the ST. Then, all test specimens were repaired with a nano hybrid resin composite. Half of the test specimens were subjected to thermocycling procedure and the other half was stored in distilled water at $37^{\circ}C$. Shear bond strength tests for all test specimens were carried out with a universal testing machine. RESULTS. There were statistically significant differences among the tested surface treatments within the all tested fracture types (P<.005). HF etching showed higher bond strength values in Groups A, C, D, and E than the other tested ST. However, bonding durability of all the surface-treated groups were similar after thermocycling (P>.00125). CONCLUSION. This study revealed that HF etching for glass ceramics and sandblasting for zirconia ceramics were adequate for repair of all ceramic restorations. The effect of ceramic type exposed on the fracture area was not significant on the repair bond strength of resin composites to different ceramic types.

• Composites Research
• /
• 제29권5호
• /
• pp.243-248
• /
• 2016

열경화성 탄소 섬유 복합재료 분리판은 높은 기계적 특성뿐만 아니라 높은 내산성을 갖으나, 높은 제조단가 및 낮은 자체저항이 극복해야 할 가장 큰 장애물이다. 따라서 본 연구에서는, 열가소성 폴리머를 복합재료 분리판의 기지로 적용하여 분리판 생산성과 자체저항이 모두 증가된 열가소성 탄소 복합재료 분리판을 개발하였다. 전기 전도도 및 기계 강도를 증가시기키 위하여 평직 형태의 탄소 섬유 직물을 사용하였으며, 분리판의 자체 저항을 감소시키기 위하여 전도성 나노입자를 열가소성 기지에 혼합하였다. 개발된 분리판의 면적 비저항 및 기계물성을 고온 연료전지 작동 온도 및 스택의 체결압에 따라 측정하였다.

• 한국염색가공학회지
• /
• 제26권2호
• /
• pp.88-98
• /
• 2014

This study is to assess the photocatalytic degradation of PET and Nylon 6 films containing nano-sized $TiO_2$ powders of anatase and rutile types. The PET and Nylon 6 films containing six kinds of the nanoparticles were prepared by melt casting method using a heating press machine. Reflectance in visible region and water contact angles of the irradiated PET and Nylon 6 composite films decreased with increasing UV/$O_3$ irradiation. Also the enhanced hydrophilicity has a close relationship with the increase in the Lewis base parameter, which indicates more oxidized polymer surfaces. The photocatalytic degradation of the nanocomposite films increased with increasing $TiO_2$ content and UV energy, which is more significant with the anatase types rather than the rutile types. The amide linkages in the Nylon 6 seemed to be more susceptible to the UV light compared to the ester groups in the PET, particularly in the presence of the $TiO_2$ photocatalysts. The photoscission and photodegradation of the polymers in the composites produced more degraded structure assisted by the photocatalytic activity of the $TiO_2$ nanoparticles. Also the composite films can bleach the methylene blue dyes more easily under the UV/$O_3$ irradiation, suggesting the photobleaching activity of the $TiO_2$ nanoparticles.