Superhydrophobic $SiO_2$ thin films were successfully fabricated on a glass substrate by sol-gel method. To fabricate $SiO_2$ thin film with a high roughness, $SiO_2$ nano particles were added into tetraethoxysilane (TEOS) solution. The prepared $SiO_2$ thin film without an addition of $SiO_2$ nano particles showed a very flat surface with ca. 1.27 nm of root mean square (RMS) roughness. Otherwise, the $SiO_2$ thin films fabricated by using coating solutions added $SiO_2$ nano particles of 1.0, 2.0 and 3.0 wt% showed a RMS roughness of ca. 44.10 nm, ca. 69.58 nm, ca. 80.66 nm, respectively. To modify the surfaces of $SiO_2$ thin films to hydrophobic surface, a hydrophobic treatment was carried out using a fluoroalkyltrimethoxysilane (FAS). The $SiO_2$ thin films with a high rough surface were changed from hydrophilic to hydrophobic surface after the FAS treatment. Especially, the prepared $SiO_2$ thin film with a RMS roughness of 80.66 nm showed a water contact angle of $163^{\circ}$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.135-135
• /
• 2003

The fast evolution in the fold of optical communication systems demands powerful optical information treatment. These functions can be performed by integrated optical systems. A key component of such systems is erbium doped waveguide amplifier(EDWA). The intra 4f radiative transition of Er at 1.5 $\mu\textrm{m}$ is particularly interesting because this wavelength is standard in optical telecommunications. The fabrication of waveguide amplifier for integrated optics using sol-gel process has received an increasing attention. Potential advantage of lower cost by less capital equipment and easy processing makes this process an attractive alternatives to conventional technologies like flame hydrolysis deposition, ion exchange and chemical vapor deposition, etc. In addition, sol-gel process has been found to be extremely suitable for the control of composition and refractive index related directly with optical properties. The main drawback of such an amplifier with respect to the EDWA is the need for a much higher Er3+ concentration to compensate for the smaller interaction length. However, the high doping of Er might be resulted in the non-radiative relaxation by clustering of Er ions End co-operative upconversion. In order to solve this problem, we investigate the possibility of avoiding short Er-Er distances by encapsulation of Er3+ ions in hosts such as organic-inorganic hybrid materials. For inorganic-organic hybrid sols, methacryloxypropyltrimethoxysilane (MPTS), zirconyl chloride octahydrate and erbium(III) chloride hexahydrate were used as starting materials, followed by conventional sol-gel process. It was observed by TEM that nano sols having core/shell toplology were formed, depending on the mole ratio of Zr/Er. The surface roughness for the coatings on Si substrate was investigated by AFM as a function of Zr/Er ratio. The local environment and vibrational Properties of Er3+ ions were studied using Near-IR, FT-IR, and UV/Vis spectroscopy. Nano hybrid coatings derived from polymer and Er doped encapsulation Eave the good luminescence at 1.55$\mu\textrm{m}$.

• Korean Journal of Materials Research
• /
• v.25 no.2
• /
• pp.107-112
• /
• 2015

The oxide films formed on etched aluminum foils play an important role as dielectric layers in aluminum electrolytic capacitors. $Y_2O_3$-doped $ZrO_2$ (YZ) films were coated on the etched aluminum foils by sol-gel dip coating, and the electrical properties of YZ-coated Al foils were characterized. YZ films annealed at $450^{\circ}C$ were crystallized into a cubic phase, and as the $Y_2O_3$ doping content increased, the unit cell of $ZrO_2$ expanded and the grain size decreased. The etch pits of Al foils were filled by YZ sol when it dried at atmospheric pressure after repeating for several times, but this step could essentially be avoided when being dried in a vacuum. YZ-coated foils indicated that the specific capacitance and dissipation factor were $2-2.5{\mu}F/cm^2$ and 2-4 at 1 kHz, respectively, and the leakage current and withstanding voltage of films approximately 200 nm thick were $5{\times}10^{-4}A$ at 21 V and 22 V, respectively. After being anodized at 500 V, the foils exhibited a specific capacitance and dissipation factor of $0.6-0.7{\mu}F/cm^2$ and 0.1-0.2, respectively, at 1 kHz, while the leakage current and withstanding voltage were $2{\times}10^{-4}-3{\times}10^{-5}A$ at 400 V and 420-450 V, respectively. This suggests that YZ film is a promising dielectric that can be used in high voltage Al electrolytic capacitors.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.511-511
• /
• 2007

Low-emissivity (low-e) coatings with visible transparency have attracted increased interest m reducing heat radiation loss through window panes from ecological and sustainable aspects. $TiO_2$-silver transparent thin films for low-e have good properties for UV and IR blocking as well as photocatalyst compared to that with commercial UV blocking films such as fluorine doped oxide (FTO), antimony doped tin oxide (ATO), etc. In this study, transparent $TiO_2$-silver thin films were prepared by successive ink-jet printing of commercial nano silver and $TiO_2$ sol. The $TiO_2$ sol, as ink for ink-jet printing, were synthesized by hydrothermal process in the autoclave externally pressurized with $N_2$ gas of 200 bar at $120^{\circ}C$ for 10 hrs. The synthesized $TiO_2$ sols were all formed with brookite phase and their particle size was several to 30 nm. At first nano sized silver sol was coated on glass substrate, after that $TiO_2$ sol was coated by ink-jet printing. With increasing coating thickness of $TiO_2$-silver multilayer by repeated ink-jet coating, the absorbance of UV region (under 400nm) and IR region (over 700nm) also increase reasonably, compared to that with commercial UV blocking films.

• Corrosion Science and Technology
• /
• v.22 no.6
• /
• pp.447-456
• /
• 2023

In this work, we performed a comparative study examining two coatings on Ti Gr.1 for use in fuel cell bipolar plates. The coatings consisted of carbon black as the conductor along with acrylic polymer and Ti Sol-Gel binder as the binder. Ti Sol-Gel that had precipitated as TiO₂ in areas impregnated between carbon black gaps, thereby acting as a binder for carbon black and serving as a polymer coating. Neither of the coatings peeled off during the 90° bend test to check formability. The contact resistance of the TiO₂ coating was found to be lower than that of the polymer binder coating. Moreover, due to coating shrinkage (denser) that occurred during the heat treatment process, the TiO₂ binder coating showed almost the same level of corrosion resistance, as measured by potentiostatic and EIS tests, despite being thinner than the polymer coating. However, both the polymer binder coating and the TiO₂ binder coating had many pores and irregularities internally (around 10 ~ 100 nm) and on the surface (0.1 ~ 2 ㎛). We considered that these pores and irregularities contributed to the lower corrosion resistance.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.727-730
• /
• 2003

Thin tin oxide film with nano-size particle was prepared on silicon substrate by hydrothermal synthetic method and successive sol-gel spin coating method. The fabrication method of tin oxide film with ultrafine nano-size crystalline structure was tried to be applied to fabrication of micro gas sensor array on silicon substrate. The tin oxide film on silicon substrate was well patterned by chemical etching upto 5${\mu}{\textrm}{m}$width and showed very uniform flatness. The tin oxide film preparation method and patterning method were successfully applied to newly proposed 2-dimensional micro sensor fabrication.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.202.1-202.1
• /
• 2013

ZnO nanostructure was fabricated on a Si substrate using two-step growth. The seed layer was grown on the Si substrate by a sol-gel spin-coating. In the first step, ZnO nanorods were grown by a hydrothermal method at $140^{\circ}C$ for 5 min. In the second step, a ZnO thin film was grown on the ZnO nanorods by spin-coating. After growth, these films were annealed at $800^{\circ}C$ for 10 min. Electrical and optical properties of ZnO nanostructures have modified by plasma-assisted molecular beam epitaxy (PA-MBE) regrowth. The carrier concentration and resistivity increased by PA-MBE regrowth. In the photoluminescence, the full width at half maximum and intensity were decreased and increased, respectively, by PA-MBE regrowth.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.62.1-62.1
• /
• 2011

현재 상용화된 LED 또는 태양전지 등의 투명전극(TCO, transparent couducting oxide)재료로 높은 전기전도도와 광투과도를 갖는 ITO (Indium Tin Oxide)가 많이 채택되고 있다. 그러나 이에 사용되는 Indium의 단가가 높다는 문제점이 있어 이를 대체하기 위한 물질의 연구가 많이 이루어지고 있다. 특히 Aluminum을 doping한 ZnO (AZO)는 우수한 전기적, 광학적 특성 등으로 인해 ITO를 대체할 차세대 TCO 물질로 각광받고 있다. 본 연구에서는 sol-gel법을 및 direct patterning법을 이용하여 moth-eye 패턴을 포함하는 AZO 박막을 제작하였다. AZO sol을 제작하기 위하여 2-methoxyethanol, zinc acetate dihydrate 및 doping source로 aluminum nitrate nonahydrate를 사용하였다. 또한 광추출 향상 효과를 갖는 moth-eye 구조의 master stamp를 Polydimethyl siloxane(PDMS)를 이용하여 역상 moth-eye 구조의 mold를 복제하였으며, 이 복제된 mold와 제작된 AZO sol을 이용한 direct patterning법을 통해 나노급 moth-eye 구조를 갖는 AZO 투명전극층을 형성하였다. 제작된 moth-eye 구조를 갖는 AZO 투명전극층의 전기적 특성 평가를 위해, 4-point probe 측정 및 Hall measurement를 시행하였으며, 광학적 특성을 확인하기 위하여 UV-Visable spectrometer를 이용하여 투과도를 측정하였다. 본 연구를 통해 현재 상용화된 광전자 소자에 사용되고 있는 ITO 투명전극을 대체할 차세대 투명전극으로써 AZO 박막의 가능성을 확인하였다.

• Journal of Magnetics
• /
• v.21 no.1
• /
• pp.40-45
• /
• 2016

Nickel substituted nano-sized ferrite powders, $Co_{1-x}Ni_xFe_2O_4$, $Mn_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ($0.0{\leq}x{\leq}0.2$), were fabricated using a sol-gel method, and their crystallographic and magnetic properties were subsequently compared. The lattice constants decreased as quantity of nickel substitution increased, while the particle size decreased in $Co_{1-x}Ni_xFe_2O_4$ ferrite but increased for the $Mn_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites. For the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-x}Ni_xFe_2O_4$ ($0.0{\leq}x{\leq}0.2$) ferrite powders, the $M{\ddot{o}}ssbauer$ spectra could be fitted as the superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. However, the $M{\ddot{o}}ssbauer$ spectrum of $Mn_{0.8}Zn_{0.1}Ni_{0.1}Fe_2O_4$ consisted of two Zeeman sextets and one single quadrupole doublet due to the ferrimagnetic and paramagnetic behavior. The area ratio of the $M{\ddot{o}}ssbauer$ spectra could be used to determine the cation distribution equation, and we also explain the variation in the $M{\ddot{o}}ssbauer$ parameters by using this cation distribution equation, the superexchange interaction and the particle size. The saturation magnetization decreased in the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites but increased in the $Mn_{1-x}Ni_xFe_2O_4$ ferrite with nickel substitution. The coercivity decreased in the $Co_{1-x}Ni_xFe_2O_4$ and $Mn_{1-2x}Zn_xNi_xFe_2O_4$ ferrites but increased in the $Mn_{1-x}Ni_xFe_2O_4$ ferrite with nickel substitution. These variations could thus be explained by using the site distribution equations, particle sizes and spin magnetic moments of the substituted ions.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.04a
• /
• pp.207-209
• /
• 2008

본 연구는 PFOA 규제대응 발수제(불소고분자의 탄소수가 6개)와 신규합성한 $TiO_2$ sol을 부피비로 혼용한 후 그에 따른 발수성과 방오성 향상에 관한 연구이다. 발수제 단독 처리 시 발수제의 사용량이 점차 줄어듬에 따라 발수도는 100에서 50${\sim}$70으로 점차 감소하였으며, 방오성은 5에서 2로 감소하였다. 그러나 $TiO_2$ sol을 발수제와 혼용하였을 경우 발수제의 사용량이 줄어듬에 따라 발수도가 100에서 80으로 방오성은 5에서 3.5로 감소하였으나, 발수제 단독 처리 시보다 우수한 결과가 나왔다.