• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.123-130
• /
• 2005

Zeolite X adsorbents with large surface area were prepared for using oxygen PSA adsorbent. Selective adsorption performance of nitrogen on the synthesized zeolite X adsorbent was improved by the cation exchange of adsorbent. The zeolite X which had over $650m^2/g$ surface area was synthesized at the conditions of $SiO_2\;:\;Na_2O\;:\;H_2O\;:\;Al_2O_3$ = 2.5 : 3.5 : 150 : 1 mole ratio, $98^{\circ}C$ temperature and 18 h synthesized time in 50 L reactor. The metal ions Li, Ag, Ca, Br, Sr, etc. were investigated for ion exchange with zeolite X. Ag ion was showed the highest ion exchange rate among these metal ions and all metal ions were exchanged with Na ion at equivalent rate. Compared with the NaX adsorbent, the ion exchanged zeolite X adsorbent remarkably improved its adsorption performance of nitrogen at the conditions of $10{\sim}40^{\circ}C$ temperature and 0~9 atm pressure. At an equilibrium pressure under 0.5 atm, adsorption performance of nitrogen on the ion exchanged zeolite adsorbent increased in the order of Ag > Li > Ca > Sr> Ba > K, whereas at an equilibrium pressure over 1 atm showed in the order of Li > Ag > Ca > Sr > Ba > K. Nitrogen/oxygen separation factor of Li ion exchanged zeolite X adsorbent was 13.023 at the partial pressure of nitrogen/oxygen gas mixture similar to air and $20^{\circ}C$ adsorption temperature.

• Journal of Environmental Science International
• /
• v.26 no.6
• /
• pp.719-728
• /
• 2017

In order to investigate the adsorption characteristics for Sr ion using the Na-X zeolite synthesized from coal fly ash, batch tests and response surface analyses were carried out. The adsorption kinetic data for Sr ions, using Na-X zeolite, fitted well with the pseudo-second-order model. The uptake of Sr ions followed the Langmuir isotherm model, with a maximum adsorption capacity of 196.46 mg/g. Thermodynamic studies were conducted at different reaction temperatures, with the results indicating that Sr ion adsorption by Na-X zeolite was an endothermic (${\Delta}H^o$>0) and spontaneous (${\Delta}G^o$<0) process. Using the response surface methodology of the Box-Behnken method, initial Sr ion concentration ($X_1$), initial temperature ($X_2$), and initial pH ($X_3$) were selected as the independent variables, while the adsorption of Sr ions by Na-X zeolite was selected as the dependent variable. The experimental data fitted well with a second-order polynomial equation by multiple regression analysis. The value of the determination coefficient ($R^2=0.9937$) and the adjusted determination coefficient (adjusted $R^2=0.9823$) was close to 1, indicating high significance of the model. Statistical results showed the order of Sr removal based on experimental factors to be initial pH > initial concentration > temperature.

• Korean Chemical Engineering Research
• /
• v.45 no.2
• /
• pp.160-165
• /
• 2007

The synthesis and the characterization of Low Silica X (LSX) zeolite for nitrogen adsorption have been studied. The performance of LSX zeolite for nitrogen adsorption was compared to that of the commercial zeolite. The $Na_2O/(Na_2O+K_2O)$ ratio in the gel and the crystallization time were fixed as the synthetic factor. The LSX zeolite was formed at the $Na_2O/(Na_2O+K_2O)$ ratio of 0.75. The formation of LSX zeolite was confirmed by XRD and SEM. The Si/Al ratio was investigated by using XRF and FT-IR. The synthesized LSX zeolite showed a lower Si/Al ratio than the NaY and NaX zeolites although they have a same faujasite structure. The Si/Al ratio of the LSX zeolite converged close to 1. 1A (Li, Na, K) and 2A (Mg, Ca, Ba) group elements were ion-exchanged to the LSX zeolite. As the charge density of cation rises, the amount of nitrogen adsorbed increased. $Li^+$ ion-exchanged LSX zeolite showed the highest nitrogen adsorption weight. When the Li/Al ratio was over 0.65, nitrogen adsorption increased remarkably. $Li^+$ ions located on the supercage (site III, III') in the LSX zeolite played a role as nitrogen adsorption sites. When the $Ca^{2+}$ ions were added to the LiLSX zeolite by ion-exchange method, the performance for nitrogen adsorption increased more. The performance for the nitrogen adsorption was the highest at the Ca/Al ratio of 0.26. Nitrogen adsorption capacity of LiCaLSX (Ca/Al=0.26) zeolite was superior to the commercial NaX zeolite.

• Journal of the Mineralogical Society of Korea
• /
• v.20 no.3
• /
• pp.223-229
• /
• 2007

The mechanism of hydrothermally synthesizing Na-A zeolite from siliceous mudstone at a $Na_2O/SiO_2$ ratio of 0.6, a $SiO_2/Al_2O_3$ 2.0 and a $H_2O/Na_2O$ 119 has been observed by IR, DTA, XRD and SEM. This mudstone is a tertiary periodic sedimentary rock and widely spreads around the Pohang area. In the early hydrothermal synthesis at $80^{\circ}C$ in an autoclave, sodium silicate and sodium aluminate were found to be preferentially reacted to generate Na-A type zeolite. Gibbsite and bayerite were also formed due to the presence of extra aluminum oxide in the feedstock. As reaction time in-creased up to 50 h, residual sodium aluminatewas reacted with siliceous mudstone, causing the Na-A zeolite crystal to grow and the hydroxylsodalite to generate. Therefore, in the $14{\sim}50\;h$ synthetic time, Na-A zeolite and hydroxylsodalite were formed. Also, if reaction time passed over 50 h, a part of the Na-A zeolite was finally redissolved and reacted with hydroxylsodalite to synthesize Na-P zeolite, generating porous surface of Na-A zeolite and disappearing hydroxylsodalite.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.2
• /
• pp.240-247
• /
• 2015

Zeolite A was prepared from coal fly ash upon NaOH fusion treatment, followed by hydrothermal treatment. The effects of treatment conditions such as NaOH/ash ratio, fusion temperature, the amount of sodium aluminate added, hydrothermal treatment temperature and time on the type and the crystallinity of zeolites were investigated. The optimal NaOH/ash weight ratio and fusion temperature to produce high crystalline zeolite A were 1.2 and $550^{\circ}C$, respectively. The dissolution of $Si^{4+}$ and $Al^{3+}$ from the fused fly ash was not affected by stirring time. The type of synthetic zeolites was found to be dependent on the amount of sodium aluminate added. The low amount of sodium aluminate favored zeolite X, while a single phase zeolite A was produced by increasing the amount sodium aluminate. Zeolite A was transformed into hydroxysodalite with increasing hydrothermal treatment time and temperature. A high crystalline zeolite A could be obtained by decreasing the temperature increasing time up to the reaction temperature.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2003.11a
• /
• pp.25-28
• /
• 2003

• Journal of the Korean Chemical Society
• /
• v.17 no.1
• /
• pp.47-52
• /
• 1973

Korean bentonite was treated with aqueous NaOH solution under the reaction conditions such as concentration of NaOH, 0.5-6N; ratio of $Na_{2}O$ to $SiO_2$, 1-4; reaction time, 2-30 days; reaction temperature, $70^{\circ}C-90^{\circ}C$. The products were examined by X-ray diffraction patterns. When it was treated with 2N NaOH at $70^{\circ}C$, zeolite species $P_1$ was formed with good yield. In higher concentration and at higher temperature than above, zeolite species $P_1$ was converted to hyeroxysodalite. Together with these crystals, some faujasite type zeolite, sodium A zeolite, mordenite type zeolite etc. was formed depending upon reaction conditions.

• Journal of the Korean Chemical Society
• /
• v.16 no.4
• /
• pp.249-256
• /
• 1972

Hadong-Kaolin was treated with aqueous sodium hydroxide solution. The crystalline structure was studied by X-ray powder diffraction method. The optimum conditions for various crystal formation were as follows: Crystal Concentration Temp. reating time Halloysite 1~4 N NaOH $60^{\circ}C$ 0.5${\sim}$4 hr Sodium A zeolite 0.5${\sim}$2 N NaOH 80${\sim}$$100^{\circ}C$ 6${\sim}$20 hr Hydoxysodalite > 4 N NaOH 80${\sim}$$100^{\circ}C$ > 4 hr The ratio of $Na_2O to SiO_2$ for crystallizing sodium A zeolite was 0.5-1.5. The $Ca^{++}$ ion exchange capacity of produced sodium A zeolite for 0.2 N $CaCl_2$ solution at $25^{\circ}C$ was amounted to 65% of theoretical value.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.521-523
• /
• 2009

본 연구에서는 식물성유지와 메탄올로부터 전이에스테르화 반응에 의해 바이오디젤 제조에 사용되는 비균질촉매로 사용하기 위하여 NaX 제올라이트 촉매에 염기도를 향상시키기 위하여 KOH를 담지하여 담지량에 따른 바이오디젤 제조특성을 조사해보았다. KOH 담지량을 10wt% - 70wt%로 달리하여 Incipient wetness 방법으로 담지한후 $500^{\circ}C$에서 소성하여 촉매를 제조하고, 제조된 KOH의 담지량이 다른 KOH/NaX 제올라이트 촉매는 SEM, XRD, BET등을 통해 촉매특성을 평가하였고, 생성된 지방산 메틸에스테르는 가스크로마토그래피로 순도를 측정하였다. NaX 제올라이트 촉매에 KOH 담지량이 높은 경우와 촉매량이 많은 경우 바이오디젤제조에 유리하였고, 특히 반응시간과 반응온도는 $120^{\circ}C$, 2시간동안 반응한 경우 가장 좋은 지방산 메틸에스테르의 수율을 얻을 수 있었다.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1999.06a
• /
• pp.351-360
• /
• 1999

A large NaX type zeolite crystal of a uniform particle size of 20${\mu}{\textrm}{m}$ are grown with various H2O content by hydrothermal reaction and added seed crystal (2~3 ${\mu}{\textrm}{m}$) to reactant solution as a function of different adding seed levels from 3 to 15 %. The result that increased purity of NaX zeolite above 95% and homogeneity of crystal size by increasing adding seed levels, also decreased crystallization time. It was explained that adding seed to synthesis solution leaded out increase of surface area of physical contact reaction and directed growth of seed crystal, so more rapid consumption of reaction gel as increase seeding levels.