• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.626-634
• /
• 1991

The specimens for the corrosion test were made by hot-pressing of SiC power with 2 wt% Nl2O3 and 10wt% Al2O3 additions at 200$0^{\circ}C$ and 205$0^{\circ}C$. The specimens were corroded in 37 mole% NaCl and 63 mole% Na2SO4 salt mixture at 100$0^{\circ}C$ up to 60 min. SiO2 layer was formed on SiC and then this oxide layer was dissolved by Na2O ion in the salt mixture. The rate of corrosion of the specimen containing 10 wt% Al2O3 was slower than that of the specimen containing 2 wt% Al2O3. This is due to the presence of continuous grain boundary phase in the specimen containing 10 wt% Al2O3. The oxidation of SiC produced gas bubbles at the SiC-SiO2 interface. The rate of corrosion follows a linear rate law up to 50 min. and then was accelerated. This acceleration is due to the disruption oxide layer by the gas evolution at SiC-SiO2 interface. Pitting corrosion has found at open pores and grain boundaries.

• Journal of Radiation Protection and Research
• /
• 제22권3호
• /
• pp.135-141
• /
• 1997

열처리 특성의 연구는 열형광선량계를 재 사용하는데 있어서 중요하다. 최근 개발된 디스크 형태 (직경 4.5 mm, 두께 약 $90mg/cm^2$)의 LiF:Mg,Cu,Na,Si Teflon TLD의 열처리 조건을 구하기 위하여 조사전열처리, 판독과정 및 판독 후 열처리의 순서로 연구하였다. Teflon TLD의 감마선 조사는 $^{60}Co$ 0.1 Gy로 하였다. LiF:Mg,Cu,Na,Si Teflon TLD의 열처리 특성의 연구는 전기로와 판독장치를 이용하여 열처리 온도와 열처리 시간을 변화시키면서, 측정반복횟수에 따른 열형광강도 변화를 관찰하는 방법으로 수행하였다. LiF:Mg,Cu,Na,Si Teflon TLD의 열처리 조건은 조사전 열처리를 $80^{\circ}C$에서 1 시간 한 후 $280^{\circ}C$까지 판독하고 판독 후 열처리를 $270^{\circ}C$에서 20 초간 하는 것으로 결정되었고, 이 조건에서 10 회 반복측정시 원래의 열형광강도는 5%의 감소를 보였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2010년도 춘계 학술대회 제22권1호
• /
• pp.389-390
• /
• 2010

본 연구는 콘크리트 결합재로 사용되는 시멘트의 대체재 개발을 위해 천연황토에 수산화나트륨(NaOH) 수용액과 액상 규산나트륨($Na_2SiO_3$)을 혼합한 후 $60^{\circ}C$에서 알칼리 활성화하여 경화시켜 강도 발현 양상을 분석한 천연황토 콘트리트 결합재 개발을 위한 기초연구이다.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1570-1576
• /
• 1994

Effect of Na2O/SiO2 molar ratio, calcining temperature and addition of NaCl were investigated on the hydrothermal formation of X-type zeolite from the natural mordenite, which is a kind of rock deposited abundantly in kuryong po. Pulverized mordenite was first mixed with NaOH or NaOH-NaCl solution, and crystallized under hydrothermal condition at 90~10$0^{\circ}C$ for 10 hrs. Optimum condition for synthesis of the X-type zeolite were \circled1 the ratio Na2O/SiO2, NaCl/Al2O3 and H2O/Na2O:0.68, 11.4 and 40, respectively, \circled2 calcining temperature of starting materials: 90$0^{\circ}C$, \circled3 aging time: 48 hrs. and \circled4 crystallization temperature: 10$0^{\circ}C$. The yield of X-type zeolite under the optimum condition was about 55~60%, and the major crystallized X-type zeolite was faujasite phase. Zeolite of then type X was crystallized when NaCl was added to treating solution with in the limit 14.25 of NaCl/Al2O3 molar ratio. As the calcination temperature (from 50$0^{\circ}C$ to 95$0^{\circ}C$) of starting materials increases, yield of zeolite x increase.

• 한국가금학회지
• /
• 제12권1호
• /
• pp.25-30
• /
• 1985

가금에서의 영양소리용성에 미치는 볏짚구성분의 영향을 고찰하기 위하여 증류수 혹은 0.25N NaClO$_2$ 800$m\ell$당 볏짚 100g의 비율로 침지하여 135$^{\circ}C$ 3.2kg/$\textrm{cm}^2$ 압력밑에서 각각 30, 60 및 120분 autoclave를 이용하여 가열하고 세척 건조(증류수 혹은 NaClO$_2$-30, 60 및 120-볏짚) NDF, ADF 및 리그닌량을 조사하였다. 갓부화한 단관백색 레그흔 숫병아리에 10일간 시판 병아리 사료를 급여하고 계속해서 8일간 밀기울(기초), 섬유소(선분), 무처리볏짚, 증류수-30-볏짚 및 NaClO$_2$-30-볏짚이 각각 17.0% 함유된 실험사료를 급여했다. 증류수-30, 60 및 120-볏짚의 건물손실율은 각각 9.7, 12.1 및 13.3%였으나, NaClO$_2$-30, 60 및 120-볏짚에서는 각각 8.8, 18.7 및 19.4%로, NaClO$_2$-60 및 120-볏짚에서는 증류수볏짚의 1.5배가 되었다. 증류수 및 NaClO$_2$ 볏짚의 건물손실은 주로 무처리볏짚의 세포내용물과 헤미셀루로스의 용출에 기인하는 것이었다. 증류수-30-볏짚을 급여한 병아리는 무처리 혹은 NaClO$_2$-30-볏짚을 급여한것에 비해서 증체량이 높고 사료요구량이 낮았다. 질소밸런스 및 축적율은 증류수-30-볏짚을 급여한것에서 무처리 및 NaClO$_2$-30-볏짚을 급여한것에 비해서 높았고, 조지방소화율은 높아지는 경향이 있었다. 무처리, 증류수-30 및 NaClO$_2$-30-볏짚을 급여한 병아리의 MEn/GE는 각각 71.9, 72.9 및 70.4%였으며, 대사체중(kg 0.75)당 MEn섭취량은 각각 307.3, 296.2 및 291.4 KCal가 되었다. 이때 kg 0.75당 1일 단백질축적량은 각각 1.647, 1.969 및 1.560g이었다. 한편 증류수-30-볏짚을 급여한 병아리의 단백질 1g 축적에 상당하는 MEn는 30.56Kcal로써 무처리 및 NaClO$_2$-30-볏짚을 급여한것의 36.90 및 37.58Kcal보다 낮았다. 따라서 무처리볏짚에는 에너지 이용성 혹은 단백질축적에 영향을 미치는 물질 혹은 성질이 존재하며, 이것은 볏짚을 끓임으로써 제거된다는 것을 시모고 있다.

• 한국응용과학기술학회지
• /
• 제10권2호
• /
• pp.35-40
• /
• 1993

Alkaline cleaning agent(ACA) was prepared by blending of POE(4)octadecylmine(S-204), $Na_2CO_3$, sodium orthosilicate(Na-OSi). Tetronix T-701(T-701), and MJU-100A. The physical properties of ACA tested with steel specimen showed the following results. The cleaning powers of ACA-6(S-204 80g/$Na_2CO_3$, 160g/Na-OSi, 80g/T-701, 60g/MJU-100A, 20g mixture) for press-rust preventing oil was 98% and 99% degreasing at 2wt%, $70^{\circ}C$ and $90^{\circ}C$, respectively : for quenching oil, the cleaning power of ACA-6 was 95% degreasing at 2wt% and $70^{\circ}C$. From these results, it was ascertained that ACA-6 exhibited a good cleaning power. Foam heights measured immediately after foaming by Ross & Miles method and Ross & Clark method at 3wt%. $60^{\circ}C$ were 17mm and 40mm, respectively. As the result, ACA-6 was proved a good low foaming cleaning agent.

• 한국식품과학회지
• /
• 제32권6호
• /
• pp.1285-1290
• /
• 2000

본 실험은 수소이온 농도, 염, Sodium tripolyphosphate(STPP) 농도에 따른 돈육 등심 드립의 열변성을 DSC를 이용하여 조사한 것이다. pH가 증가함에 따라 돈육 등심 드립의 열안정성은 증가하였으며 특히 $T_1$이 $pH\;5.5{\sim}6.0$에서 $6.33^{\circ}C$의 가장 큰 증가를 보였다. 0.1 N, 0.2 N NaOH/1, 2 N HCl 및 $0{\sim}5%$ NaCl과 $0{\sim}0.5%$ sodium tripolyphosphate(STPP)로 처리하였을 때, pH가 증가함에 따라 드립의 열안정성은 증가하였으며, 특히 $T_1$이 $pH\;5.5{\sim}6.0$에서 $6.33^{\circ}C$의 가장 큰 증가를 보였다. 그리고 NaCl농도의 증가는 드립의 열안정성을 감소시켰는데 그중 $T_1$은 5% NaCl농도 수준에서 $9.41^{\circ}C$의 감소를 보였다. 한편 STPP는 드립이 열안정성을 증가시켰으며 0.5% STPP농도 수준에서 $T_1$이 $5.84^{\circ}C$의 증가를 보였다. $40{\sim}100^{\circ}C$로 증가함에 따라 $Lightness(L^*)$는 41.13에서 69.54로 증가하였고 $redness(a^*)$는 26.70에서 5.40으로 감소하였다. 특히 $L^*-$과 $a^*-$값 모두 $40{\sim}60^{\circ}C$에서 약 78%의 가장 큰 변화를 보였다.

• Elastomers and Composites
• /
• 제53권2호
• /
• pp.75-79
• /
• 2018

ZnS:Mn-glycine (ZnS:Mn-Gly) nanocomposites were synthesized by capping ZnS:Mn nanocomposites with glycine. Zinc sulfate heptahydrate ($ZnSO_4{\cdot}7H_2O$), glycine ($C_2H_5NO_2$), manganese sulfate monohydrate ($MnSO_4{\cdot}H_2O$), and sodium sulfide ($Na_2S$) were used as the source reagents. $ZnS:Mn-Gly-C_{60}$ nanocomposites were obtained by heating the ZnS:Mn-Gly nanocomposites and fullerene ($C_{60}$) at a 2:1 mass ratio in an electric furnace at $700^{\circ}C$ for 2 h. X-ray diffraction (XRD) was used to characterize the crystal structure of the synthesized nanocomposites. The photocatalytic activity of the $ZnS:Mn-Gly-C_{60}$ nanocomposites was evaluated, via the degradation of brilliant green (BG) dye under 254 nm irradiation, with a UV-vis spectrophotometer.

• Korean Chemical Engineering Research
• /
• 제50권4호
• /
• pp.627-631
• /
• 2012

휴대용 고분자전해질 연료전지의 수소발생용으로써 $NaBH_4$는 많은 장점을 갖고 있다. 본 연구에서는 $NaBH_4$ 가수분해 반응용 Co-P-B/Cu 촉매의 내구성에 대해 연구하였다. Co-P-B/Cu 촉매의 내구성 미치는 반응 온도, $NaBH_4$ 농도, NaOH 농도, 촉매 소성온도 등의 영향에 대해 실험하였다. 촉매의 내구성은 가수분해 반응 중에 발생하는 gel 형성에 영향을 받았다. 즉 gel 형성에 의해 촉매 손실률이 증가하였다. $NaBH_4$ 농도가 고농도일 때는 $60^{\circ}C$ 이상에서는 gel 형성이 안 되어 촉매 손실률이 낮았다. 그러나 $40^{\circ}C$ 이하에서는 gel이 형성되어 촉매 손실률이 증가했다. $NaBH_4$ 20 wt%, $40^{\circ}C$에서 NaOH 농도증가에 따라 겔이 형성되어 촉매 손실률이 증가함을 보였다. Co-P-B/Cu 촉매의 높은 온도에서 소성은 내구성을 향상시켰지만 촉매 활성을 감소시켰다.

• 대한약학회:학술대회논문집
• /
• 대한약학회 2002년도 Proceedings of the Convention of the Pharmaceutical Society of Korea Vol.2
• /
• pp.336.3-337
• /
• 2002

We previously reported that a synthetic naphthoquinone analog. 2.3-dichloro-5.8-dihydroxy-1, 4-naphthoquinone (NA). effectively induces apoptosis in human leukemic HL-60 cells. However. the cellular mechanism by which NA induces cell death remain unclear. In this study. we show that NA induces activation of capases. release of cytochrome c and upregulation of proapoptotic Bax protein. Futhermore. NA suppressed phosphorylation of Akt and Bad. suggesting that Akt regulates NA-induced apoptosis. Expresson of a dominant negative Akt enhancde NA-induced apoptosis. suggesting that naphthoquinone analog induces apoptosis through activating proapoptotic pathway and by the inactivation of antiapoptotic pathway.