• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.626-634
• /
• 1991

The specimens for the corrosion test were made by hot-pressing of SiC power with 2 wt% Nl2O3 and 10wt% Al2O3 additions at 200$0^{\circ}C$ and 205$0^{\circ}C$. The specimens were corroded in 37 mole% NaCl and 63 mole% Na2SO4 salt mixture at 100$0^{\circ}C$ up to 60 min. SiO2 layer was formed on SiC and then this oxide layer was dissolved by Na2O ion in the salt mixture. The rate of corrosion of the specimen containing 10 wt% Al2O3 was slower than that of the specimen containing 2 wt% Al2O3. This is due to the presence of continuous grain boundary phase in the specimen containing 10 wt% Al2O3. The oxidation of SiC produced gas bubbles at the SiC-SiO2 interface. The rate of corrosion follows a linear rate law up to 50 min. and then was accelerated. This acceleration is due to the disruption oxide layer by the gas evolution at SiC-SiO2 interface. Pitting corrosion has found at open pores and grain boundaries.

• Journal of the Korean institute of surface engineering
• /
• v.57 no.2
• /
• pp.86-91
• /
• 2024

In this study, we investigated the effect of Na₂SiO₃ concentration on the Plasma Electrolytic Oxidation(PEO) film formation of Al6061 alloy. The morphology of the PEO films were examined by Optical Microscope(OM) and Scanning Electron Microscope(SEM). PEO film thickness increases as the Na₂SiO₃ concentration increases. The elemental analysis of PEO films was conducted using Dispersive X-ray Spectrometer(EDS). The cross-sectional elemental analysis result shows that the Si concentration tends to increase as the concentration of Na₂SiO₃ increases. X-Ray Diffraction(XRD) analysis was performed to confirm the degree of phase change according to Na₂SiO₃ concentration. In addition, Vickers hardness was measured to confirm the mechanical strength of the PEO film. As the concentration of Na₂SiO₃ increases, the hardness value also tends to increase.

• Resources Recycling
• /
• v.18 no.4
• /
• pp.62-69
• /
• 2009

We researched separation of mixed waste acids with HF, $CH_3COOH$, $HNO_3$ that were produced during a semiconductor wafer process to recycle these acids. At first, we manufactured the fluoride compound in form of $Na_2SiF_6$ by precipitating HF using $NaNO_3$ and Si powder. The concentration of HF was reduced from the initial concentration of 127 g/L to 0.5 g/L with an HF recovery ratio of 99.5%. After the manufacture of $Na_2SiF_6$, the concentration of $HNO_3$ and $CH_3COOH$ demonstrated 502 g/L and 117 g/L respectively. Following these findings we added NaOH in this $CH_3COOH/HNO_3$ mixed acid in order to obtain pH=4. Next we separated the $CH_3COOH$ and recoverd it through the use of vaccum evaporation at -440 mmHg, $95^{\circ}C$. The concentration of the recovered $CH_3COOH$ was approximately 15% and the recovery ratio of $CH_3COOH$ was over 85%. We precipitated the $NaNO_3$ by cooling the concentrated solution to $20^{\circ}C$ with a $HNO_3$ recovery ratio of over 93%. We confirmed that only $Na_2SiF_6$ and $NaNO_3$ were manufactured by XRD analysis after drying these precipitants at $90^{\circ}C$. The precipitants demonstrated a purity of approximately 97% and 98% respectively. Therefore, the purity of the precipitants proved to be similar to that of commercial products.

• Resources Recycling
• /
• v.17 no.4
• /
• pp.57-65
• /
• 2008

The behavior of Na-A type zeolite formed in hydrothermal synthesis of melting slag from municipal incineration ash has been investigated with varying synthesis time and $SiO_2/Al_2O_3$ ratio. Sodium silicate and sodium aluminate feed was found to initially form nuclei of Na-A type zeolite in the behavioral study of the reaction products with different synthesis times. As the synthesis time increased, the nuclei have grown to Na-A type zeolite crystals by reacting with $SiO_2$ and $Al_2O_3$ dissolved from the melting slag. The hydrothermal synthesis was completed in 10 hr in the $SiO_2/Al_2O_3$ ratio of 1.38 and after that time, the Na-A type zeolite formed was dissolved and transformed into hydroxysodalite. Only Na-A type zeolite was formed in the $SiO_2/Al_2O_3$ ratio ranging 0.80 to 1.96, whereas Na-P type zeolite as well as Na-A type was formed in the $SiO_2/Al2O_3$ ratio of 2.54.

• Horticultural Science & Technology
• /
• v.30 no.3
• /
• pp.250-255
• /
• 2012

The effect of different source silicon ($CaSiO_3$, $K_2SiO_3$, and $NaSiO_3$) and their application methods (foliar application and subirrigation) on the growth of potted kalanchoe was investigated. Rooted terminal cuttings of Kalanchoe blossfeldiana 'Peperu' were transplanted into 10.5 cm plastic pots containing a commercial growing medium. Then, a nutrient solution, containing 0 or $50mg{\cdot}L^{-1}$ Si as $K_2SiO_3$, $Na_2SiO_3$, or $CaSiO_3$ and adjusted to EC 1.4-$1.6mS{\cdot}cm^{-1}$ and pH 6.0, was supplied through subirrigation along with the nutrient solution or by a foliar application. Plants were grown in a glasshouse under a mean temperature of $23^{\circ}C$ and RH of 70-80%. After 12 weeks of cultivation, plant growth characteristics and leaf tissue contents of P, K, Ca, Mg, Na, S, and Si were measured. Both subirrigational supply and foliar application of Si decreased the plant height and flower stem length. However, the plant condition in the foliar application resulted in disease-like soft rot on the leaf. Among three silicon sources tested, $CaSiO_3$ supplied through a subirrigation system increased shoot tissue contents of Si and chlorophyll as compared to the $Na_2SiO_3$ or $K_2SiO_3$ treatment. Shoot tissue contents of Ca, K, and Na increased when the plant was supplied with $CaSiO_3$, $K_2SiO_3$, and $Na_2SiO_3$, respectively. Subirrigational supply of $K_2SiO_3$ and $NaSiO_3$ decreased the shoot tissue contents of Ca and Mg, and K and Ca, respectively. Therefore, $CaSiO_3$ supplied through a subirrigation system could improve plant quality of kalanchoe 'Peperu' making compact potted plants.

• Bulletin of the Korean Chemical Society
• /
• v.8 no.1
• /
• pp.6-9
• /
• 1987

The study of the $Na_3YSi_3O_9$ structure, by x-ray diffraction and infrared spectrum, showed that $Na_3YSi_3O_9$ is similar to $Na_4CaSi_3O_9$ except for its being pseudo-cubic instead of cubic. The peaks in the x-ray diffraction pattern of $Na_3YSi_3O_9$ could therefore be indexed on the basis of the $Na_4CaSi_3O_9$ cell. Also, modified $Na_3MSi_3O_9$ (M = Lu, Yb, Tm, Er, Y, Ho, Dy, Gd, Eu, and Sm) type compounds were synthesized by introducing excess sodium, decreasing M(III) concentration, and substituting small amount of phosphorus for silicon. The unit cell parameters of the composition $Na_{3.2}M_{0.7}Si_{2.9}P_{0.1}O_{8.7}$ were estimated from x-ray powder diffraction patterns using the Cohen method.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.98.1-98.1
• /
• 2017

본 연구에서는 정전류 조건에서 알루미늄 합금의 PEO(Plasma Electrolytic Oxidation) 피막 형성 거동에 대한 전해질 조성의 영향을 아크 발생 양상, 전압-시간 곡선 및 형성된 표면피막의 구조를 관찰하여 연구하였다. 실험에 사용된 전해질은 NaOH 수용액에 $Na_2SiO_3$을 혼합하여 구성되었으며, NaOH와 $Na_2SiO_3$의 농도는 각각 0.01 ~ 1.0 M 와 0 ~ 2.0 M 사이로 조절되었다. 0.01 M NaOH 이하의 용액에서는 양극전압이 500 V 이상으로 상승되고 미세한 아크가 시편 표면 전체에 발생했으나, 0.02 M NaOH 이상의 농도에서는 양극전압이 300 V 이하로 감소되었고 아크발생이 관찰되지 않았다. 아크발생이 일어나지 않는 고농도의 0.5 M NaOH 용액의 경우 0.1 M 이상의 $Na_2SiO_3$를 첨가하였을 때 작은 아크의 무리가 발생되었다. 0.5 M NaOH 수용액에 0.1 M ~ 0.2 M $Na_2SiO_3$가 첨가되었을 땐 아크 무리가 발생하나 이내 일부 영역에서만 반복적으로 아크가 발생하는 로컬 버닝 현상이 일어났다. 한편 0.5 M NaOH 수용액에 0.5 M 이상의 $Na_2SiO_3$가 첨가되었을 때는 로컬 버닝이 일어나지 않고 전 표면에 걸쳐서 아크 무리가 이동하며 PEO 피막이 형성되었다. 0.01 M NaOH 수용액에서 형성된 PEO 피막의 두께는 처리 시간에 따라 증가하지 않고 $10{\mu}m$ 이하의 낮은 값을 보였다. 반면에 NaOH와 $Na_2SiO_3$ 혼합수용액에서 형성된 피막의 두께는 약 $30{\mu}m$ 이상의 높은 값을 보였다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.12-20
• /
• 2017

This report presents the results of an investigation on the fundamental properties of mortars high fluidity high volume slag cement(HVSC) activated with sodium silicate($Na_2SiO_3$). The ordinary Portland cement(OPC) was replaced by ground granulated blast furnace slag(GGBFS) from 40% to 80% and calcium sulfoaluminate(CSA) was 2.5% or 5.0% mass. The $Na_2SiO_3$ was added at 2% and 4% by total binder(OPC+GGBFS+CSA) weight. A constant water-to-binder ratio(w/b)=0.35 was used for all mixtures. The research carried out the mini slump, V-funnel, setting time, compressive strength and drying shrinkage. The experimental results showed that the contents of superplasticizer, V-funnel, setting time and drying shrinkage increased as the contents of CSA and $Na_2SiO_3$ increase. The compressive strength increases with and an increase in CSA and $Na_2SiO_3$. One of the major reason for these results is the accelerated reactivity of GGBFS with CSA and $Na_2SiO_3$. The maximum performance was CSA 5.0% + $Na_2SiO_3$ 4% specimens.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.444-448
• /
• 2016

Hollow silicon/carbon (H-Si/C) composites as anode materials for lithium ion batteries were investigated to overcome the large volume expansion. H-Si/C composites were prepared as follows; hollow $SiO_2\;(H-SiO_2)$ was prepared by adding $NaBH_4$ to $SiO_2$ synthesized using $st{\ddot{o}}ber$ method followed by magnesiothermic reduction and carbonization of phenolic resin. The H-Si/C composites were analyzed by XRD, SEM, BET and EDX. To improve the capacity and cycle performance, the electrochemical characteristics of H-Si/C composites synthesized with various $NaBH_4$ contents were investigated by charge/discharge, cycle, cyclic voltammetry and impedance tests. The coin cell using H-Si/C composite ($SiO_2:NaBH_4=1:1$ in weight) in the electrolyte of $LiPF_6$ dissolved in organic solvents (EC : DMC : EMC = 1 : 1 : 1 vol%) has better capacity (1459 mAh/g) than those of other composition coin cells. It is found that the coin cell ($SiO_2:NaBH_4=1:1$ in weight) has an excellent capacity retention from 2nd cycle to 40th cycle.

• Journal of the Korean Ceramic Society
• /
• v.19 no.1
• /
• pp.13-18
• /
• 1982

The crystallization of metastable "orthorhombic" phase from the glass in the system of Na $AlSi_3O_8-CaAl_2Si_2O_8$ is studied. These crystals are crystallized in the range of composition from $Ab_80An_20$ to An100. The symmetry of these crystals show orthorhombic as a possible space group P22121. Two probable twin models are proposed. proposed.