• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.5
• /
• pp.411-417
• /
• 2020

In this study, we introduce a Na β"-alumina composite thick film as a solid electrolyte, to reduce the resistance of electrolyte for a Na/S battery. An alumina/zirconia composite material was used to enhance the mechanical properties of the electrolyte. A solid electrolyte of about 40 ㎛ thick was successfully fabricated through the conversion and tape-casting methods. In order to investigate the effect of the surface treatment process of the solid electrolyte on the battery performance, the electrolyte was polished by dry and wet processes, respectively, and then the Na/S batteries were prepared for analyzing the battery characteristics. The battery with the dry process performed much better than the battery made with the wet process. As a result, the battery manufactured by the dry process showed excellent performance. Therefore, it is confirmed that the surface treatment process of the solid electrolyte has an important effect on the battery capacity and coulombic efficiency, as well as the interface reaction.

• Journal of the Korean Ceramic Society
• /
• v.38 no.8
• /
• pp.749-754
• /
• 2001

마이크로파 추출 및 하소 공정을 통하여 카올린으로부터 베타 알루미나 전구체 및 베타 알루미나 분말을 합성하였다. 황산 알루미늄 및 가성소다의 혼합 용액을 교반되는 에탄올 용액 중에 적하시켜서 $Al_2$(SO$_4$)$_3$.17$H_2O$ 및 $Na_2$SO$_4$.10$H_2O$의 균일한 침전물을 얻었다. $\beta$- 및 $\beta$\"-Al$_2$O$_3$상으로 구성된 베타 알루미나를 얻기 위하여 재래식 및 마이크로파 하소법으로 주어진 온도에서 약 2h 동안 침전물 시료를 하소하였다. 재래식 하소된 시료에 비하여 마이크로파 하소된 시료는 $\beta$\"-Al$_2$O$_3$상이 상대적으로 많이 존재하였다. 또한, 재래식 하소된 시료와 마이크로파 하소된 시료의 미세구조는 매우 상이하였다. 매우 상이하였다.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1076-1084
• /
• 1995

A mixture of aluminum isopropoxide (Al(OC3H7i)3) solution and sodium hydroxide (NaOH) solution was hydrolyzed in the range between pH 1~14. the powder obtained from sol-gel process was calcined at several temperatures and crystallization behaviors of various samples were investigated. The hydrolyzed sols of pH 1~6 wre clear, or near clear. On the other hand, powder precipitated from sols of pH 7~14. The sample obtained from pH 3 solution crystallized via complicated route, and $\beta$-Al2O3 and $\beta$"-Al2O3 phases appeared at lower temperature than samples from other pH conditions. And the quantity of remained $\beta$"-Al2O3 phase after heat treatment at 150$0^{\circ}C$ was more than samples from other pH conditions. After sintering, ionic conductivities were 1.3$\times$10-4S.cm-1 to 0.76$\times$10-4S.cm-1.0-4S.cm-1.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.3
• /
• pp.124-134
• /
• 2012

Environmental concerns over the use of fossil fuels and their resource constraints have spurred increasing interest of renewable energy, and the needs for energy storage from the renewable resources is getting rapidly increase. Na/$NiCl_2$ cell could be use electric vehicles as well as energy storage, because it has a high energy-efficiency, environmental-friendly, low cost. However, there remain several issues on improvement of materials, component, cell design, and process, to use in broad applications and to penetrate to market. This paper offers a comprehensive review on R&D status of the structure, chemistry, key materials, and cell design & manufacture for Na/$NiCl_2$ cells.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.4
• /
• pp.57-61
• /
• 2016

Thick film sealing glass paste is required for cell packaging of NaS based battery for energy storage system, to join the beta-alumina electrolyte tube and the alpha-alumina battery cell cap components. This paper presents the effect of the particle sizes of seal glass powder and the sealing temperatures on the microstructure of the glass sealants was investigated. It was found that the larger in the particle size of seal glass powder, the smaller the pore volume and the number of pores in a unit area. Also, the number of pores decreased with increasing the sealing temperatures while the pore size was increased. This result enables the control of porosity, pore distribution and number of pores in a microstructure of glass sealing component by proper selection of glass powders particle size and sealing temperature.

• Journal of the Korean Ceramic Society
• /
• v.54 no.3
• /
• pp.200-204
• /
• 2017

Molybdenum (Mo), an electrode material of alkali metal thermal-to-electric converters (AMTEC), facilitates grain growth behavior and forms Mo-Na-O compounds at high operating temperatures, resulting in reduced performance and shortened lifetime of the cell. Mo/TiN composite materials have been developed to provide a solution for such issues. Mo is a metal that possesses excellent electrical properties, and TiN is a ceramic compound with high-temperature durability and catalytic activity. In this study, a dip-coating process with an organic solvent-based slurry was used as an optimal coating method to achieve homogeneity and stability of the electrodes. Cell performance was evaluated under various conditions such as the number of coatings, ranging from 1 to 3 times, and heat treatment temperatures of $800-1100^{\circ}C$. The results confirmed that the cell yielded a maximum power of 9.99 W for the sample coated 3 times and heat-treated at $900^{\circ}C$.

• Journal of the Korean Electrochemical Society
• /
• v.16 no.3
• /
• pp.111-122
• /
• 2013

Sodium sulfur (NAS) battery is a high energy storage system (ESS). These days, as the use of renewable green energy like wind energy, solar energy and ocean energy is rapidly increasing, the demand of ESS is increasing and NAS battery is considered to be one of the most promising ESS. Since NAS battery has a high energy density(3 times of lead acid battery), long cycle life and no self-charge and discharge, it is a good candidate for ESS. A NAS battery consists of sulfur as the positive electrode, sodium as the negative electrode and ${\beta}$"-alumina as the electrolyte and a separator simultaneously. Since sulfur is an insulator, carbon felt should be used as conductor with sulfur and so the composition and property of the cathode could largely influence the cell performance and life cycle. Therefore, in this paper, the composition of NAS battery, the property of carbon felt and sodium polysulfides ($Na_2S_x$, intermediates of discharge), and the effects of these factors on cycle performance of cells are described in detail.

• The Korean Journal of Nuclear Medicine Technology
• /
• v.22 no.2
• /
• pp.67-73
• /
• 2018

$[^{11}C]PIB$ synthesis has been performed by a loop-methylation and HPLC purification in our lab. However, this method is time-consuming and requires complicated systems. Thus, we developed an on-cartridge method which simplified the synthetic procedure and reduced time greatly by removing HPLC purification step. We compared 6 different cartridges and evaluated the $[^{11}C]PIB$ production yields and specific activities. $[^{11}C]MeOTf$ was synthesized by using TRACERlab FXC Pro and was transferred into the cartridge by blowing with helium gas for 3 min. To remove byproducts and impurities, cartridges were washed out by 20 mL of 30% EtOH in 0.5 M $NaH_2PO_4$ solution (pH 5.1) and 10 mL of distilled water. And then, $[^{11}C]PIB$ was eluted by 5 mL of 30% EtOH in 0.5 M $NaH_2PO_4$ into the collecting vial containing 10 mL saline. Among the 6 cartridges, only tC18 environmental cartridge could remove impurities and byproducts from $[^{11}C]PIB$ completely and showed higher specific activity than traditional HPLC purification method. This method took only 8 ~ 9 min from methylation to formulation. For the tC18 environmental cartridge and conventional HPLC loop methods, the radiochemical yields were $12.3{\pm}2.2%$ and $13.9{\pm}4.4%$, respectively, and the molar activities were $420.6{\pm}20.4GBq/{\mu}mol$ (n=3) and $78.7{\pm}39.7GBq/{\mu}mol$ (n=41), respectively. We successfully developed a facile on-cartridge methylation method for $[^{11}C]PIB$ synthesis which enabled the procedure more simple and rapid, and showed higher molar radio-activity than HPLC purification method.

• Journal of dental hygiene science
• /
• v.11 no.5
• /
• pp.405-410
• /
• 2011

The aim of this study was to evaluate antibacterial effect of Cl coated titanium. To coat the Cl on the titanium, first, the titanium was modified by blasting treatment with hydroxyapatite and alumina powder. Anodization process was completed using electrolyte solution of 0.04 M ${\beta}$-glycerol phosphate disodium salt n-hydrate, 0.4 M calcium acetate n-hydrate and 1 M NaCl on the condition of 250 voltages for 3 min. Surface morphology and elements' observation were performed with scanning electron microscopy and energy dispersive spectroscopy and surface profiler was used to analyze the surface roughness. Antibacterial effect was evaluated by film adhesion method. The anodized titanium after blasting showed dimpled surface contained the Cl. Surface average roughness of these surfaces had significantly higher compared to polished titanium. Result of antibacterial test showed that anodized titanium after blasting had an enhanced antibacterial effect compared to the polished titanium. Therefore, these results suggested that titanium contained Cl by anodization after blasting had a rough surface as well as antibacterial effect.