• Elastomers and Composites
• /
• v.53 no.2
• /
• pp.67-74
• /
• 2018

Magneto-rheological elastomers (MREs) are smart materials in which the inherent stiffness and damping properties can be changed by the influence of an external magnetic field. The magneto-rheological (MR) effect depends on the orientation characteristics of the dispersed magneto-responsible particles (MRPs) in the matrix. In this study, natural rubber (NR) and ethylene propylene diene rubber (EPDM) were blended and used as a matrix of an MRE. EPDM was pre-cured before blending with NR. The Mooney viscosity, curing characteristics, and mechanical properties were analyzed with various pre-curing conditions of EPDM and the NR/EPDM blend. The results show that excellent mechanical properties of the NR/EPDM blend-based MRE were obtained when the pre-curing time of EPDM was 60 min. The aging property of the NR-based MRE was improved by the introduction of pre-cured EPDM. Also, the anisotropic MRE showed a higher MR effect than that of the isotropic MRE.

• Elastomers and Composites
• /
• v.7 no.2
• /
• pp.183-192
• /
• 1972

As a series of tile studies of EPDM-Polymer blends, tile experiment are concentrated to the investigation of the physical properties of tile EPDM-NR-SBR blends. The results are shown as follows: 1. In blending, tensile strength decreased with increase in EPDM contents, especially the ratio of EPDM/NR-SBR is 75/25. 2. Elongation and tear strength were much influenced by blending, especially the ratio of EPDM/NR-SBR is 50/50. 3. Ozone resistance is much improved after blending. It was effective more than tile ratio of EPDM/NR-SBR is 25/75. 4. Aging resistance is much improved after blending. It was effective more than the ratio of EPDM/NR-SBR is 50/50. 5. Hardness increased with increase in EPDM contents and on the other hand, abrasion resistance decreased.

• Elastomers and Composites
• /
• v.29 no.2
• /
• pp.121-130
• /
• 1994

The physical properties of rubber blend between natural rubber(NR) and ethylene propylene diene terpolymer(EPDM) were investigated as a study of EPDM composite materials. For EPDM/NR blends, the effects of ethylene and diene contents in EPDM, blend ratio, dicumyl peroxide(DCP) curing system on the physical properties, interfacial adhesion force and dynamic crack growth etc. were studied. EPDM/NR blends loaded with carbon black were prepared by mechanical mixing and cured by plate heating cure press. Crosslinking density was measured by swelling method with toluene. The physical properties of all blends were measured with Instron, fatigue to failure(FTF), Demattia flex cracking tester(DMFC), scanning electron microscopy (SEM), etc. As the ethylene and diene contents in EPDM increased, the physical properties, such as dynamic crack growth, adhesion to other component were increased too. Interfacial adhesion force of EPDM/NR blends to dissimilar layer was improved by the use of optimum peroxide curing system.

• Macromolecular Research
• /
• v.9 no.6
• /
• pp.319-326
• /
• 2001

Fatigue crack growth (FCG) behavior of natural rubber/ethylene-propylene-diene rubber (NR/EPDM) blend vulcanizates under dynamic tearing condition was investigated by using a fracture mechanics approach. It appeared that variation of crack growth rate with blend compositions was dependent on the level of imposed tearing energy G. At low tearing energy region, the FCG rates of the blend were lower as the EPDM content was increased, while at high tearing energy region, the trend was reversed. Over the measured range of tearing energy G, all blend compositions showed the lower crack growth rates compared to the average of properties of component elastomers. When the blends were thermally aged, the fatigue resistance of the blends was deteriorated in proportion to the concentration of EPDM phase. Fatigue crack growth behavior of the blends was supposed to be associated with the inhomogeneities of the crosslink structure of the blends arising from cure incompatibility of the EPDM and NR when they are sulphur cured.

• Elastomers and Composites
• /
• v.6 no.2
• /
• pp.65-72
• /
• 1971

The purpose of this study is to establish an effective way to utilize the application of EPDM-Polymer blends. First of all, the physical properties for EPDM/NR blends and compounding agents were studied. The results are shown as follows: 1. In blending, tensile strength and tear strength decreased with increase in EPDM contents. It was not effective more than the ratio of EPDM/NR is 50/50. 2. Elongation is influenced by blending, especially the ratio of EPDM/NR is 50/50. 3. It was found that both the resistance for ozone and aging were much improved after blending.

• Elastomers and Composites
• /
• v.6 no.2
• /
• pp.73-79
• /
• 1971

As a series of the studies of EPDM-Polymer blends, the experiments are concentrated to the investigation of the physical properties of the EPDM-SBR blends. The results are shown as follows: 1. Tensile strength decreased with increase in EPDM contents and the decreasing value was good results than NR blending. 2. It was found that the aging were much improved after blending and experiments data was good results than NR blending.

• Journal of Adhesion and Interface
• /
• v.2 no.4
• /
• pp.32-38
• /
• 2001

Effects of the ratio of rubber composition on covulcanization and ozone resistance were studied in this study. Specimens used in this study were rubber compounds(specimen-A) blended with various ratio of NR, SBR, BR, IIR, and EPDM, unsaturated rubber compounds(specimen-B) with NR/BR/SBR, and saturated rubber compounds(specimen-C) with NR/IIR/EPDM. PAD adhesion specimen was prepared from vulcanizing specimen-A and B, and specimen-A and C, respectively. Using same adhesion specimen, peel strength was measured and tested ozone resistance. In specimen-A, peel strength was higher with increasing NR ratio for NR and BR contained blends. In other specimen-A containing NR and SBR, the peel strength was also increased with increasing SBR ratio. NR/BR/IIR/EPDM rubber compounds had also better adhesion property than NR/SBR/IIR/EPDM compounds. As more unsaturated rubber was blended, the peel strength was higher but ozone resistance was worse. Optimum ratio of unsaturated and saturated rubbers for the peel strength and ozone resistance was 60/40.

• Elastomers and Composites
• /
• v.22 no.4
• /
• pp.314-323
• /
• 1987

A blend ratio of rubber vulcanzates comprising NBR, CR, EPDM, NR, BR, and SBR alone or blended is determind through a P.G.C. It is found that a characteristic peak of elastomer is proportional to the content of each elastomer when they are pyrolysed. It is also classified to the different AN content in NBR vulcanizates, identification of sulfur-modified and non-sulfur bearing CR polymers, and the content of ethylene, propylene monomer and the third monomer in EPDM vulcanizetes.

• Journal of Veterinary Clinics
• /
• v.24 no.2
• /
• pp.201-207
• /
• 2007

The teat cup liner compounds with improved physical property were developed using tri-polymer blend of natural rubber(NR), ethylene propylene diene monomer rubber(EPDM) and butyl rubber, and the changes of the physical properties of compounds were measured under various conditions such as standard, thermal, alkaline detergent and acid solutions aging conditions. The hardness of the new teat cup liner compound 1 was 50 and that of the compound 2 was 51 under standard condition. The tensile strength and elongation of the new compound 1 were $154kgf/cm^2$ and 675% under the standard condition, respectively. Also, those of the new compound 2 were 180 kgf/cm and 634% under the same condition. Their hardness were increased about $2{\sim}6%$ and the tensile strength and elongation were decreased about 10% under the $25^{\circ}C$ water and detergent solutions. Even though the new teat cup liner compounds exhibited so much decreased tensile properties under the $105^{\circ}C$ thermal aged condition, they sustained more stable aged physical properties including tensile strength and elongation than those of imported teat cup liner materials. Consequently, the new teat cup liner compounds would give prolonged lift cycle if they are used as a teat cup liner product.