• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.7
• /
• pp.713-719
• /
• 2016

The NOx conversion properties of Mn-Cu-$TiO_2$ and $V_2O_5$/$TiO_2$ catalysts were studied for the selective catalytic reduction (SCR) of NOx with ammonia. The performance of the catalysts was investigated in terms of their $NOx$ conversion activity as a function of the reaction temperature and space velocity. The activity of the Mn-Cu-$TiO_2$ catalyst decreased with increasing reaction temperature and space velocity. However, the activity of the $V_2O_5$/$TiO_2$ catalyst increased with increasing reaction temperature. High activity of the Mn-Cu-$TiO_2$ catalyst was observed at temperatures below $200^{\circ}C$. H2-TPR and XPS analyses were conducted to explain these results. It was found that the activity of the Mn-Cu-$TiO_2$ catalyst was influenced by the thermal shock caused by the change of the initial reaction temperature, whereas the $V_2O_5$/$TiO_2$ catalyst was not affected by the initial reaction temperature. In the case of catalyst C, the $NO_x$ conversion efficiency decreased with increasing space velocity. The decrease in the $NO_x$ conversion efficiency with increasing space velocity was much less for catalyst D than for catalyst C.

• Journal of Korean Society for Atmospheric Environment
• /
• v.18 no.E1
• /
• pp.29-36
• /
• 2002

The selective catalytic reduction (SCR) reaction of promoter catalysts was investigated in this study. A pure anatase type of TiO$_2$ was used as support. Activation measurement of prepared catalysts was practiced on a fixed reactor packing by the glass bead after filling up catalysts in 1/4 inch stainless tube. The reaction temperature was measured by K-type thermocouple and catalyst was heated by electric furnace. The standard compositions of the simulated flue gas mixture in this study were as follows: NO 1,780ppm, NH$_3$1,780ppm, $O_2$1% and $N_2$ as balance gas. In this study, gas analyzer was used to measure the outgassing gas. Catalyst bed was handled for 1hr at 45$0^{\circ}C$, and the reactivity of the various catalyst was determined in a wide temperature range. Conversion of NH$_3$/NO ratio and of $O_2$ concentration was practiced at 1,1.5 and 2, respectively. The respective space velocity were as follows . 10,000, 15,000 and 17,000 hr-1. It was found that the maximum conversion temperature range was in a 5$0^{\circ}C$. It was also found toi be very sensitive at space velocity, $O_2$ concentration, and NH$_3$/NO ratio. We also noticed that the maximum conversion temperature of (W, Mo, Sn) -V$_2$O$_{5}$/TiO$_2$ catalysts was broad. Specially WO$_3$-V$_2$O$_{5}$TiO$_2$2 catalyst appeared nearly 100% conversion at not only above 30$0^{\circ}C$ ut also below 25$0^{\circ}C$. At over 30$0^{\circ}C$, NH$_3$ oxidation decreased with decrease of surface excess oxygen. In addition, WO$_3$-V$_2$O$_{5}$TiO$_2$ catalyst did not appear to affect space velocity, $O_2$ concentration, and NH$_3$/NO ratio.ratio.

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.4
• /
• pp.609-617
• /
• 2000

This study is aimed at investigating an effect of HCl gas on selective reduction of NOx over a CuHM and $V_2O_5-WO_3/TiO_2$ catalyst. SCR process is the most effective method to remove NOx, but catalyst can be deactivated by the acidic gas such as HCl gas which is also included in flue gas from the incinerator. In dry condition of flue gas, the CuHM catalyst treated by HCl gas has shown higher NO removal activity than the fresh catalyst. The activity of the catalyst can be restored by treating at $500^{\circ}C$. On the contrary. $V_2O_5-WO_3/TiO_2$ catalyst is obviously deactivated by HCl and the deactivation increases in proportion to the concentration of HCl gas. The deactivated catalyst is not restored to it's original activity by heat treatment for regeneration. In wet flue gas stream, the CuHM catalyst has shown lower activity than fresh catalyst and $V_2O_5-WO_3/TiO_2$ catalyst was severely deactivated by HCl treatment. The activity loss of catalysts are mainly due to the decrease of Br$\ddot{o}$nsted acid site on the catalyst surface by $NH_3$ TPD. The change of BET surface area of CuHM catalyst after the reaction isn't observed but $V_2O_5-WO_3/TiO_2$ catalyst is observed. The amount of $Cu^{{+}{+}}$ and $V_2O_5$ is decreased after the reaction. From these results, it is expected that CuHM catalyst should be better than $V_2O_5-WO_3/TiO_2$ catalyst for its application to the incineration of flue gas.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.4
• /
• pp.451-463
• /
• 2004

The performance of disk-type catalytic filters impregnated by TiO$_2$ or TiO$_2$-3Al$_2$O$_3$ㆍ 2SiO$_2$ supports and V$_2$O$_{5}$ catalyst was evaluated for selective catalytic reduction (SCR) of NO with ammonia as a reductant. XRD, FT -IR, BET and SEM were used to characterize the catalytic filters prepared in this work. Optimal V$_2$O$_{5}$ loading and reaction temperature for V$_2$O$_{5}$/TiO$_2$ catalytic filters were 3-6 wt.% and 350-40$0^{\circ}C$ at GHSV 14,300 $hr^{-1}$ in the presence of oxygen, respectively. With increasing the V$_2$O$_{5}$ loading from 0.5 to 6 wt%, NO conversion increased from 24 to 96% at 40$0^{\circ}C$ and 14.300$hr^{-1}$, and maintained at 80% over in the V$_2$O$_{5}$ loading range of 3-6 wt.% and then dropped at V$_2$O$_{5}$ loading of 7wt.% over. In comparing V$_2$O$_{5}$/ TiO$_2$ and V$_2$O$_{5}$/ TiO$_2$-3Al$_2$O$_3$ㆍ2SiO$_2$ catalytic fillers, which have same 3wt.% V$_2$O$_{5}$ loading, the V$_2$O$_{5}$/ TiO$_2$-3A1$_2$O$_3$ㆍ2SiO$_2$ catalytic filter showed higher activity than V$_2$O$_{5}$/ TiO$_2$ catalytic filter, but higher differential pressure drops owing to its low air permeability. low air permeability.