• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.225-231
• /
• 2013

In this study, we observed the effect of carboxylated SBR latex and zinc oxide on styrene-butadiene-styrene( SBS) composites for improving abrasion and debris. SBS composite, which added only silica, showed poor mechanical properties, NBS abrasion, and debris, caused by strong filler-filler interaction of silica. In case of adding carboxylated SBR latex, mechanical properties, NBS abrasion and debris of SBS composite were improved. Because of carboxyl group of carboxylated SBR latex interacted with silanol group of silica. Both carboxylated SBR latex and zinc oxide were added, SBS composite showed highest mechanical properties, NBS abrasion, and debris by forming ion cluster between carboxylated SBR latex and zinc oxide. By FT-IR analysis, ion clusters were confirmed that observed zinc carboxylated group stretch peak at $1550{\sim}1650cm^{-1}$ range. SBS composite, SC-4, showed excellent mechanical properties ; tensile strength $156kgf/cm^2$, elongation 936%, tear strength 59.4kgf/cm ; and excellent abrasion characteristics ; NBS abrasion 338%. Also, debris of SC-4 was minimized and showed wave-shape in fracture surface.

• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.195-200
• /
• 2013

The main objective of this study is to improve abrasion resistance and wet slip resistance of thermoplastic polyurethane (TPU) by blending with ethylene-propylene-diene monomer rubber (EPDM) or polybutadiene rubber (BR) for the application of the footwear outsole materials. With addition of 10 wt% of EPDM or BR, TPU/EPDM and TPU/BR blends exhibited higher NBS abrasion resistance, tensile properties and wet slip resistance than TPU. However, with further increasing content of EPDM and BR, abrasion resistance and tensile properties of the blends decreased. Improvement in abrasion resistance and tensile properties with 10 wt% of addition of EPDM or BR may be due to better microphase separation of TPU.

• Elastomers and Composites
• /
• v.53 no.4
• /
• pp.202-206
• /
• 2018

Five solution styrene butadiene rubber/neodymium butadiene rubber (SSBR/NdBR) composites were manufactured using different ratios of SSBR and NdBR. In this study, the composites were reinforced with NdBR and silica to confirm the physical properties of SSBR used for treads of automobile tires and the dispersibility with silica. The morphologies of the rubber composites were observed using field-emission scanning electron microscopy (FE-SEM). The crosslinking behaviors of the composites were tested using a rubber process analyzer (RPA), and the abrasion resistances were tested using a National Bureau of Standards (NBS) abrasion tester. The hardness values, tensile strengths, and cold resistances of the composites were also tested according to ASTM standards. Increased NdBR content yielded composites with excellent crosslinking properties, abrasion resistances, hardnesses, tensile strengths, and cold resistances. The crosslinking point increased due to the double bond in NdBR, thereby increasing the degree of crosslinking in the composites. The NdBR-reinforced composites exhibited excellent abrasion resistances, which is explained as follows. In SSBR, a breakage is permanent because a resonance structure between styrene and SSBR forms when the molecular backbone is broken during the abrasion process. However, NdBR forms an additional crosslink due to the breakdown of the molecular backbone and high reactivity of the radicals produced. In addition, the low glass transition temperature (Tg) of NdBR provided the rubber composites with excellent cold resistances.

• Journal of Adhesion and Interface
• /
• v.19 no.2
• /
• pp.55-59
• /
• 2018

In this study, to overcome a complicated shoe adhesion process such as buffing, pre-treatment by primer in the rubber component of the shoe, we studied adhesion mechanical properties with rubber compound added water-soluble salt for the purpose of improving the adhesion between midsole and outsole. Acid salts, basic salt and neutral salts were evaluated, rubber containing basic salts showed excellent adhesion to water-based adhesion. Since the basic salt is present as the hydroxy salt, the surface of rubber is hydrophilized. The results are confirmed by contact angle and IR spectroscopy measurement. In addition, in the case of rubber compound added basic salts, NBS abrasion resistance and hardness were increased by increasing crosslink density, but crosslink time was delayed.

• Clean Technology
• /
• v.15 no.3
• /
• pp.172-179
• /
• 2009

The thermoplastic polyurethane waste (TPU-S) with good tensile properties, hardness, NBS abrasion resistance, specific gravity and low wet coefficient of kinetic friction was melt-blended with ethylene propylene diene monomer rubber (EPDM) with high wet slip resistance and low mechanical properties to form EPDM/TPU-S blend films, and their composition-property relationship was investigated to find the optimum composition for shoe outsole material. The properties except the wet slip resistance increased with increasing TPU-S contents in the blend. All the properties except elongation at break, specific gravity and the wet coefficient of kinetic friction in the range of $0{\sim}65\;wt%$ of TPU-S did not attain the values predicted by the simple additive rule. The optimum weight ratio of EPDM/TPU-S for the application to the typical shoe outsole material was found to be 30/70.