Superparamagnetic Properties off Zn0.5Ni0.5Fe2O4 Nanoparticles (나노입자 Zn0.5Ni0.5Fe2O4 초상자성 성질 연구)

  • Lee, Seung-Wha
    • Journal of the Korean Magnetics Society
    • /
    • v.16 no.1
    • /
    • pp.40-44
    • /
    • 2006
  • [ $Zn_{0.5}Ni_{0.5}Fe_2O_4$ ] nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, and Mossbauer spectroscopy, VSM. $Zn_{0.5}Ni_{0.5}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically at room temperature. The estimated size of superparammagnetic $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle is around 7 nm. The hyperfine fields of the A and I patterns at 4.2 K were found to be 510 and 475 kOe, respectively. The blocking temperature $(T_B)$ of superparammagnetic $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle is about 90 K. The magnetic anisotropy constant and relaxation time constant of $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle were calculated to be $K=1.6\times10^6erg/cm^3$.

Mossbauer study of $CoCr_xFe_{2-x}O_4$ (Mossbauer 분광법에 의한 $CoCr_xFe_{2-x}O_4$의 연구)

  • 채광표;이혁진;이재광;이성호;이영배
    • Journal of the Korean Magnetics Society
    • /
    • v.10 no.2
    • /
    • pp.74-80
    • /
    • 2000
  • CoCr$_{x}$ Fe$_{2-x}$O$_4$(0.0$\leq$x$\leq$1.0) ferrites have been fabricated by sol-gel method. The crystallographic and magnetic properties of the samples were investigated by means of x-ray diffraction, scanning electron microscophy, Mossbauer spectroscopy and vibrating sample magnetometry. The structure of all the samples is cubic spinel type and the lattice constant decrease with increasing Cr content. The substituted Cr ions were located only in the B-site. The particle size also decreases with increasing Cr content. The Mossbauer spectra consist of two sextets due to Fe$^{3+}$ions at A- and B sites for 0.0$\leq$x$\leq$0.6, while, a paramagnetic doublet appears for 0.8$\leq$x$\leq$1.0. The magnetic hyperfine field decreases with increasing Cr content. The relaxation spectra was shown at 0.8$\leq$x$\leq$1.0 in CoCr$_{x}$ Fe$_{2-x}$O$_4$. The coercivity decreases drastically, while, the saturation magnetization decreases linearly with increasing x.ing x.

  • PDF

Growth and Magnetic Properties of $Y_{3-x}La_xFe_5O_{12}(0.0{\le}X{\le}1.0)$ Powders and Thin Films by a Sol-Gel Method (Sol-Gel 법에 의한 $Y_{3-x}La_xFe_5O_{12}(0.0{\le}X{\le}1.0)$ 분말과 박막의 합성 및 자기적 특성에 관한 연구)

  • 엄영랑;김철성;임연수;이재광
    • Journal of the Korean Magnetics Society
    • /
    • v.8 no.6
    • /
    • pp.350-356
    • /
    • 1998
  • $Y_{3-x}La_xFe_5O_{12}$ (x=0.0, 0.25, 0.5, 0.75, 1.0) powders and thin films were fabricated by a sol-gel method and their magnetic properties and crystal structure were investigated by using X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), vibrating sample magnetometer (VSM), and Mossbauer spectroscopy. XRD and Mossbauer spectroscopy measurements show that garnet powders annealed at 900 $^{\circ}C$ for 8 hours were single-phased and that thin films fired at 800 $^{\circ}C$ for 2 hours were crystallized without any preferred direction. X-ray diffraction patterns of $Y_{3-x}La_xFe_5O_{12}$ powders annealed at 1000 $^{\circ}C$ had only peaks of the garnet structure in case of x$\leq$0.75 but those of $Y_2LaFe_5O_{12}$ powders consisted of peaks from garnets and $LaFeO_3$. Mossbauer sepectra of garnet powders grown by the sol-gel method had a similar shape of those of powders grown by a conventional ceramic method. Grain sizes of garnet powders were 200~300 nm and the averaged surface roughness was 3.17 nm. Results of VSM measurements show the powders and thin films had soft magnetic properties and that the garnet powders had the largest saturation magnetization, 30 emu/g, and the lowest coercivity, 52 Oe.

  • PDF

Crystallographic and Magnetic Properties of Cu0.1Fe0.9Cr2S4 (Cu0.1Fe0.9Cr2S4의 결정학적 및 자기적 성질에 관한 연구)

  • Son, Bae-Soon;Kim, Sam-Jin;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.14 no.1
    • /
    • pp.33-37
    • /
    • 2004
  • Cu$_{0.1}$Fe$_{0.9}$Cr$_2$S$_4$ has been studied with Mossbauer spectroscopy, x-ray diffraction, vibrating sample magnetometer (VSM), and magnetoresistance (MR) measurement. The crystal structure was determined to be a cubic spinel with lattice parameter a$_{0}$=9.9880 $\AA$. The MR measurements show a semiconductor behavior below 110 K and metal behaved above 100 K. The temperature dependence of magnetization of Cu$_{0.1}$Fe$_{0.9}$Cr$_2$S$_4$ was reported. In addition to a large irreversibility between the zero-field-cooling (ZFC) and the field-cooling (FC) magnetization at applied field H=100 Oe, a cusp-like anomaly was observed in both the FC and ZFC curves. It shifted toward the lower temperature region with increasing magnetic field, and then showed convex type maximum at 110 K, under the applied field of 5 kOe. The Mossbauer spectra were measured from 15 K to room temperature. The asymmetric line broadening was observed for the sample Cu$_{0.1}$Fe$_{0.9}$Cr$_2$S$_4$, and it was considered to be dynamic Jahn-Teller relaxation. The charge state of Fe ions was ferrous in character. The unusual reduction of magnetic hyperfine field below 110 K was interpreted in terms of cancellation effect between the mutually opposite orbital current field (H$_{L}$) and Fermi contact field (H$_{C}$).

Investigation of Mössbauer Spectra of Ba2Mg0.5Co1.5(Fe0.99In0.01)12O22 (Ba2Mg0.5Co1.5(Fe0.99In0.01)12O22의 뫼스바우어 분광 연구)

  • Lim, Jung-Tae;Kim, Chin-Mo;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.22 no.1
    • /
    • pp.19-22
    • /
    • 2012
  • $Ba_2Mg_{0.5}Co_{1.5}(Fe_{0.99}In_{0.01})_{12}O_{22}$ was prepared by the conventional solid-state reaction method, and studied by x-ray diffractometer, vibrating sample magnetometer, and Mossbauer spectrometer. The crystal structure was determined to be a single-phased rhombohedral with space group R-3m. Magnetization value were $M_s$ = 28.6 emu/g at 295 K. The hysteresis loops indicate that all the samples are ferrimagnetic behaviors. Mossbauer spectra of $Ba_2Mg_{0.5}Co_{1.5}(Fe_{0.99}In_{0.01})_{12}O_{22}$ have been 6-sextet taken at various temperatures ranging from 4.2 to 620 K. Based on the isomer shift (${\delta}$) values of all samples, the charge states were found to be $Fe^{3+}$ state at all temperatures, the Curie temperature was determined to be 630 K by the ZVC curve.

The Effect of Non Magnetic ion Substitution for the FeCr2-xMxS4(M=Ga, In) by Mossbauer Spectroscopy (비자성 이온 Ga, In이 치환된 유화물 스피넬의 뫼스바우어 분광학 연구)

  • Son, Bae-Soon;Kim, Sam-Jin;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.16 no.1
    • /
    • pp.6-10
    • /
    • 2006
  • The sulphur spinel $FeCr_{2-x}M_xS_4$(M=Ga, In) have been studied with Mossbauer spectroscopy, x-ray diffraction (XRD), and vibrating sample magnetometer. The XRB patterns for samples $FeCr_{2-x}M_xS_4$(M=Ga, In: x=0.1, 0.3) reveal a single phase, which the Ga and In ions are partially occupied to the tetrahedral (A) site. The Neel temperature for the Ga substituted samples increases from 180 to 188 K, with increase from x=0.1 to 0.3. While, it decreases from 173 to 160 K, for the In substituted samples of the x=0.1 and 0.3, respectively. The Mossbauer spectra were collected from 4.2 K to room temperature. We have analyzed the Mossbauer spectra using eight Lorentzian lines fitting method for the $FeCr_{2-x}In_xS_4$(x=0.1) at 4.2 K, yielding the 1311owing results; $H_{hf}=146.0kOe,\;{\Delta}E_Q=1.88mm/s,\;\theta=36^{\circ},\;\phi=0^{\circ},\;\eta=0.6$, and R=1.9. The Ga ions enter into the both sites octahedral (B) and tetrahedral (A), simultaneously the same amounts of Fe ions migrate from the A to the B site, this result is an agreement with XRD results, too. The ${\Delta}E_Q$ of the A and B site in Mossbauer spectra of the samples $FeCr_{2-x}Ga_xS_4$(x=0.3) are 0.83 and 2.94mm/s, respectively. While they are 0.56 and 2.36mm/s for the $FeCr_{2-x}In_xS_4$(x=0.3). It is noticeable that the ${\Delta}E_Q$ for the Ga doped samples are larger than that of the corresponding In doped samples, in spite of the larger ionic radius for In ions. The bond lengths of Cr-S, for the Ga and In doped samples (x=0.3) are found to be 2.41 and $2.43\;{\AA}$, respectively. We interpret that the larger covalence effect from the smaller bond length induces a large asymmetric charge distribution. Finally, it gives a large quadrupole interaction.

Crystallographic and Magnetic Properties of Li0.5Fe2.5-χRhχO4 by Using Applied Field Mossbauer Spectrometer (외부자기장 뫼스바우어 분광기를 이용한 Li0.5Fe2.5-χRhχO4의 자기적 성질과 결정학적 구조에 관한 연구)

  • Kang, Kun-Uk;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.14 no.6
    • /
    • pp.219-223
    • /
    • 2004
  • L $i_{0.5}$F $e_{2.5-{\chi}}$R $h_{\chi}$ $O_4$ ($\chi$ = 0.25, 0.50, 0.75, 1.00) has been prepared by solid state reaction. Crystallographic and magnetic properties were investigated by Mossbauer spectroscopy, SQUID magnetometry, and x-ray diffraction. The crystal structure is found to be a cubic spinel structure with space group Fd3m for all the samples. The lattice constant $a_{0}$ increases from 8.3365 $\AA$ to 8.3932 $\AA$ with increasing Rh concentration $\chi$. The migration of Li ion has been confirmed by x-ray patterns and the results of applied field Mossbauer analysis. The temperature dependence of the absorption area of each site was analyzed with the Debye model for the recoil-free fraction. The Debye temperature for the octahedral sites is almost as large as for the tetrahedral sites, thereby suggesting similar inter-atomic binding forces for the octahedral and the tetrahedral sites. The saturated magnetic moment and the Mossbauer spectra taken at 4.2 K under the applied field (6 T) show that the spin structure of L $i_{0.5}$F $e_{2.5-{\chi}}$R $h_{\chi}$ $O_4$ is compatible with the collinear Neel Model.

Crystallization and Magnetic Properties of Iron Doped La-Ba-Mn-O (Fe이 치환된 LaBaMnO계 산화물의 중성자 회절 및 Messbauer분광학연구)

  • Choi, Kang-Ryong;Kim, Sam-Jin;Shim, In-Bo;Kim, Chul-Sung
    • Journal of the Korean Magnetics Society
    • /
    • v.14 no.1
    • /
    • pp.38-44
    • /
    • 2004
  • The iron doped colossal magnetoresistance materials with La-Ba-Mn-O perovskites structure have been synthesized by chemical reaction of sol-gel methods. Their crystallographic and magnetic properties have been studied with x-ray diffraction, VSM, RBS, Mossbauer spectroscopy, and magnetoresistance measurements. The crystal structure of the La$\_$0.67/Ba$\_$0.33/Mn$\_$0.99/Fe$\_$0.01/ $O_3$ at room temperature was determined to be orthorhombic of Pnma. The lattice parameters a$\_$0/ and c$\_$0/ increased gradually, but b$\_$0/ deceased with increase of iron substitution. The magnetization and coercivity deceased, also the Curie temperature decreased from 360 K as x increased from 0.00 to 0.05. Magnetoresistence measurements were carried out, and the maximum MR ($\Delta$$\rho$/$\rho$(0)) was observed at 281 K, about 9.5 % in 10 kOe. The temperature of maximum resistance (R$\_$MAX/) decreased with increasing substitution of Fe ions and a semiconductor-metal transition temperature (T$\_$SC-M/) decreased too. This phenomena show that ferromagnetic transition temperature decreased by substituting Fe for Mn ions, it decreases double exchange interaction. This result accords with magnetic structure of neutron diffraction. Mossbauer spectra of La$\_$0.67/Ba$\_$0.33/Mn$\_$0.99/Fe$\_$0.01/ $O_3$were taken at various temperatures ranging from 15 to 350 K. With lowering temperature of the sample, two magnetic phases were increased and finally it showed the two sharp sextets of spectra at 15 K. The isomer shift at all temperature range is about 0.3 mm/s relative to Fe metal, which means that both Fe ions are Fe$\^$3+/ states.Fe$\^$3+/ states.

Mossbauer Study Of $Co{1+x}Fe{2-2x}Ti_xO_4$ ferrite Powders (Mossbauer 분광법에 의한 $Co{1+x}Fe{2-2x}Ti_xO_4$ 페라이트 분말의 연구)

  • 채광표;정성근;김원기;이성호;이영배
    • Journal of the Korean Magnetics Society
    • /
    • v.10 no.5
    • /
    • pp.220-224
    • /
    • 2000
  • Ultra-fine $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$ferrite powders have been prepared by the sol-gel method. The crystallographic and magnetic properties of the sample have been investigated by means of x-ray diffraction, Mossbauer spetroscopy and vibrating sample magnetometry. The formation of nano crystallized particles is confirmed. The x-ray diffractions of all samples with various compositions clearly indicate the presence of spinel structure. The Mossbauer spectra could be fitted as the superposition of two sextets due to F $e^{3+}$ A-site and B-site. The IS and QS values nearly constant with substituted Co-Ti contents, whereas $H_{hf}$ of B-site decreases with increasing Co-Ti substitution in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$. The magnetic behaviour of powders shows that the saturation magnetization and the coercivity decrease with increasing x in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$.$.X>.

  • PDF

Spin-Flop of α-Fe2O3 Nano Particles (α-Fe2O3 나노 입자에서 Spin-Flop에 관한 연구)

  • Sur, Jung-Chul;Park, Chul-Jin;Choi, Jung-Wan;Gee, S.H.;Hong, Y.K.
    • Journal of the Korean Magnetics Society
    • /
    • v.14 no.5
    • /
    • pp.169-173
    • /
    • 2004
  • We have synthesized monodispersed $\alpha$-F $e_2$ $O_3$ nano particles to investigate the spin change during the Morin transition temperature( $T_{M}$). The particle size was founded to have a very uniform distribution of 80 nm by x-ray diffraction and size dispersion analyzer. The Mossbauer spectra between the 4.2 K and the room temperature show that $T_{M}$ was shifted and the spin states of Fe ion were changed with the particle size. The Morin transition temperature of bulk usually quoted in literature is 265 K but, it decreases with the size and no transition was found at the critical size down to 4.2K. The spin direction of 80 nm sized particles are normal to the hexagonal c-axis above the $T_{M}$ and are tilted about 28~29$^{\circ}$ below $T_{M}$, which is the [110] direction of rombohedral structure.