• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.141-161
• /
• 1998

The depth and patterns of demineralization according to the difference in concentration and application time of phosphoric acid were observed through the transmission electron microscope, and shear bond strengths to the acid -conditioned dentin were then measured and compared with the TEM results. To investigate the influence of polymer addition into the phosphoric acid and the effect of difference in concentration and application time of the acid, the specimens were randomly divided into 9 groups. Among the specimens, the exposed dentin surfaces were acid-conditioned with 10% polymer-thickened phosphoric acid(All Bond 2, Bisco, U.S.A.) and aqueous 10%, 20%, 30%, 40% phosphoric acid for 20 seconds, The rest of the specimens were acid-conditioned with 10% phosphoric acid for 15s, 30s, 60s, 120s respectively. The specimens were immersed in 4% glutaraldehyde in 0.1M sodium cacodylate buffer and postfixed with 1 % osmium tetroxide without decalcification and then observed under a JEOL Transmission Electron Microscope(JEM 1200 EX II, Japan). After the specimens were acid-conditioned as the above, primer and adhesive resin were applied to blot-dried dentin and shear bond strengths were then measured and analysed. The results were as follows : 1. The intertubular demineralization depth of 4.0-$5.0{\mu}m$ in 10% polymer-thickened phosphoric acid gels was similar or slightly deeper than that of 4.0-$4.5{\mu}m$ in aqueous 10% phosphoric acid solution. 2. The intertubular demineralization depth of aqueous 20%, 30% and 40% phosphoric acid solution was 6.5-$7.0{\mu}m$, 6.5-$7.5{\mu}m$ and 9.0-$15.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is partly related to the concentration of phosphoric acid solution. 3. The intertubular demineralization depth of aqueous 10% phosphoric acid solution in application time for 15s, 30s, 60s and 120s was 2.5-$3.0{\mu}m$, 4.0-$6.0{\mu}m$, 6.5-$7.0{\mu}m$ and 8.5-$14.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is directly related to the application time of phosphoric acid solution. 4. The partially demineralized dentin layer between demineralized collagen layer and unaffected dentin was showed to a width of 0.5-$1.0{\mu}m$ in lower concentration groups treated with aqueous 10% phosphoric acid for 20s, 60s, 120s and 20% phosphoric acid for 20s. 5. The demineralization effect at the border of intertubular-peritubular junction was less evident than that in the peritubular and intertubular dentin. The collagen fibers in the intertubular dentin had a random orientation, whereas those that lined the tubules were circumferentially aligned. The cross-linkage of dentinal collagen in demineralized collagen layer was clearly seen. 6. A statistically significant difference of bond strengths according to the difference in phosphoric acid concentration did not exist among the groups treated with 10%, 20%, 30% and 40% acid solution (P>0.05). However, bond strengths to the treated dentin with 10% phosphoric acid solution for 30s were significantly higher than that for 120s (P<0.05).

• Tuberculosis and Respiratory Diseases
• /
• 제48권4호
• /
• pp.478-486
• /
• 2000

연구배경 : 급성폐손상에서 폐포대식세포는 초기에 일어나는 염증반응 뿐 아니라, 후기의 복구 및 섬유화 과정에 관여하는 중요한 세포로 형태, 기능면에서 특성이 다른 여러 세포군으로 구성되어져 있는 것으로 알려져 있다. 95% 이상의 고농도산소로 폐손상을 일으킨 쥐를 12시간군, 24시간군, 48시간군으로 나누어서 고농도 산소 투여시기에 따른 폐포대식세포의 숫적인 변화 및 아형군의 분포변화를 관찰하고, 이들 아형군세포의 형태학적인 차이를 통해서 고농도 산소에 의한 폐손상시에 관련되는 특정 아형세포군이 있는지를 알아보고 이러한 분포의 차이와 조직병리적인 변화를 비교 관찰하였다. 방 법 : Sprague-Dawley계 흰쥐를 대상으로 고농도 산소 투여 후 12시간, 24시간, 48시간 경과시의 폐포대식세포를 추출하여 아형세포군의 분포 및 형태 변화와 조직의 변화를 비교 관찰하였다. 결 과 : 1) 총 폐포대식세포는 정상군 $171.6{\pm}24.1({\times}10^5)$, 12시간군 $194.8{\pm}17.9$, 24시간군 $207.6{\pm}27.1$, 48시간군 $200.0{\pm}77.8$개로 초기 장시간까지는 증가하나 이후에는 유의한 차이를 보이지 않았다. 2) 광학현미경 관찰로 측정한 폐포간질의 두께는 정상군 $0.7{\pm}0.2{\mu}m$, 12시간군 $1.5{\pm}0.4{\mu}m$, 24시간군 $2.3{\pm}0.4{\mu}m$, 48시간군 $2.5{\pm}0.4{\mu}m$로 24시간까지는 시간에 따라서 증가하나 24시간 이후로 유의한 차이는 없었다. 3) 폐포대식세포 분포의 시간 경과에 따른 변화는 fraction 1과 fraction 2는 의미 있게 증가되었으며 fraction 3는 의미 있게 감소하였다. fraction 4는 감소되어지는 양상을 보이나 통계적인 의의는 없었다. 4) 고밀도군에서 주로 관찰되는 세포는 세포 및 핵의 모양이 불규칙적이며 크기가 작고 한쪽으로 치우쳐 있으며, pseudopod, electron dense inclusion의 수가 현저히 많이 관찰됐다. 반면 저밀도군에서 주로 관찰되는 세포는 크기가 크고 세포 및 핵이 둥근형태를 보였다. heterogenous, empty inclusion이 보다 많이 관찰되었고 전반적인 inclusion의 수도 증가했다. 결 론 : 이상의 결과로 고농도산소에 의한 폐손상에서 특정한 폐포대식세포아형군이 폐손상에 중요한 역할을 할 것으로 보여지며 추후 이들 세포군이 증가한 이유 및 기전과 이들 세포군의 기능 및 표현형등에 관한 연구가 계속되어야 할 것이다.