• 한국결정성장학회지
• /
• 제33권6호
• /
• pp.244-249
• /
• 2023

본 연구에서는 고순도 C₃A 합성을 위해 다양한 실험 변수를 설정한 뒤 그에 따른 영향 인자를 확인하였다. 실험 결과 고순도 C₃A 합성을 위해서는 소성 온도가 가장 중요한 인자라고 판단되었으며, 합성량이 증가할 경우 소성 시간을 증가시켜야 한다고 판단되었다. 또한, 탄산칼슘이 C₃A의 초기 수화 반응에 미치는 영향을 확인한 결과 일반 시멘트와는 다르게 초기 반응 생성물로 모노카보알루미네이트가 생성되었으며, 수화 24시간 경과 후 모노카보알루미네이트가 헤미카보알루미네이트로 변환되는 것이 확인되었다. 또한, 탄산칼슘 함량에 따라 모노카보알루미네이트가 생성되는 양이나 속도가 상이한 것을 확인하였다.

• Advances in concrete construction
• /
• 제5권3호
• /
• pp.289-301
• /
• 2017

The synergistic interactions of supplementary cementitious materials (SCMs) with ordinary portland cement (OPC) in multi-blended systems could enhance the mechanical and durability properties of concrete and increase the amount of cement that can be replaced. In this study, the characteristics of the hydration products as well as paste microstructure of blended cement containing 20% coal fly ash, 10% rice hull ash and 10% sugar mill lime sludge in quaternary blended system was investigated. Portlandite content, hydration products, compressive strength, pore size distribution and microstructural architecture of hydrated blended cement pastes were examined. The quaternary blended cement paste showed lower compressive strength, reduced amount of Portlandite phases, and higher porosity compared to plain hardened cement paste. The interaction of SCMs with OPC influenced the hydration products, resulting to the formation of ettringite and monocarboaluminate phases. The blended cement paste also showed extensive calcium silicate hydrates and calcium aluminate silicate hydrates but unrefined compared to plain cement paste. In overall, the expected synergistic reaction was significantly hindered due to the low quality of supplementary cementitious materials used. Hence, pre-treatments of SCMs must be considered to enhance their reactivity as good quality SCMs can become limited in the future.

• 한국세라믹학회지
• /
• 제48권6호
• /
• pp.584-588
• /
• 2011

In this work, effects of limestone powder on hydration of $C_3A-CaSO_4{\cdot}2H_2O$ system was discussed based on the XRD Quantitative analysis, and the possibility of Delayed Ettringite Formation was also discussed. The early hydration of $C_3A$ was delayed by addition of $CaCO_3$ powder. The delay effect was enhanced by increasing of $CaCO_3$ content and finer powder of $CaCO_3$ addition. After consumption of $CaSO_4{\cdot}2H_2O$, the reaction of $CaCO_3$ is started. Delayed Ettringite Formation would take place because monosulfoaluminate is not stable in presence of $CaCO_3$. In order to prevent the delayed ettringite formation in $C_3A-CaSO_4{\cdot}2H_2O-CaCO_3$ system, the reduction of monosulfoaluminate formation is important. Therefore, by increasing the amount of $CaCO_3$ addition and finer $CaCO_3$ powder addition, the delayed ettringite formation can be prevented.

• 한국세라믹학회지
• /
• 제40권1호
• /
• pp.24-30
• /
• 2003

AFm상의 생성과 전이는 시멘트에서의 수화반응, 경화속도 그리고 내구성에 큰 영향을 미친다. 실험실에서 제조한 3종류의 대표적인 AFm상에 CaC $O_3$, CaC $l_2$ 및 CaS $O_4$.2$H_2O$를 첨가하였을 때의 상변화를 검토를 하였다 AFm상의 상전이는 각 수화물의 용해도적과 밀접한 관계가 있다. 각종 AFm상( $M_{S}$ , $M_{C}$, $M_{Cl}$ )에 CaS $O_4$.2$H_2O$를 첨가한 경우, 모든 경우에서 AFm상은 ettringite로 전이를 하였다. 전이의 순서는 $M_{S}$ 가 가장 빠르게 ettringite로 전이를 하였으며 $M_{Cl}$ 이 가장 늦게 전이를 하였다. CaC $O_3$를 AFm상에 첨가하였을 경우에는 $M_{S}$ 는 보다 안정한 상인 $M_{C}$로 전이를 하였으며, 또 $M_{S}$ 중의 S $O_4$$^{2-}$ 이온이 방출되어 ettringite가 생성된다. $M_{C}$ 및 $M_{Cl}$ 에 CaC $O_3$를 첨가한 경우에는 아무런 상 변화가 일어나지 않았다. CaC $l_2$를 AFm상에 첨가하였을 경우, $M_{S}$ 는 $M_{Cl}$ 로 전이를 하였으며, $M_{S}$ 중의 S $O_4$$^{2-}$ 이온이 방출되어 ettringite가 생성된다. $M_{C}$에 CaC $l_2$를 첨가한 경우 $M_{C}$는 완전히 $M_{Cl}$ 로 전이를 하였다. $M_{Cl}$ 에 CaC $l_2$를 첨가하였을 경우에는 아무런 수화물의 변화는 발생하지 않았다. 따라서 CaS $O_4$.2$H_2O$를 CaC $O_3$및 CaC $l_2$와 반응시켰을 때의 AFm상의 안정성 순서는 $M_{S}$ < $M_{C}$< $M_{Cl}$ 로 된다.