• 한국세라믹학회지
• /
• 제23권4호
• /
• pp.62-68
• /
• 1986

$(Pb_{1-x} La_x)(Zr_{0.65} Ti_{0.35})_{1-x/4}O_3$ (PLZT X/65/35) powders were prepared by molten salt synthesis using NaCl-K Cl and conventional calcining of oxides. The effects of molten salt on formation and charactrization of PLZT powder and on dielectric piezolectric and optical properties of PLZT ceramics were studied, The completed PLZT powder formation in the presence of fused salt was attained at 50-10$0^{\circ}C$ lower temperature than that in solid state reaction and the particle size of the powder made by molten salt synthesis was markedly increased with increasing calcining temperature. The substitution of Na and/or K ions in NaCl-KCl for Pb ion in process of molten salt synthesis was increased with increasing La concentration Z. These substituted Na and/or K ions were identified as the origins of decreasing coupl-ing factor and optical transmittance of PLZT ceramics.

• 한국세라믹학회지
• /
• 제24권6호
• /
• pp.579-585
• /
• 1987

The effects of flux KCl and dopant Nb2O5 on the PTCR characteristics of BaTiO3 prepared by molten salt synthesis method have been investigated. As the amount of dopant Nb2O5 is over the solubility limit in BaTiO3, the room-temperature resistivity increases, and the PTCR effect and the grain size decrease. The variation of the amount of flux KCl slightly influences on the room-temperature resistivity, PTCR effect and grain size in Nb2O5 doped BaTiO3, but BaTiO3 ceramics prepared by the method of molten salt synthesis show larger PTCR effect than those of conventional calcining of mixed oxides.

• 한국전기전자재료학회논문지
• /
• 제11권5호
• /
• pp.378-383
• /
• 1998

Microstructure and additive effect of Lead Zirconate-Titanate(PZT) ceramics prepared by molten salt synthesis method with additives $Nb_2O_5, Fe_2O_3$ and MnO were investigated.The grain PZT ceramics ws decreased with the increase $Nb^{5+} or Fe^{3+}$ while increased with the increase $Mn^{2+}$ addition. The relative resistivity of PZT ceramics was increased with the increase $Mn^{5+}$ addition, while decreased with the increase $Mn^{2+}$ addition. And the dielectric and the piezoelectric constant of PZT ceramics showed 2,100 and 342pC/N at $Mn^{5+}$ addition of 0.75 mol%, respectively.

• 한국세라믹학회지
• /
• 제22권3호
• /
• pp.13-18
• /
• 1985

Semiconductive $Ba_{0.9}Sr_{0.1}TiO_3$ was prepared by both the Calcining of mixed Oxides (C. M. O) and the Molten Salt Synthesis(M.S.S) methods to investigate the PTCR effects. In the Molten Salt Synthesis method the temperature of calcination for Synthesis of $BaTiO_3$ could be lowered from 110$0^{\circ}C$ to 80$0^{\circ}C$. The M.S.S Specimens had smaller grain size and more homogeneous size distribution at the same sintering temperature as compared with the C. M. O specimens. The M. S. S. specimens showed greater PTCR effects and current variations in the time vs. current charac-teristics than those of C. M. O Specimens.

• 한국결정성장학회지
• /
• 제15권3호
• /
• pp.99-103
• /
• 2005

NaCl-KCl을 flux로 사용한 용융염 합성법을 이용하여 $Pb(Sc_{1/2}Ta_{1/2})O_3$, 분말을 제조하였다. $700^{\circ}C$에서 $800^{\circ}C$의 온도범위에서 상형성 및 분말 상태의 변화를 조사하였다. 용융염 합성법으로 $750^{\circ}C$ 2시간 하소하였을 때, 순수한 페로브스카이트 구조를 가진 $Pb(Sc_{1/2}Ta_{1/2})O_3$ 상이 형성되었으며, 평균 입자 크기는 $0.5\{mu}m$ 이하이고 입방체와 유사한 형상을 갖는 분말이 제조되었다. DIA, X-선 회절 분석, 미세구조 변화를 통해 합성된 분말의 특성을 고찰하였다.

• 한국세라믹학회지
• /
• 제28권1호
• /
• pp.79-85
• /
• 1991

The effects of MnO2 on the microstructure and dielectric properties of Pb(Fe1/2Nb1/2)O3 ceramics prepared by KCl-NaCl molten salt synthesis(MSS) method have been investigated. As the amount of MnO2 increased up to 0.25wt%, the density increased and the grain size decreased, while above 0.25wt%, the density decreased with the grain growth. Dielectric constant increased with increasing the amount of MnO2, and dielectric loss decreased up to 0.25wt% and then increased. This is due to the compensation effect by the substitution of Mn4+ to Fe3+ and the appearance of the second phase.

• 한국결정성장학회지
• /
• 제6권4호
• /
• pp.501-508
• /
• 1996

NaCl-KCl 용융염을 사용하여 strontium barium niobate 분말을 합성하였으며 반응온도, 시간 및 용융염의 첨가량 변화에 따른 반응과정 및 입자 형상 변화를 조사하였다. 반응 온도 및 반응 시간이 증가함에 따라 반응율은 증가하였으며, 분말의 형상은 덩어리 형태에서 침상형태로 변화하였다. 용융염의 첨가량 증가에 따라 반응율은 크게 증가하였으나, 분말의 형상은 침상형태에서 구상형태로 변화하였다. NaCl-KCl 용융염을 사용한 합성법에 의해 융제비가 1인 경우 $1000^{\circ}C$에서, 융제비가 4인 경우 $650^{\circ}C$에서 반응율 90 % 이상의 strontium barium niobate 분말 합성이 가능하였다.

• 한국세라믹학회지
• /
• 제42권10호
• /
• pp.672-677
• /
• 2005

In this study we prepared the Sr-ferrite powders and magnet by a molten salt method using the (NaCl+KCl) salt mixture. Starting materials of $Fe_{2}$$O_{3}$ and Sr$Co_{3}$ were mixed as the molar ratio of 5.70:1, and 0.08 mol$ \% $ $Al_{2}$$O_{3}$, 0.10 mo1$ \% $ Si$O_{2}$ and 0.12 mo1$ \% $ CaO were added as additives. Sr-ferrite powders synthesized at the reaction temperatures of 800$\∼$1200$ ^{\circ}C $ showed the typical M-type hexagonal ferrite phase, and hexagonal plate-like morphology with uniform distribution of 1$\∼$3 $\mu$m particle size. The bulk density of the sintered Sr-ferrite magnet prepared with powders by the molten salt method showed the maximum density of 4.82 g/$cm^{3}$ at the sintering temperature of 1200$^{\circ}C $. The maxima of remanent flux density (Br, 45 emu/g) and coercive force (iHc, 3.75 kOe) occurred at the sintering temperatures of 1150$ ^{\circ}C$ and 1200$^{\circ}C $.

• Korean Chemical Engineering Research
• /
• 제53권5호
• /
• pp.603-608
• /
• 2015

일반적으로 결정은 계면에 따라 그 성장속도가 다르기 때문에 계면의 성장을 제어함으로써 다양한 형태의 결정입자를 얻는 것이 가능하다. 알루미나의 경우 산업적 이용범위가 다양해지고 있어, 다양한 크기 또는 종횡비가 다른 다양한 형상의 분말이 요구되기도 한다. 용융염(molten-salt)을 이용하여 세라믹 입자를 성장시킬 경우, $800{\sim}900^{\circ}C$ 이상에서 용융되는 salt의 조건을 변화함으로써 세라믹 입자의 결정 성장 방향을 제어할 수 있는데, 알루미나의 경우 주로 판상형으로 입자가 성장하게 되며, 이때 salt의 ionic strength에 따라 판상형으로 성장하는 결정의 성장 속도를 제어하는 것이 가능하다. 본 연구에서는 NaCl, $Na_2SO_4$, $Na_3PO_4$를 이용하여 ionic strength가 다른 다양한 salt 조건에서 알루미나 입자를 성장시켰으며, 이들이 알루미나 결정 성장에 미치는 영향과 온도, 농도 변화에 따라 형성되는 알루미나의 크기 및 형상의 변화에 관하여 연구하였다.

• 한국결정성장학회지
• /
• 제7권3호
• /
• pp.400-405
• /
• 1997

KCl을 flux로 사용한 용융염 합성법을 이용하여 $Pb(Sc_{1/2}Nb_{1/2})O_3$ 분말을 제조하였다. $700^{\circ}C$부터 $850^{\circ}C$까지의 온도 범위에서 상형성 및 분말 상태의 변화를 조사하였다. 85$0^{\circ}C$에서 2시간동안 하소하였을 때 순수한 $Pb(Sc_{1/2}Nb_{1/2})O_3$상이 형성되었으며, 평군 입자 크기는 0.5 $\mu \textrm{m}$ 이하이었다. 시차열분석, X-선 회절 분석, 미세구조 변화를 통해 결과를 고찰하였다.