• Journal of the Korean Ceramic Society
• /
• v.23 no.4
• /
• pp.62-68
• /
• 1986

$(Pb_{1-x} La_x)(Zr_{0.65} Ti_{0.35})_{1-x/4}O_3$ (PLZT X/65/35) powders were prepared by molten salt synthesis using NaCl-K Cl and conventional calcining of oxides. The effects of molten salt on formation and charactrization of PLZT powder and on dielectric piezolectric and optical properties of PLZT ceramics were studied, The completed PLZT powder formation in the presence of fused salt was attained at 50-10$0^{\circ}C$ lower temperature than that in solid state reaction and the particle size of the powder made by molten salt synthesis was markedly increased with increasing calcining temperature. The substitution of Na and/or K ions in NaCl-KCl for Pb ion in process of molten salt synthesis was increased with increasing La concentration Z. These substituted Na and/or K ions were identified as the origins of decreasing coupl-ing factor and optical transmittance of PLZT ceramics.

• Journal of the Korean Ceramic Society
• /
• v.24 no.6
• /
• pp.579-585
• /
• 1987

The effects of flux KCl and dopant Nb2O5 on the PTCR characteristics of BaTiO3 prepared by molten salt synthesis method have been investigated. As the amount of dopant Nb2O5 is over the solubility limit in BaTiO3, the room-temperature resistivity increases, and the PTCR effect and the grain size decrease. The variation of the amount of flux KCl slightly influences on the room-temperature resistivity, PTCR effect and grain size in Nb2O5 doped BaTiO3, but BaTiO3 ceramics prepared by the method of molten salt synthesis show larger PTCR effect than those of conventional calcining of mixed oxides.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.5
• /
• pp.378-383
• /
• 1998

Microstructure and additive effect of Lead Zirconate-Titanate(PZT) ceramics prepared by molten salt synthesis method with additives $Nb_2O_5, Fe_2O_3$ and MnO were investigated.The grain PZT ceramics ws decreased with the increase $Nb^{5+} or Fe^{3+}$ while increased with the increase $Mn^{2+}$ addition. The relative resistivity of PZT ceramics was increased with the increase $Mn^{5+}$ addition, while decreased with the increase $Mn^{2+}$ addition. And the dielectric and the piezoelectric constant of PZT ceramics showed 2,100 and 342pC/N at $Mn^{5+}$ addition of 0.75 mol%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.22 no.3
• /
• pp.13-18
• /
• 1985

Semiconductive $Ba_{0.9}Sr_{0.1}TiO_3$ was prepared by both the Calcining of mixed Oxides (C. M. O) and the Molten Salt Synthesis(M.S.S) methods to investigate the PTCR effects. In the Molten Salt Synthesis method the temperature of calcination for Synthesis of $BaTiO_3$ could be lowered from 110$0^{\circ}C$ to 80$0^{\circ}C$. The M.S.S Specimens had smaller grain size and more homogeneous size distribution at the same sintering temperature as compared with the C. M. O specimens. The M. S. S. specimens showed greater PTCR effects and current variations in the time vs. current charac-teristics than those of C. M. O Specimens.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.3
• /
• pp.99-103
• /
• 2005

Lead scandium tantalate powders were prepared by a molten salt synthesis method using NaCl-KCl as a flux. Variations in phase formation and particle morphology were investigated for the temperature range from $700^{\circ}C\;to\;800^{\circ}C$. $Pb(Sc_{1/2}Ta_{1/2})O_3$, with pure perovskite phase was formed at $750^{\circ}C$ fur 2 hrs and the prepared powder had the cubic-like morphology and the average particle size below $0.5{\mu}m$. The results were discussed with respect to DTA, X-ray diffraction, and microstructural characterization data.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.79-85
• /
• 1991

The effects of MnO2 on the microstructure and dielectric properties of Pb(Fe1/2Nb1/2)O3 ceramics prepared by KCl-NaCl molten salt synthesis(MSS) method have been investigated. As the amount of MnO2 increased up to 0.25wt%, the density increased and the grain size decreased, while above 0.25wt%, the density decreased with the grain growth. Dielectric constant increased with increasing the amount of MnO2, and dielectric loss decreased up to 0.25wt% and then increased. This is due to the compensation effect by the substitution of Mn4+ to Fe3+ and the appearance of the second phase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.4
• /
• pp.501-508
• /
• 1996

Strontium barium niobate powders were prepared by NaCl-KCl molten salt, and reaction process and morphology change of strontium barium niobate were investigated as a function of reaction temperature, time, and amount of molten salt. With increasing the reaction temperature and time, the reacted fraction was increased and the morphology of powder was changed from lumpy shape into meedle-like shape. With increasing the amount of molten salt, reacted fraction was increased rapidly, but the morphology of powder was changed from needle-like shape into spherical shape. Strontium barium niobate powder, over 90 % in fraction reacted, was obtained from the reaction conditions at $1000^{\circ}C$ for small flux ratio (=1) and at $650^{\circ}C$ for large flux ratio (=4).

• Journal of the Korean Ceramic Society
• /
• v.42 no.10 s.281
• /
• pp.672-677
• /
• 2005

In this study we prepared the Sr-ferrite powders and magnet by a molten salt method using the (NaCl+KCl) salt mixture. Starting materials of $Fe_{2}$$O_{3}$ and Sr$Co_{3}$ were mixed as the molar ratio of 5.70:1, and 0.08 mol$ \% $ $Al_{2}$$O_{3}$, 0.10 mo1$ \% $ Si$O_{2}$ and 0.12 mo1$ \% $ CaO were added as additives. Sr-ferrite powders synthesized at the reaction temperatures of 800$\∼$1200$ ^{\circ}C $ showed the typical M-type hexagonal ferrite phase, and hexagonal plate-like morphology with uniform distribution of 1$\∼$3 $\mu$m particle size. The bulk density of the sintered Sr-ferrite magnet prepared with powders by the molten salt method showed the maximum density of 4.82 g/$cm^{3}$ at the sintering temperature of 1200$^{\circ}C $. The maxima of remanent flux density (Br, 45 emu/g) and coercive force (iHc, 3.75 kOe) occurred at the sintering temperatures of 1150$ ^{\circ}C$ and 1200$^{\circ}C $.

• Korean Chemical Engineering Research
• /
• v.53 no.5
• /
• pp.603-608
• /
• 2015

Alumina powder have been expanded its application in industry and required to control its morphology such as powder size and aspect ratio of single particle. It can be synthesized by molten - salt method which is possible to obtain various shapes of ceramic particles by controlling the growth direction because each crystal face has different growth rate. In this study, various combinations of salts such as NaCl, $Na_2SO_4$, $Na_3PO_4$ and their mixture were used for control the growth of plate like alumina particle from the initial stage of synthesis because salt having different ionic strength can control the growth direction of ceramic particle under its melting condition around $800{\sim}900^{\circ}C$, and growth behavior of plate-like alumina particle with different reaction conditions such as temperature and concentration on the crystal size and shape was studied.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.400-405
• /
• 1997

Lead scandium niobate powders were prepared by a molten salt synthesis method using KCl as a flux. Variations in phase formation and particle morphology were investigated for the temperature range $700^{\circ}C$ to $850^{\circ}C$. Pure $Pb(Sc_{1/2}Nb_{1/2})O_3$ perovskite phase was formed at $850^{\circ}C$ after 2hrs and the average particle size of powder was below 0.5 $\mu\textrm{m}$. The results are discussed with respect to DTA, X-ray diffraction, and microstructural characterization data.