The use of Zn-Al-Mg alloy coatings for enhancing the corrosion resistance of steel sheets is gaining prominence over traditional Zn coatings. There is a growing demand for the development of thermal spray wires made from Zn-Al-Mg alloys, as a replacement for the existing wires produced using Al and Zn. This is particularly crucial to secure corrosion resistance and durability in the damaged areas of coated steel sheets caused by deformation and welding. This study focuses on the casting and extrusion processes of Zn-2Al-1Mg alloy for the fabrication of such spray wires and analyzes the changes in microstructure during the extrusion process. The Zn-2Al-1Mg alloy, cast in molds, was subjected to a heat treatment at 250 ℃ for 3 hours prior to extrusion. The extrusion process was carried out by heating both the material and the mold up to 300 ℃. Microstructural analysis was conducted using FE-SEM and EDS to differentiate each phase. The mechanical properties of the cast specimen were evaluated through compression tests at temperatures ranging from 200 to 300 ℃, with strain rates of 0.1 to 5 sec^-1. Vickers hardness testing was utilized to assess the inhomogeneity of mechanical properties in the radial direction of the extruded material. Finite Element Analysis (FEA) was employed to understand the inhomogeneity in stress and strain distribution during extrusion, which aids in understanding the impact of heterogeneous deformation on the microstructure during the process.

• Restorative Dentistry and Endodontics
• /
• v.31 no.5
• /
• pp.344-351
• /
• 2006

The purpose of this study was to evaluate the thermal expansion characteristics of injectable ther-moplasticized gutta-perchas and a Resilon. The materials investigated are Obtura gutta-percha, Diadent gutta-percha, E&Q Gutta-percha Bar and Epiphany (Resilon). The temperature at the heating chamber orifice of an Obtura II syringe and the extruded gutta-percha from the tip of both 23- and 20-gauge needle was determined using a Digital thermometer. A cylindrical ceramic mold was fabricated for thermal expansion test, which was 27 mm long, with an internal bore diameter of 3 mm and an outer diameter of 10 mm. The mold was filled with each experimental material and barrel ends were closed with two ceramic plunger. The samples in ceramic molds were heated in a dilatometer over the temperature range from $25^{\circ}C$ to $75^{\circ}C$. From the change of specimen length as a function of temperature, the coefficients of thermal expansion were deter-mined. There was no statistical difference between four materials in the thermal expansion in the range from $35^{\circ}C$ to $55^{\circ}C$ (p > 0.05). However, Obtura Gutta-percha showed smaller thermal expansion than Diadent and Metadent ones from $35^{\circ}C$ to $75^{\circ}C$ (p < 0.05). The thermal expansion of Epiphany was similar to those of the other gutta-percha groups.