• Korean Journal of Materials Research
• /
• v.20 no.8
• /
• pp.412-417
• /
• 2010

Mo thin films were used for the back electrode because of the low resistivity in the Mo/$CuInGaSe_2$ contact in chalcopyrite solar cells. $1\;{\mu}m$ thick Mo thin films were deposited on soda lime glass by varying the Ar pressure with the dc-magnetron sputtering process. The effects of the Ar pressure on the morphology of the Mo back electrode were studied and the relationships between the morphology and electro-optical properties, namely, the resistivity as well as the reflectance of the Mo thin films, were investigated. The resitivity increased from $24\;{\mu}{\Omega}{\cdot}cm$ to $11833\;{\mu}{\Omega}{\cdot}cm$; this was caused by the increased surface defect and low crystallinity as the Ar pressure increased from $3{\times}10^{-3}$ to $3{\times}10^{-2}\;Torr$. The surface morphologies of the Mo thin films changed from somewhat coarse fibrous structures to irregular and fine celled structures with increased surface cracks along the cell boundaries, as the Ar pressure increased from $3{\times}10^{-3}$ to $3{\times}10^{-2}\;Torr$. The changes of reflectances in the visible light range with Ar pressures were mainly attributed to the surface morphological changes of the Mo thin films. The reflectance in the visible light range showed the highest value of 45% at $3{\times}10^{-3}\;Torr$ and decreased to 18.5% at $3{\times}10^{-2}\;Torr$.

• Korean Journal of Materials Research
• /
• v.32 no.2
• /
• pp.57-65
• /
• 2022

Herein a rich, Se-nanoparticle modified Mo-W₁₈O₄₉ nanocomposite as efficient hydrogen evolution reaction catalyst is reported via hydrothermal synthesized process. In this work, Na₂SeSO₃ solution and selenium powder are used as Se precursor material. The structure and composition of the nanocomposites are characterized by X-ray diffraction (XRD), high-resolution field emission scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), EDX spectrum analysis and the corresponding element mapping. The improved electrochemical properties are studied by current density, and EIS analysis. The as-prepared Se modified Mo-W₁₈O₄₉ synthesized via Na₂SeSO₃ is investigated by FE-SEM analysis and found to exhibit spherical particles combined with nanosheets. This special morphology effectively improves the charge separation and transfer efficiency, resulting in enhanced photoelectric behavior compared with that of pure Mo-W₁₈O₄₉. The nanomaterial obtained via Na₂SeSO₃ solution demonstrates a high HER activity and low overpotential of -0.34 V, allowing it to deliver a current density of 10 mA cm^-2.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.661-668
• /
• 2010

Cu(In,Ga)$Se_2$(CIGS) photovoltaic thin films were electrodeposited on Mo/glass substrates with an aqueous solution containing 2 mM $CuCl_2$, 8 mM $InCl_3$, 20 mM $GaCl_3$ and 8mM $H_2SeO_3$ at the electrodeposition potential of -0.6 to -1.0 V(SCE) and pH of 1.8. The best chemical composition of $Cu_{1.05}In_{0.8}Ga_{0.13}Se_2$ was found to be achieved at -0.7 V(SCE). The precursor Cu-In-Ga-Se films were annealed for crystallization to chalcopyrite structure at temperatures of 100-$500^{\circ}C$ under Ar gas atmosphere. The chemical compositions, microstructures, surface morphologies, and crystallographic structures of the annealed films were analyzed by EPMA, FE-SEM, AFM, and XRD, respectively. The precursor Cu-In-Ga-Se grains were grown sparsely on the Mo-back contact and also had very rough surfaces. However, after annealing treatment beginning at $200^{\circ}C$, the empty spaces between grains were removed and the grains showed well developed columnar shapes with smooth surfaces. The precursor Cu-In-Ga-Se films were also annealed at the temperature of $500^{\circ}C$ for 60 min under Se gas atmosphere to suppress the Se volatilization. The Se amount on the CIGS film after selenization annealing increased above the Se amount of the electrodeposited state and the $MoSe_2$ phase occurred, resulting from the diffusion of Se through the CIGS film and interaction with Mo back electrode. However, the selenization-annealed films showed higher crystallinity values than did the films annealed under Ar atmosphere with a chemical composition closer to that of the electrodeposited state.

• Ceramist
• /
• v.21 no.2
• /
• pp.29-37
• /
• 2018

In order to overcome the problems of existing low-dimensional materials (carbon nanotubes, graphene, transition metal dichalcogenides, etc) researches on new 1D materials have been studied. In the case of $LiMo_3Se_3$ and $Mo_6S_{9-x}I_x$, continuous researches have been carried out for 3D bulk synthesis and atomic scale dispersion. Recently, quantum confinement effect of $LiMo_3Se_3$ and bio-stability of $Mo_6S_{9-x}I_x$ have been proven and various applications have started to be studied. In addition, device application results using new 1D materials such as $Sb_2Se_3$ (optoelectronic devices using the property of effectively reducing exciton decay due to no dangling bond) and $VS_4$ (electrochemical energy storage using the space between 1-D nanostructures) have been reported very importantly. Therefore, it can be claimed that it has reached a very important time to find and synthesize new 1D materials and to report various characteristics not existing.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.9
• /
• pp.701-706
• /
• 2013

We have focused on the conversion efficiency of CIGS thin film solar cell prepared by co-evaporation method as well as the optimization of process condition. The total thickness of back electrode was fixed at 1 ${\mu}m$ and the structural, electric and optical properties of CIGS thin film were investigated by varying the thickness of Mo:Na bottom layer from 0 to 500 nm. From the experimental results, the content of Na was appeared as 0.28 atomic percent when the thickness of Mo:Na layer was 300 nm with compactly densified plate-shape surface morphology. From the XRD measurements, (112) plane was the strongest preferential orientation together with secondary (220) and (204) planes affecting to the crystallization. The lowest roughness and resistivity were 2.67 nm and 3.9 ${\Omega}{\cdot}cm$, respectively. In addition, very high carrier density and hole mobility were recorded. From the optimization of Mo:Na layer, we have achieved the conversion efficiency of 9.59 percent.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.11
• /
• pp.3225-3227
• /
• 2010

The thermal conductivity of layered metal chalcogenides such as $MT_2$ (M = Mo, W; T = S, Se) shows a marked decrease after exfoliation and subsequent restacking process. Random stacking of two-dimensional crystalline sheets circumvents thermal conduction pathways along a longitudinal direction, which results in a reduction in thermal conductivity. $WS_2$ and $WSe_2$ compounds retain p-type conducting behavior after exfoliation and restacking with decreased electrical conductivity due to the change in carrier concentration. $MoSe_2$ compound exhibits metallic behavior < $130^{\circ}C$ with a small Seebeck coefficient, which results from metastable 1T-$MoSe_2$ structure of the restacked phase.

• Korean Journal of Materials Research
• /
• v.5 no.8
• /
• pp.988-996
• /
• 1995

CuInSe$_2$this films as a light absorber layer were fabricated by vacuum evaporation using In$_2$Se$_3$and Cu$_2$Se precursors and their properties were analyzed. Indium selenide films of 0.5${\mu}{\textrm}{m}$ thickness were first deposited by vacuum evaporation of In$_2$Se$_3$ on a Corning 7059 glass substrate. The films deposited at suscepor temperature of 40$0^{\circ}C$ showed a flat surface morphology with densely Packed grain structure. CuInSe$_2$films directly formed by evaporating Cu$_2$Se on the predeposited In$_2$Se$_2$films also showed a very flat surface when the susceptor temperature was $700^{\circ}C$. Cu$_2$Se, a second phase in the CuInSe$_2$film, was removed by evaporating additional In$_2$Se$_3$on the CuInSe$_2$film at $700^{\circ}C$. The grain size of 1.2${\mu}{\textrm}{m}$ thick CuInSe$_2$, film was about 2${\mu}{\textrm}{m}$ and the film had a (112) preferred orientation. As the amount of deposited In$_2$Se$_3$increased, the electrical resistivity of CuInSe$_2$films increased because of the decrease of hole concentration. But the optical band gap was almost constant at the value of 1.04eV, The CuInSe$_2$film grown on a Mo/glass substrate had a similar smooth microstructure compared to that on a glass substrate. A solar cell with ZnO/CdS/CuInSe$_2$/Mo structure may be realized based on the above CuInSe$_2$films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05c
• /
• pp.63-66
• /
• 2002

Bi-layer Mo films were deposited on sodalime glass substrates using DC magnetron sputtering. As the gas pressure and power density, the resistivity varied from $1.5{\times}10^{-5}$ to $4.97{\times}10^{-4}{\Omega}{\cdot}cm$. Furthermore, stress direction yielded compressive-to-tensile transition stress curves. The microstructure of the compressive stress films which had poor adhesion consists of tightly packed columns, but of the tensile-stressed films had less dense structure. Under all gas pressure conditions, Mo films exhibited distinctly increasing optical reflection with decreasing gas pressure. The expansion of (110) peak width with the gas pressure meant the worse crystalline growth. Also, The highest efficiency was 15.2% on 0.2 $cm^2$. The fill factor, open circuit voltage and short circuit current were 63 %, 570 m V and 42.6 $mA/cm^2$ respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.318-318
• /
• 2010

전기로를 이용하여 셀렌화한 $CuInSe_2$ (CIS)박막에 대해 연구한 결과를 발표하고자 한다. 화석연료의 과도한 사용으로 지구온난화의 환경문제가 대두되면서 영구적이고 무상의 태양에너지 이용에 대한 필요성이 점차 높아지고 있다. 빛에너지를 전기에너지로 변화시키기 위한 태양전지는 재료에 따라 다양하게 개발되고 있으며 그 중 가장 주목을 받고 있는 것 중의 하나가 $CuInSe_2$을 흡수층으로 하는 CIS 박막 태양전지이다. CIS 박막은 태양전지의 흡수층으로 사용되는데 직접천이형 밴드구조를 가지고 있고, 약 $10^5\;cm^{-1}$의 높은 광흡수계수를 가지고 있어 태양전지의 흡수층으로 적합한 물질로 각광받고 있다. 에너지 밴드갭이 1eV로 실리콘과 유사한 밴드갬을 가지고 있으나 이는 Ga, Al을 In 대신 치환함으로 조절할 할 수 있다. 무엇보다도 유리와 같은 저가의 기판위에 스퍼터와 같은 장치로 대면적 CIS 태양전지를 만들수 있다는 것이 산업적인면에서의 장점으로 알려져 있다. 본 연구에서는 $50mm{\times}50mm$ 넓이의 sodalime 유리판을 기판으로 하여 CIS 박막을 제조하고 연구하였다. 스퍼터를 이용하여 유리기판 위에 Mo (Molybdenum) 을 증착하고 그 위에 Cu-In막을 증착하였다. Cu-In/Mo/유리기판 시료는 전기로에 도입되어 셀렌화 처리 하였다. 전기로는 $10^{-1}$ Torr 정도의 진공을 수분간 유지하여 반응할 수 있는 공기(산소)를 제거하였다. 진공 혹은 5N의 고순도 질소를 흘려주며 열을 가하여 셀렌화를 하였다. 전기로에는 1g의 셀레늄(Se)이 Cu-In/Mo/유리기판 시료와 함께 도입되었다. Se이 Cu-In 막과 높은 반응성을 갖도록 Se과 Cu-In 시료는 그라파이드 상자에 함께 넣었고, 그라파이트 상자는 전기로에 넣어 셀렌화하였다. 셀렌화 온도는 $400^{\circ}C{\sim}500^{\circ}C$까지 변화시켜 가며 CIS 박막을 제조하였으며 그 물성도 조사하였다. 물성 조사는 사진, 현미경, SEM, EDX, XRD, Hall effects를 이용하였다. 셀렌화 온도가 $450^{\circ}C$ 이상에서는 CIS 박막의 흡착성이 낮아 CIS 박막이 Mo 표면에서 떨어짐을 알 수 있었다. 셀렌화 후 박막에 함유된 Se은 48%~49% 정도있었다. 제조된 CIS 박막시료를 SEM으로 확인한 결과 생성된 CIS/Mo 사이에 계면층이 생겼있음 알 수 있었다. 이러한 계면층은 $MoSe^2$층으로 사료되고, 셀렌화 온도가 높으면 계면층의 두께도 증가되는 경향을 보였다. 셀렌화 온도가 높아질수록 많은 양의 산소가 CIS 박막에 들어가는 것도 알 수 있었다. 학술회의에서 보다 깊은 조사결과를 발표하고자 한다.

• Current Photovoltaic Research
• /
• v.7 no.1
• /
• pp.1-8
• /
• 2019

The $Cu(In,Ga)Se_2$ (CIGS) thin film obtained by two-step process (metal deposition and Se annealing) has a rough surface morphology and many voids at the CIGS/Mo interface. To solve the problem a precursor that contains Se was employer by depositing a (In,Se)/(Cu,Ga) stacked layer. We devised a two-step annealing (vacuum pre-annealing and Se annealing) for the precursor because direct annealing of the precursor in Se environment resulted in the small grains with unwanted demarcation between stacked layers. After vacuum pre-annealing up to $500^{\circ}C$ the CIGS film consisted of CIGS phase and secondary phases including $In_4Se_3$, InSe, and $Cu_9(In,Ga)_4$. The secondary phases were completely converted to CIGS phase by a subsequent Se annealing. A void-free CIGS/Mo interface was obtained by the two-step annealing process. Especially, the CIGS film prepared by vacuum annealing $450^{\circ}C$ and subsequent Se annealing $550^{\circ}C$ showed a densely-packed grains with smooth surface, well-aligned bamboo grains on the top of the film, little voids in the film, and also little voids at the CIGS/Mo interface. The smooth surface enhanced the cell performance due to the increase of shunt resistance.