• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.332.2-332.2
• /
• 2016

Two dimensional transition-metal dichalcogenides (TMDs) semiconductors are attractive materials for optoelectric devices because of their direct energy bandgap and transparency. To investigate the feasibility of transparent p-n junctions, we have fabricated a p-n heterojunction consisting of p-type WSe2 and n-type MoS2 flakes since WSe2 and MoS2 with proper electrode metals exhibit p-type and n-type behaviors, respectively. These heterojunctions exhibits gate-tunable rectifying behaviors and photovoltaic effects (ECE ~ 0.2%) indicating that p-n junctions were formed. In addition, photocurrent and photovoltaic effects were observed under light illumination, which were dependent on the gate voltage. In addition, the photocurrent mapping images indicate that the photovoltaic effects comes from the junction area. Possible origins of gate-tunability are discussed.

• 한국분말재료학회지
• /
• 제5권4호
• /
• pp.241-249
• /
• 1998

Sintering kinetics of ball-milled $MoSi_2$ was studied with the addition of Ni. $MoSi_2$ powder with the average particle size of 1 $\mu\textrm{m}$ was obtained from ball-milling of 10 $\mu\textrm{m}$ powder. Small amount of Ni was added to the ball-milled $MoSi_2$ powder by salt solution and reduction method. The powder was compacted into cylindrical shape at 200 MPa and isothermally sintered in a $H_2$ atmosphere at the temperature range of 1100~$1400^{\circ}C$ for 3~600 minutes. The changes of linear shrinkage and sintered density were monitored as a function of sintering time. The microstructure was observed by using optical microscopy and scanning electron microscopy. Phases were identified by X-ray diffratometer and electro-probe micro analysis. Sintering kinetics of Ni-added powder was compared to as-milled powder and the apparent activation energy was calculated from Arrhenius plot.

• 한국세라믹학회지
• /
• 제24권1호
• /
• pp.63-69
• /
• 1987

Effect of MoO3 additiion on the semiconductive BaTiO3 ceramics doped with 0.2 mole% Nb2O5 and their frequency characteristics have been investigated on the view of intergranular barrier layer model through the observation of changes in their electrical properties. The resistivity increases with the increase of MoO3 addition, but the capacitance, the frequency dependence of capacitance and the effect of positive temperature coefficient of resistivity (PTCR) decrease. It is explained by the possible increase in the thickness of potential barrier due to the formation of insulating layer and thus decrease in the degree of energy band bending. Both the PTCR effect and resistivity decrease with the increase of frequency due to the possible elimination of barrier layer at the grain boundary.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1998년도 춘계학술대회 및 발표대회 강연 및 발표논문 초록집
• /
• pp.22-22
• /
• 1998

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1995년도 추계학술강연 및 발표대회 강연 및 발표논문 초록집
• /
• pp.15-15
• /
• 1995

• 대한화학회지
• /
• 제29권5호
• /
• pp.510-515
• /
• 1985

진한 메탄설폰산(약10M)에서 초록색의 $MoO_{(aq)}^{3+}$는 진한 초록색의 이합체인$Mo_2O_2(OH)_{2(aq)}^{4+}$를 생성한다. 또한 이러한 진한 초록색은 15-16M의 메탄설폰산에서 존재하는 $MoO_{(aq)}^{3+}$용액에 물을 가하면 나타나며 15M의 메탄설폰산에서 단위체의 몰흡광계수는 415nm에서 약 20이다. 속도 상수는 이 실험조건하에서 아쿠오몰리브덴(V)와 수소이온농도에 의존하지 않는다. $Mo_2O_2(OH)_{2(aq)}^{4+}$의 수산화이온은 HPTS 약 6M, $CH_3SO_3H$는 10M이하에서 탈수소화반응이 일어난다. 마지막 생성물의 말단산소와 다리산소의 구조는 (*image) 단위를 가진 것으로 확인되었다.

• 대한금속재료학회지
• /
• 제50권9호
• /
• pp.645-651
• /
• 2012

This study investigated changes in phase fraction caused by the addition of Mo, as well as the subsequent behaviour of N and its effect on the mechanical properties of welded 24Cr-N duplex stainless steel weld metals. Filler metal was produced by fixing the contents of Cr, Ni, N, and Mn while adjusting the Mo content to 1.4, 2.5, 3.5 wt%. The delta ferrite fraction increased as the Mo content increased. In contrast, the ${\gamma}$ fraction decreased and changed from a round to an acicular shape. Secondary austenite (${\gamma}^{\prime}$) was observed in all specimens in a refined form, but it decreased as the Mo content increased to the extent that it was nearly impossible to find any secondary austenite at 3.5 wt% Mo. Both tensile and yield strengths increased with the addition of Mo. In contrast, the highest value of ductility was observed at 1.41 wt% Mo. At all temperatures, impact energy absorption showed the lowest value at 3.5 wt% Mo, at which the amount of ${\delta}$-ferrite was greatest. There was no significant temperature dependence of the impact energy absorption values for any of the specimens. As the fraction of ${\gamma}$ phase decreased, the amount of N stacked in the ${\gamma}$ phase increased. Consequently, the stacking fault energy decreased, while the hardness of ${\gamma}$ increased.

• 대한금속재료학회지
• /
• 제46권12호
• /
• pp.788-799
• /
• 2008

This study is concerned with the effects of Mo, Cr, and V addition on tensile and Charpy impact properties of API X80 linepipe steels. Four kinds of steels were processed by varying Mo, Cr, and V additions, and their microstructures and tensile and Charpy impact properties were investigated. Since the addition of Mo and V promoted to form fine acicular ferrite and granular bainite, while prohibiting the coarsening of granular bainite, it increased the strength and upper shelf energy, and decreased the energy transition temperature. The Cr addition promoted the formation of coarse granular bainite and secondary phases such as martensite-austenite constituents, thereby leading to the increased effective grain size, energy transition temperature, and strength and to the decreased upper shelf energy. The steel containing 0.3wt.% Mo and 0.06wt.% V without Cr had the highest upper shelf energy and the lowest energy transition temperature because its microstructure was composed of fine acicular ferrite and granular bainite, together with a small amount of hard secondary phases, while its tensile properties maintained excellent.

• 청정기술
• /
• 제25권2호
• /
• pp.123-128
• /
• 2019

EGME, GL 및 EG와 물을 용매를 사용하여 $Bi_2MoO_6$ 산화물을 수열합성법으로 성공적으로 합성하였다. 이들 촉매들의 물리적 특성을 XRD, DRS, BET, SEM 및 PL 등으로 분석하였고 제조된 촉매들을 사용하여 가시광선 조사 하에서의 로다민 B의 광분해 반응에서의 활성을 조사하였다. XRD의 분석 결과에 의하면 대부분의 촉매들은 수열합성법에 의해 이 합성조건에서 용매의 종류와 관계없이 Aurivillius 구조를 가진 ${\gamma}-Bi_2MoO_6$의 결정화가 잘 이루어졌으며 12에서 18 nm의 크기를 나타내었다. 또한, 합성온도가 $140^{\circ}C$ 이하에서는 $Bi_2MoO_6$ 산화물의 특성피크가 잘 나타나지 않았으나, $160^{\circ}C$ 이상의 온도에서는 $Bi_2MoO_6$ 산화물의 특성피크가 잘 나타났다. 모든 촉매들은 자외선 영역부터 470 nm보다 낮은 파장의 가시광 영역에서 강한 흡수스펙트럼을 보여주고 있다. 이 결과는 $Bi_2MoO_6$ 산화물들이 가시광 영역에서도 광촉매 활성을 보여주고 있는 것을 의미한다. EGME를 용매로 사용하여 제조된 $Bi_2MoO_6$ 촉매가 가장 높은 광분해 활성을 나타내었고 $180^{\circ}C$에서 합성된 촉매가 가장 높은 광활성을 보여주었다. 모든 촉매들은 560 nm 부근에서 강하고 넓은 PL 흡수밴드가 나타났으며, 이 피크의 세기가 커질수록 광분해 활성이 증가하는 것으로 나타났다.

• 자원리싸이클링
• /
• 제12권2호
• /
• pp.36-44
• /
• 2003

전구용 필라멘트 제조 공정에서 발생되는 Mo함유 폐산 내에 암모니아 가스를 취입하여 유가금속인 Mo를 암모늄테트라몰리브데이트($_3$.2NH$4MoO_3$.$H_2$O) 형태로 침전 회수하고, 여과 후 발생되는 중화 여액을 활용하기 위한 연구를 수행하였다. 암모니아 중화법을 이용한 Mo 회수공정에 있어 다양한 공정 변수들에 의한 제품의 회수율, 순도, 입도 등 특성을 평가하였으며, 그 결과로부터 Mo 염의 회수율 99.5% 이상, 순도 99.5% 이상을 확보하기 위한 최적 조업조건을 도출하였다. Bench 및 Pilot규모의 실험을 통하여 상업화 가능성을 확인하였으며, 폐산의 중화반응 후 발생된 여액은 엽면시비용 액상 복합비료의 원료로 사용 가능함을 확인하였다.