• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.11a
• /
• pp.114-114
• /
• 1993

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.651-651
• /
• 2000

• Korean Journal of Materials Research
• /
• v.8 no.9
• /
• pp.860-864
• /
• 1998

We investigated the photoluminescence and the crystalline properties with Ga doping concentrations (0-12 mol%) in $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}\textrm{SiO}_{4}$ green phosphors prepared by the solid state reaction. The photoluminescence was improved by a doping of Ga element in $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}(\textrm{Si_{1-x}\textrm{Ga}_{x})\textrm{O}_{4}$ phosphors which showed the highest emission intensity and good color purity in the doping concentration of x=0.08. The emission intensity of $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}(\textrm{Si_{1-x}\textrm{Ga}_{x})\textrm{O}_{4}$(x= 0.08) phosphors was increased to 7 times with increasing the sintering temperatures from $1100^{\circ}C$ to $1400^{\circ}C$, showing the improved crystalline quality. The decay time was not affected by Ga doping concentrations with constant values around 24ms. It was found from SEM and PSA analyses that the phosphors were composed of a large number of small grains around 1-3$10\mu\textrm{m}$ with a small amounts of agglomerated particles above $10\mu\textrm{m}$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.418-427
• /
• 1997

The effect of $La_2O_3$ as a dopant on the microstructure structure, crystal structure and electrical properties was studied. $0.05Pb(Sn_{0.5}Sb_{0.5})O_3＋0.11PbTiO_3＋0.84PbZroO_3＋0.4Wt%MnO_2$ (=0.05PSS ＋0.11PT＋0.84PZ+0.4wt%$MnO_2$) systems doped with 0, 0.1, 0.3, 0.5, 0.7, 1, 3, 5 mole% $La_2O_3$ were fabricated and investigated sintering density, crystal structure and micro-structure. The sintered 0.05PSS＋0.11PT＋0.84PZ+0.4wt%$MnO_2$ system doped with $La_2O_3$showed sintering density of the range of 7.683 g/㎤ of 0 mole% doping to 7.815 g/㎤ of 0 mole% doping. The average grain sizes in the range of 0 to 5 mole% $La_2O_3$were decreased from 9.0 $\mu\textrm{m}$ to 1.3 $\mu\textrm{m}$. X-ray diffraction investigation of sintered bodies showed that solid solutions were formed between 0.05PSS＋0.11PT＋0.84PZ+0.4wt%$MnO_2$ system and $La_2O_3$ in the range of 0 to 1 mole% but second phases were formed in case of 3, 5 mole%. Dielectric constants at 1 kHz were increased with 0 to 3 mlole% $La_2O_3$ before and after poling at the condition of 5 $KV_{DC}$/mm at $120^{\circ}C$ or $140^{\circ}C$ during 20 minutes. All Dielectric losses at 1 kHz were less than 1%, Curie temperatures were $208^{\circ}C$, $183^{\circ}C$, $152^{\circ}C$ and $127^{\circ}C$ at 0, 0.5, 1, 3 mole% $La_2O_3$ respectively. The values of $K_p$ were increased from 0 to 3 mole% $La_2O_3$ after poling at condition of 5 $KV_{DC}$mm at the condition of $120^{\circ}C$ or $140^{\circ}C$. The case of 0.7 mole% $La_2O_3$doped 0.05PSS＋0.11PT＋0.84PZ+0.4wt%$MnO_2$ system showed $K_p$ of 14.5% by poling at $140^{\circ}C$ during 20 minutes.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.571-576
• /
• 1988

The microstructure and electrical properties of 0.02Pb[Cd1/2W1/2)O3-0.505PbZrO3-0.475PbTiO3 with MnO2 addition have been investigated. The amount of MnO2 addition was 0, 0.2, 0.4, 0.6, 0.8, 1wt%, respectively. When MnO2 is added up to 0.2wt%, Mn3+ which is substituted for Ti4+ site make hole and act as a acceptor. When MnO2 is added over 0.2wt% Mn3+ which is substituted for Cd2+ site create electron and act as a donor. The variation of grain size show that it was rapidly increased by 0.4wt% addition of MnO2, and while that in the range of over 0.6wt% addition of MnO2 it was decreased. The solid solution range of MnO2 that assumed in this composition according to the variations of microstructure and electrical properties was 0.4-0.6wt%.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.149-153
• /
• 1999

Frequency and temperature dependence of magnetic loss has been investigated in Mn-Zn ferrites containing the sesistive temary compounds of $SiO_2-CaO-V_2O_5$. The Mn-Zn ferrite with the composition of $MnO:ZnO:Fe_2O_3=36:11:53$(by mol %) are prepared by self-propagating high-temperature synthesis. From the results of frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency region where the hysteresis loss is dominant becomes wide. The core-loss minimum occurs at about 4$0^{\circ}C$ in the specimens with the additive because of the reduction in eddy current loss.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2009.05a
• /
• pp.703-708
• /
• 2009

In this paper, synthesis here Mn add to Ar any a vacuum an atomosphere $ZnGa_2O_4$ : Mn, ZnO and $Ga_2O_3$ power of 1:1 mole ratio mixture. Manufacture a close examination of oxygen a component variation luminescence a specific character reach an in fluence of $ZnGa_2O_4$ : Mn, luminescence spectrum, the surface a picture and a component ratio measurement, also an explanation of Mn site symmetry and at luminescence spectrum reach an influence from low temperature photoluminescence spectrum.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.11a
• /
• pp.113-113
• /
• 1993

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.1
• /
• pp.1-16
• /
• 2023

A non-rare earth-based strontium-aluminate red light emitting phosphor was synthesized by a solid-state reaction method and the effect of synthesis temperature and Mn⁴⁺ activator concentration on the photoluminescence characteristics of the phosphor was studied. The synthesized SrAl₂O₄:Mn⁴⁺ phosphor showed broad band absorption characteristics in the near-ultraviolet and blue regions with peaks at wavelengths of near 330 and 460 nm, and a triple band deep red emission consisted of three peaks at near 644, 658, and 673 nm. The SrAl₂O₄:Mn⁴⁺ phosphor synthesized at a temperature 1600℃ and a Mn⁴⁺ activator concentration of 0.5 mol% showed the strongest PL emission intensity, and concentration quenching was observed at concentrations higher than 0.7 mol%. FE-SEM and DLS particle size distribution analysis showed that the synthesized SrAl₂O₄:Mn⁴⁺ phosphor had a particle size distribution of 2~6.4 ㎛ and an irregular spherical shape with an average particle size of ~4 ㎛.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.84-92
• /
• 2001

(La,Sr)MnO$_3$(LSM)-YSZ 복합체 양극의 산소환원 반응기구에 대해 고찰하였다. YSZ를 첨가함에 따라 복합체 양극의 ohmic 저항이 증가하고, 분극 저항은 YSZ를 40 wt%~50 wt% 혼합하였을 때 최소값을 나타내었다. 또한 LSM-YSZ 복합체 양극의 산소환원 반응기구는 1가 산소이온의 표면확산과 산소이온전달반응에 의해서 지배됨을 알 수 있었다. 임피던스 분석 결과에 따르면 고주파수 영역에서 나타나는 반원은 산소이온전달반응으로 산소분압 의존성이 거의 없고, YSZ가 40 wt% 첨가되었을 때 최소값을 나타내었다. 중간주파수 영역에서 나타나는 반원은 1가 산소이온의 표면확산반응으로 산소분압 의존성은 약 1/4이고, YSZ가 40~50 wt% 첨가되었을 때 최소값을 나타냈다. 한편, 저주파수 영역에 나타나는 반원은 가스확산반응으로 산소분압 의존성이 1이고, 온도에 따른 의존성이 거의 없었다.