• 한국표면공학회지
• /
• 제19권2호
• /
• pp.31-43
• /
• 1986

The properties of the electroless nickel deposit mainly depends on the pH of the bath, the plating temperature, and the molar ratio of nickel to hypophosphite but they are also affected by its formulation and concentration of complexing and buffering agents. According to changeing the concentration of triethanolamine and boric acid, phosphorous contents, microsturcture, crystalline, hardness and wear resistance of deposits obtained from ammoniacal alkaline bath were investigated by EPMA, differential thermal analyser, X-ray diffractometer and wear tester. The results are as follows; (1) Increasing concentration of triethanolamine in the bath, the deposits is slightly inclined to increase its phosphorous content(3.7% P). (2) In the as-plated state, the deposits are not crystallized state but they are thermally unstable phase, and they are crystallized with precipitating $Ni_3P$ at 400$^{\circ}C$. (3) The deposit containing 2.3% P has higher hardness value in the as plated and heat treated state at below 300$^{\circ}C$ than those of 3.7% phosphorous deposit (1090Hk). But in the case of heat treating at 400$^{\circ}C$, the former has lower hardness value (1000Hk) than the latter and has remarkably Ni(III) orientation by heat treatment. (4) The 3.7% phosphorous deposit heat treated at 400$^{\circ}C$ has better wear resistance than hard chromium plating.

• 대한치과기공학회지
• /
• 제21권1호
• /
• pp.15-26
• /
• 1999

This study was carried out by observing to composition of oxide on the surface of dental porcelain low gold alloy with various Indium additions according to the degassing and analysing the change composition of additional elements In on diffusion behaviors of Porcelain-matal surface. The specimens used were Au-Pd-Ag alloys by small indium addition. These specimens were treated for 10min at $1000^{\circ}C$ in vacuum condition. To investigate the microsturcture of oxidized alloy surface, SEM and EDAX were used, and EPMA were used to investigate the diffusion behaviors of porcelain-metal surface. X-ray diffraction were used to observe the morphological changes in the oxidation zone. The results of this study were obtained as follows ; 1) The hardness of alloy increased with increasing amount of In addition. 2) The formation of oxidation increased with increasing In content after heat treatment. 3) Diffusion of indium elements increased with increasing In content in metal-porcelain surface after firing. 4) The oxidations of alloy surface were mainly $In_2O_3$.

• 한국결정성장학회지
• /
• 제15권5호
• /
• pp.202-207
• /
• 2005

Kaolin과 규석 및 $Mg(OH)_2$등의 원료로 만들어진 slip을 casting 할 때 slip의 점도가 slip casting 속도와 소결체의 미세조직에 미치는 영향을 보면 slip-casting속도는 slip의 점도가 낮을 경우 감소하였으며 slip의 점도범위는 $3.0\~17.0\;cP$가 적당하였다. Slip의 점도를 조절하면 표면층, 표면 내부층, 중간층, 내면층의 미세조직을 비교적 균일하게 casting 할 수 있다 소성온도 $1350^{\circ}C$에서 시편의 구성광물은 cordierite 결정만으로 되어있었다.

• 한국재료학회지
• /
• 제6권11호
• /
• pp.1099-1106
• /
• 1996

니켈-수소화물전지의 음극재료로서 주목을 받고 있는 다원계 Zr기 Laves 합금의 조성에 따른 결정구조, 방전특성등을 조사하였다. 전극은 아크 용해한 합금을 분쇄한 분말과 PVA를 다공성니켈 foam에 충진하여 제작하였고 충방전시험은 6M KOH 용액중에서 수행하였다. 대상 합금은 ZrNi2를 기본조성으로 하여 이중 Ni의 일부를 V, Mn, Cr, Mo 또는 W로 치환한 삼원계 및 사원계 합금이었다. 이들 합금의 충방전 실험결과 ZrV0.5Mn0.5Ni1.0의 경우가 260 mAh/g로 가장 높은 방전용량을 나타내었다. 이 합금의 방전용량은 방전전류밀도의 영향을 크게 받았으며 10 mA/g과 200mA/g의 방전전류에서 각각 300mAh/g와 150mAh/g이었다. 이 합금을 110$0^{\circ}C$에서 열처리한 경우 저율방전시에는 방전용량의 변화가 거의 없었으나 수소의 확산이 율속이 될 것으로 생각되는 고율 방잔시에서는 방전용량이 현저하게 감소하였다. 이러한 현상은 열처리에 의해 수소의확산을 용이하게 해주는 격자결함이 감소하기 때문이 아닌가 생각된다.

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.130-135
• /
• 1999

고로슬래그 시멘트의 저온 조기 강도를 증진키 위하여 고로슬래그의 분말도를 높이고 낮은 물:시멘트 비(W/C)의 혼합수량을 사용하였다. 분쇄조제를 사용하여 6,280$\textrm{cm}^2$/g(Blaine)로 미분쇄한 고로슬래그를 일반 포틀랜드 시멘트와 혼합하여 고로슬래그 40%의 고로슬래그 시멘트를 만들었다. 그리고 시판의 naphthalene계 고성능감수제를 사용하여 혼합수량을 W/C=0.50(KS L 5105)에서 W/C=0.33으로 저하시킬 수 있었다. 상술한 방법을 통하여 고로슬래그 시멘트의 저온 조기 강도를 포트랜드 시멘트 강도보다 오히려 더 높게 향상시킬 수 있었으며, 기공구조 및 임피던스 분석의 방법으로 본 시멘트의 미세구조를 조사하였다.

• 한국주조공학회지
• /
• 제34권3호
• /
• pp.100-106
• /
• 2014

In recent years, Mg and its alloys have attracted a great deal of attention due to their low density, relatively excellent castability, and straightforward recyclability. Mg alloys have been widely applied to various industrial fields, and are representatively used in automotive and electronic parts. According to previous researches, the electrical conductivity of Mg alloys greatly decreases with increasing Al content. However, with the addition of Zn and/or Cu, the electrical conductivity of Mg alloys is maintained or slightly increased, and improved mechanical properties are obtained as well. On this basis, Mg-Zn-Cu alloys have been investigated in the present study with a focus on the effect of adding Zn and Cu on the electrical conductivity. The Zn and Cu contents ranged from 4 to 6wt.% and 0 to 1.5wt.%, respectively. Ternary Mg-Zn-Cu alloys have been prepared by gravity casting in a steel mold. In the as-casting condition, the electrical conductivity of Mg-Zn-Cu alloys showed a linear increasing trend with decreasing Zn and increasing Cu contents. Furthermore, impact values of Zn = -1.5 and Cu = 2.5 were determined for these alloys by electrical conductivity tests.

• 한국식품조리과학회지
• /
• 제7권1호
• /
• pp.11-14
• /
• 1991

가열온도를 달리하여 제조한 도토리와 밤 전분 gel의 물리적 특성을 비교한 결과는 아래와 같다. 1. $60^{\circ}C$로 가열한 경우 도토리보다 밤의 전분 입자가 훨씬 많이 풀어져 있었고, 도토리는 9$0^{\circ}C$$90^{\circ}C$로 가열한 gel에서 규칙적인 3차원적 망상구조를 보였으며 밤 전분 gel은 $70^{\circ}C$부터 미세한 다공성의 network를 보여 주었다. 2. X-ray 회절도는 두 시료 전분 gel모두 8~$11^{\circ}C$와 16~$19^{\circ}C$부근에서 두개의 약한 peak만을 보여주었다. 3. 3. Hardness는 70% 압착, 24시간 성형 gel에서, cohesiveness는 60% 압착, 3시간 성형 gel에서 크게 나타났으며, 특히 cohesiveness에서 압착율 변화에 의한 효과가 크게 나타났다. 또한 도토리는 90, $98^{\circ}C$에서, 밤은 $80^{\circ}C$에서 최고의 hardness값을 보였으며 cohesiveness는 두 시료 모두 가열 온도가 높아질수록 증가하였다.

• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.258-261
• /
• 2000

Highly (h00)-oriented (Ba, Sr)TiO$_3$(BST) thin films were grown by pulsed laser deposition on the perovskite LaNiO$_3$(LNO) metallic oxide layer as a bottom electrode. The LNO films were deposited on SiO$_2$/Si substrates by rf-magnetron sputtering method. The crystalline phases of the BST film were characterized by x-ray $\theta$-2$\theta$, $\omega$-rocking curve and $\psi$-scan diffraction measurements. The surface microsturcture observed by scanning electron microscopy was very dense and smooth. The low-frequency dielectric responses of the BST films grown at various substrate temperatures were measured as a function of frequency in the frequency range from 0.1 Hz to 10 MHz. The BST films have the dielectric constant of 265 at 1 kHz and showed multiple dielectric relaxation at the low frequency region. The origin of these low-frequency dielectric relaxation are attributed to the ionized space charge carriers such as the oxygen vacancies and defects in BST film, the interfacial polarization in the grain boundary region and the electrode polarization. We studied also on the capacitance-voltage characteristics of BST films.

• 한국정밀공학회지
• /
• 제16권9호
• /
• pp.41-47
• /
• 1999

The scale of dendritic structure of a cast preform plays a key role in determining the mechanical properties of cast/forged products. In this study, casting experiments are carried out to reduce dendrite arm spacing (DAS) to smaller than 20 ${\mu}$m by increasing cooling rate of the mold and then to spheriodize dendritic structures by addition of alloying elements such as Zr and Ti-B. From the casting experiments, appropriate casting conditions for producing the cast preform of a motorcycle connecting rod are obtained. To obtain fine microstructures of the cast preform, mold temperature must set to be low whilst cooling rate being high. When cooling rate is 10 $^{\circ}C$/s, the size of DAS is 17.4 ${\mu}$m. And the degree of spheriodization of a grain in the cast preform is described by aspect ratio, which is defined as the ratio of major and minor radii of an elliptical grain. When 0.5% Zr and 0.24 % Ti+B are added to the molten aluminum alloy, the best aspect-ratio 0.75 is obtained. After forging the cast preform of a motorcycle connecting rod, the microstructure and mechanical properties of the cast preform are compared with those of the cast/forged product. Cast/forged products are superior in microstructure and in mechanical properties such as ultimate strength, elongation, and hardness.

• 한국결정성장학회지
• /
• 제9권2호
• /
• pp.231-239
• /
• 1999

세라믹 복합체의 미세구조는 이차상의 종류 및 양, 소결 조제, 그리고 소결 조건(즉, 소결온도, 압력, 유지시간)에 영향을 받는다. 또한, 내마모 특성은 미세구조와 작업 조건이 내마모 특성에 크게 영향을 미친다. 본 실험에서는 질화규소에 마그네시아의 양을 변화시켜 가압 소결(Hot Press) 방법으로 시편을 제조하였다. 마그네시아 양에 따른 미세구조, 기계적 특성(경도, 강도, 파괴인성), 그리고 다양한 분위기(공기, 물, paraffin oil)에서의 내마모 특성을 조사하였다. 질화규소에 마그네시아의 양이 증가하였을 때, 입계의 유리상이 $\beta$-상의 장주형 입자를 커지게 하고, 또한 Hertzian contact damage를 저하시킨다. 대기 중에서 내마모 거동은 강도뿐만 아니라 파괴인성과 관련이 있고, 물과 paraffin oil에서는 경도와 밀접하다. 물속에서 마모시험 중 많은 유리상이 물과 반응하는 것을 생각할 수 있다. 그러므로 마찰 화학적 반응(tribochemical reaction)은 마모도 저하시킨다. Paaraffin oil에서 높은 하중을 부하할 경우, Hertzian contact damage 때문에 초기 마모가 마모량에 지배적이다.