• Journal of Periodontal and Implant Science
• /
• v.25 no.3
• /
• pp.741-755
• /
• 1995

Currently titanium is the material of choice for implants because of its biological acceptance. This high degree of biocompatibility is thought to result, in part, from the protective and stable oxide layer that presumably aids in the bonding of the extracellular matrix at the implant-tissue interface. Endosseous dental implants are interfaced with bone, connective tissue, and epithelium when implanted into the jaw bone. The soft tissue interface including connective tissue and epithelium is one of the most critical factors in the determination of implant maintenance and prognosis. For maintenance of failing or failed implants, it is essential to treat the implant fixture surface to remove bacterial endotoxins and make a surface tolerated by surrounding soft and hard tissues. In this study, the effect of mechanical treatment on titanium plasma sprayed implant on adhesiveness and proliferation of human gingival fibroblasts and changed surface characteristics were studied. titanium plasma sprayed discs manufactured by Friedrichsfeld company were treated with loaw speed stone bur, a rubber point and a jetpolisher. Its surface components were analyzed with Energy dispersive X-ray spectroscopy to evaluate whether the surface characteristics were altered or not. To observe the spreading pattern of the human gingival fibroblasts which attached to the all specimens author used the scanning electron microscope. The results were as follows : Pure titanium and plasma sprayed titanium, stone polished titanium showed titanium peak and small amout of aluminum, so there was no alteration on surface characteristics. Under the scanning electron microscopic examination in the initial attachment of human gingival fibroblast, there was a slight enhancement in pure titanium, stone polished titanium than plasma sprayed titanium. After 6 hours, the pure titanium and stone polished titanium showed human gingival fibroblasts were elongated and connected with numerous processes. Human gingival fibroblasts were more intimately attached on the pure titanium discs than on the other discs. The human gingival fibroblasts attached on the plasma sprayed titanium by thin and elongated processes. After 24 hours, the human gingival fibroblasts connected with each other via numerous processes and compeletly covered the pure titanium and stone polshed titanium discs. Human gingival fibroblasts had multiple point contacts with more long and thin lamellopodia and showed a little bare surface on plasma sprayed titanium discs.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.14 no.2
• /
• pp.79-87
• /
• 1978

This is an experimental study on friction welding and heat treatment of engine exhaust valve materials whose welding combination is SCr4 as stem to 21-4N as head and SUH3 to 21-4N. In this study, not only the experiments of friction welding under the selected optimum welding condition and the examination of the mechanical properties were carried out, but also the heat treatment of friction welded specimens under the two selected conditions was taken to obtain the better welding character, eliminating the latent stress and the hardness peak which appeared at the welded zones of heat resisting steel(21-4N, SUH3) and low alloyed steel ($SCr_4$) friction weldments. The results obtained by the experiments and consideration in this study are as follows: I) It was experimentally proved quite reasonable that 'speed=3,OOO rpm, heating pressure Pl=8 kg/ mm2, upsetting pressure p, = 20 kg/mm', heating time $t_1$ = 3 see, upsetting time TEX>$t_2$ = 2.5 sec' was selected as the optimum welding condition for friction-welding the engine exhaust valve materials $SCr_4$ to 21-4 Nand SUH 3 to 21-4 N. 2) The results of the previous study and this one on friction welding of such dissimilar materials as SUH 3-SUH 31, SCr 4-SUH 31, SCr 4-SUH 3, SUH 3-CRK 22, SCr4-21-4 Nand SUH3-21-4 N agreed with each other substantially in the friction welding characteristics at welded interface zones. 3) It was also certified quite satisfactory that '600\ulcornerCX30 min. Xroom air cooling' as an optimum heat treatment condition of the friction welded materials SCr 4-21-4 Nand SUH 3-21-4 N was experimentally determined to eliminate the latent stress and the hardness peak at welded zones. 4) About 20% of the tensile strength before heat treatment of friction welded specimens was decreased after heat treatment 600\ulcornerCX30 min. Xair cooling, but the location of fracture was moved from heat affected zone to parent $SCr_4$ & SUH3. 5) Microscopic examination of the weld joints friction-welded and heat-treated under the above mentioned conditions revealed that the weld zone is very narrow and has a fine grained intermixed structure without any welding defects. 6) The above mentioned conditions can be also utilized as friction welding parameters of the other dissimiar materials for engine valve production.

• Journal of Periodontal and Implant Science
• /
• v.37 no.sup2
• /
• pp.427-445
• /
• 2007

To improve osseointegration at the boneto-implant interface, several studies have been carried out to modify titanium surface. Variations in surface texture or microtopography may affect the cellular response to an implant. Osteoblast-like cells attach more readily to a rougher titanium surface, and synthesis of extracellular matrix and subsequent mineralization were found to be enhanced on rough or porous coated titanium. However, regarding the effect of roughened surface by physical and mechanical methods, most studies carried out on the reactions of cells to micrometric topography, little work has been performed on the reaction of cells to nanotopography. The purpose of this study was to examme the response of osteoblast-like cell cultured on blasted surfaces and alkali treated surfaces, and to evaluate the influence of surface texture or submicro-scaled surface topography on the cell attachment, cell proliferation and the gene expression of osteoblastic phenotype using ROS 17/2.8 cell lines. In scanning electron micrographs, the blasted, alkali treated and machined surfaces demonstrated microscopic differences in the surface topography. The specimens of alkali treatment had a submicro-scaled porous sur-face with pore size about 200 nm. The blasted surfaces showed irregularities in morphology with small(<10 ${\mu}m$) depression and indentation among flatter-appearing areas of various sizes. Based on profilometry, the blasted surfaces was significantly rougher than the machined and the alkali treated surfaces (p$TiO_2$) were observed on alkali treated surfaces, whereas not observed on machined and blasted surfaces. The attachment morphology of cells according to time was observed by the scanning electron microscope. After 1 hour incubation, the cells were in the process of adhesion and spreading on the prepared surfaces. After 3 hours, the cells on all prepared surfaces were further spreaded and flattened, however on the blasted and alkali treated surfaces, the cells exhibited slightly irregular shapes and some gaps or spaces were seen. After 24 hours incubation, most cells of the all groups had a flattened and polygonal shape, but the cells were more spreaded on the machined surfaces than the blasted and alkali treated surfaces. The MTT assay indicated the increase on machined, alkali treated and blasted surfaces according to time, and the alkali treated and blasted surfaces showed significantly increased in optical density comparing with machined surfaces at 1 day (p<0.01). Gene expression study showed that mRNA expression level of ${\alpha}\;1(I)$ collagen, alkaline phosphatase and osteopontin of the osteoblast-like cells showed a tendency to be higher on blasted and alkali treated surfaces than on the machined surfaces, although no siginificant difference in the mRNA expression level of ${\alpha}\;1(I)$ collagen, alkaline phosphatase and osteopontin was observed among all groups. In conclusion, we suggest that submicroscaled surfaces on osteoblast-like cell response do not over-ride the one of the surface with micro-scaled topography produced by blasting method, although the microscaled and submicro-scaled surfaces can accelerate osteogenic cell attachment and function compared with the machined surfaces.