• Restorative Dentistry and Endodontics
• /
• 제45권1호
• /
• pp.12.1-12.8
• /
• 2020

Objectives: The aim of this in vitro study was to evaluate the microhardness and surface roughness of composite resins before and after tooth bleaching procedures. Materials and Methods: Sixty specimens were prepared of each composite resin (Filtek Supreme XT and Opallis), and BisCover LV surface sealant was applied to half of the specimens. Thirty enamel samples were obtained from the buccal and lingual surfaces of human molars for use as the control group. The surface roughness and microhardness were measured before and after bleaching procedures with 35% hydrogen peroxide or 16% carbamide (n = 10). Data were analyzed using 1-way analysis of variance and the Fisher test (α = 0.05). Results: Neither hydrogen peroxide nor carbamide peroxide treatment significantly altered the hardness of the composite resins, regardless of surface sealant application; however, both treatments significantly decreased the hardness of the tooth samples (p < 0.05). The bleaching did not cause any change in surface roughness, with the exception of the unsealed Opallis composite resin and dental enamel, both of which displayed an increase in surface roughness after bleaching with carbamide peroxide (p < 0.05). Conclusions: The microhardness and surface roughness of enamel and Opallis composite resin were influenced by bleaching procedures.

• Restorative Dentistry and Endodontics
• /
• 제28권4호
• /
• pp.354-359
• /
• 2003

This study evaluated the effectiveness of the light emitting diode(LED) units for composite curing. To compare its effectiveness with conventional quartz tungsten halogen (QTH) light curing unit. the microhardness of 2mm composite. Z250, which had been light cured by the LEDs (Ultralume LED2, FreeLight, Developing product Dl) or QTH (XL 3000) were compared on the upper and lower surface. One way ANOVA with Tukey and Paired t-test was used at 95% levels of confidence. In addition. the amount of linear polymerization shrinkage was compared between composites which were light cured by QTH or LEDs using a custom-made linometer in 10s and 60s of light curing, and the amount of linear polymerization shrinkage was compared by one way ANOVA with Tukey. The amount of polymerization shrinkage at 10s was XL3000 > Ultralume 2. 40. 60 > FreeLight, D1 (P<0.05) The amount of polymerization shrinkage at 60s was XL3000 > Ultralume 2, 60> Ultralume 2.40 > FreeLight, D1 (P<0.05) The microhardness on the upper and lower surface was as follows ; (equation omitted) It was concluded that the LEDs produced lower polymerization shrinkage in 10s and 60s compared with QTH unit. In addition. the microhardness of samples which had been cured with LEDs was lower on the lower surfaces than the upper surfaces whereas there was no difference in QTH cured samples.

• 한국재료학회지
• /
• 제20권8호
• /
• pp.439-443
• /
• 2010

Nano sized SiC particles (270 nm) are easily agglomerated in nickel sulfamate electrolytic bath during a composite electrodeposition process. The agglomeration of nano particles in composite coatings can significantly reduce the mechanical properties of the composite coatings. In this study, Ni-SiC nano composite coatings were fabricated using a conventional electrodeposition process with the aid of ultrasound. Nano particles were found to be distributed homogeneously with reduced agglomeration in the ultrasonicated samples. Substantial improvements in mechanical properties were observed in the composite coatings prepared in presence of ultrasound over those without ultrasound. Ni-SiC composite coatings were prepared with variable ultrasonic frequencies ranging from 24 kHz to 78 kHz and ultrasonic powers up to 300 watts. The ultrasonic frequency of 38 kHz with ultrasonic power of 200 watt was revealed to be the best ultrasonic conditions for homogeneous dispersion of nano SiC particles with improved mechanical properties in the composite coatings. The microstructures, phase compositions, and mechanical properties of the composite coatings were observed and evaluated using SEM, XRD, Vickers microhardness, and wear test. The Vickers microhardness of composite coatings under ultrasonic condition was significantly improved as compared to the coatings without ultrasound. The friction coefficient of the composite coating prepared with an ultrasonic condition was also smaller than the pure nickel coatings. A synergistic combination of superior wear resistance and improved microhardness was found in the Ni-SiC composite coatings prepared with ultrasonic conditions.

• Restorative Dentistry and Endodontics
• /
• 제39권1호
• /
• pp.17-23
• /
• 2014

Objectives: This study evaluated the efficacy of Endosolv-R and Xylene in softening epoxy resin based sealer after 1 to 2 min exposure. Materials and Methods: Sixty Teflon molds ($6mm{\times}1.5mm$ in inner diameter and depth) were equally divided into 3 groups of 20 each. AH 26 (Dentsply/De Trey), AH Plus (Dentsply/De Trey), Adseal (Meta-Biomed) were manipulated and placed in the molds allotted to each group and allowed to set at $37^{\circ}C$ in 100% humidity for 2 wk. Each group was further divided into 2 subgroups according to the solvents used, i.e. Xylene (Lobachemie) and Endosolv-R (Septodont). Specimens in each subgroup were exposed to respective solvents for 1 and 2 min and the corresponding Vicker's microhardness (HV) was assessed. Data was analysed by Mauchly's test and two-way analysis of variance (ANOVA) with repeated measures, and one-way ANOVA. Results: Initial hardness was significantly different among the three sealers with AH Plus having the greatest and Adseal having the least. After 2 min, Xylene softened AH Plus and Adseal sealer to 11% and 25% of their initial microhardness, respectively (p < 0.001), whereas AH 26 was least affected, maintaining 89.4% of its initial microhardness. After 2 min, Endosolv-R softened AH 26, AH Plus and Adseal to 12.7, 5.6 and 8.1% of their initial microhardness, respectively (p < 0.001). Conclusions: Endosolv-R was a significantly more effective short term softener for all the tested sealers after 2 min whereas Xylene was an effective short term softener against AH plus and Adseal but less effective against AH 26.

• Restorative Dentistry and Endodontics
• /
• 제39권4호
• /
• pp.310-318
• /
• 2014

Objectives: This study examined the influence of the resin thickness on the polymerization of silorane- and methacrylate-based composites. Materials and Methods: One silorane-based (Filtek P90, 3M ESPE) and two methacrylate-based (Filtek Z250 and Z350, 3M ESPE) composite resins were used. The number of photons were detected using a photodiode detector at the different thicknesses (thickness, 1, 2 and 3 mm) specimens. The microhardness of the top and bottom surfaces was measured (n = 15) using a Vickers hardness with 200 gf load and 15 sec dwell time conditions. The degree of conversion (DC) of the specimens was determined using Fourier transform infrared spectroscopy (FTIR). Scratched powder of each top and bottom surface of the specimen dissolved in ethanol for transmission FTIR spectroscopy. The refractive index was measured using a Abbe-type refractometer. To measure the polymerization shrinkage, a linometer was used. The results were analyzed using two-way ANOVA and Tukey's test at p < 0.05 level. Results: The silorane-based resin composite showed the lowest filler content and light attenuation among the specimens. P90 showed the highest values in the DC and the lowest microhardness at all depth. In the polymerization shrinkage, P90 showed a significantly lower shrinkage than the rest two resin products (p < 0.05). P90 showed a significantly lower refractive index than the remaining two resin products (p < 0.05). Conclusions: DC, microhardness, polymerization rate and refractive index linearly decreased as specimen thickness linearly increased. P90 showed much less polymerization shrinkage compared to other specimens. P90, even though achieved the highest DC, showed the lowest microhardness and refractive index.

• 대한치위생과학회지
• /
• 제5권1호
• /
• pp.29-38
• /
• 2022

Background: This study aimed to compare the remineralization effects of sodium caseinate and other substances on artificially demineralized enamel. Methods: We selected 25 healthy human premolars and molars and produced a total of 75 specimens by dividing them into five groups: control group, with distilled water; experimental group 1 (EG1), with 3% sodium caseinate; EG2, with 10% sodium caseinate; EG3, with casein phosphopeptide-amorphous calcium phosphate (CPP-ACP); and EG4, with 0.05% NaF. Subsequently, the specimens were immersed in an artificial demineralization solution for 60 min. The demineralized specimens were then immersed in a remineralization solution for 7 days. Surface microhardness was measured using a microhardness tester, and remineralized lesions were observed under a scanning electron microscope (SEM). Regarding statistical analysis, the paired t-test and analysis of variance were performed using the SPSS program. Results: Although the surface hardness of the remineralized lesions increased significantly in all groups (p<0.05), the average increment did not differ significantly between the groups. The surface microhardness of CPP-ACP was the highest, followed by that of 0.05% NaF and 10% sodium caseinate. The remineralization effect of sodium caseinate was similar to that of 0.05% NaF. SEM confirmed that all groups treated with the remineralization solution were remineralized. Conclusions: Although the remineralization effect of sodium caseinate was slightly lower than that of CPP-ACP, it was similar to that of 0.05% NaF. Therefore, to enhance the remineralization effect of sodium caseinate, the appropriate concentration and application time should be determined.

• 사물인터넷융복합논문지
• /
• 제9권3호
• /
• pp.61-67
• /
• 2023

구리의 전기주조 공정을 최적화하기 위하여 이중 비밀 다층구조의 역전파 뉴럴 네트워크가 구성된다. 샘플 학습을 통하여, 구리 전기주조 공정 조건과 목표 특성 간의 함수관계가 정확히 성취되고, 구리 전기주조 공정 내에서 다층구조의 미세강도와 장력에 대한 예측이 이루어진다. 예측된 결과는 펄스 전원공급기를 장착한 구리 피로인산염 솔루션 시스템 내에서 구리의 전해석출 시험에 의하여 증명된다. 그 결과는 다음과 같이 나타난다. "3-4-3-2" 구조의 이중비밀 다층구조 뉴럴 네트워크에 의하여 예측된 구리 다층구조의 미세강도와 장력은 실험값에 매우 근접하며 그 상대적 오차는 2.32%보다 작다. 주어진 파라미터의 범위 내에서, 구리의 미세강도는 100.3~205.6MPa이며, 장력은 112~485MPa 정도로 측정된다. 미세강도와 장력이 최적인 조건에서 그에 대응하는 공정 조건은 다음과 같다: 전류밀도는 2A·dm-2, 펄스 주파수는 2KHz, 펄스의 듀티싸이클은 10%이다.

• Restorative Dentistry and Endodontics
• /
• 제49권2호
• /
• pp.18.1-18.13
• /
• 2024

Objectives: This study was conducted to evaluate the mechanical properties of relined and non-relined fiberglass posts when cemented to root canal dentin using a conventional dual-cure resin cement or a self-adhesive resin cement. Materials and Methods: Two types of resin cements were utilized: conventional and self-adhesive. Additionally, 2 cementation protocols were employed, involving relined and non-relined fiberglass posts. In total, 72 bovine incisors were cemented and subjected to push-out bond strength testing (n = 10) followed by failure mode analysis. The cross-sectional microhardness (n = 5) was assessed along the root canal, and interface analyses (n = 3) were conducted using scanning electron microscopy (SEM). Data from the push-out bond strength and cross-sectional microhardness tests were analyzed via 3-way analysis of variance and the Bonferroni post-hoc test (α= 0.05). Results: For non-relined fiberglass posts, conventional resin cement exhibited higher pushout bond strength than self-adhesive cement. Relined fiberglass posts yielded comparable results between the resin cements. Type II failure was the most common failure mode for both resin cements, regardless of cementation protocol. The use of relined fiberglass posts improved the cross-sectional microhardness values for both cements. SEM images revealed voids and bubbles in the incisors with non-relined fiberglass posts. Conclusions: Mechanical properties were impacted by the cementation protocol. Relined fiberglass posts presented the highest push-out bond strength and cross-sectional microhardness values, regardless of the resin cement used (conventional dual-cure or self-adhesive). Conversely, for non-relined fiberglass posts, the conventional dual-cure resin cement yielded superior results to the self-adhesive resin cement.

• Restorative Dentistry and Endodontics
• /
• 제27권4호
• /
• pp.403-410
• /
• 2002

Several ways of curing are being tried to improve material's properties and reduce marginal gap. However, all are considering about the pattern of light intensity. It was noted from the preliminary study the change of light wavelength from filter changing may give an impact on material's property and microleakage. The object of this study was to verify the effect of filters with various wavelength width on the microhardness and microleakage of composite resin ; hybrid type of DenFil and submicron hybrid type of Esthet X. Composite resins were cured using 3 kinds of filter; narrow-banded(465-475 nm), mid-banded(430-470 nm), wide-banded(400-500 nm). After the estimation of microhardness. degree of dye penetration and the maximum gap from SEM evaluation were done between 4 groups that showed no difference in microhardness value of the lower surface . The results were as follows : 1 Adequate microhardness could not be gained with a narrow-banded filter irrespective of curing time. At the upper surface, DenFil should be polymerized with middle or wide-banded filter for 20 seconds at least, while Esthet X be col$.$ed with middle or wide-banded filter for 30 seconds at least to get simitar hardness value to control group. 2. There was little dye penetration in enamel margin, but all dentin margins skewed much more dye penetration irrespective of curing conditions. Although there was no statistical difference, groups cured with mid-banded filter for 40 seconds and with wide-width filter for 20 seconds showed relatively less dye penetration. 3. It was revealed from the SEM examination that group cured with wide-banded filter had the smallest gap without statistical significance. Spearman's rho test showed that the correlation between the results of dye penetration and SEM examination was very low. From these results, it could be concluded that curing with wide-width filter would be better than the other techniques, even though the curing technique using mid-width filter seems to have its own unique advantage.

• 한국치위생학회지
• /
• 제13권2호
• /
• pp.351-360
• /
• 2013

Objectives : The purpose of this study was to evaluate the effects of tooth bleaching agent contained 15% carbamide peroxide on the color, microhardness and surface roughness of tooth-colored restorative materials by using pH cycling model. Methods : Four types of tooth-colored restorative materials, including a composite resin(Filtek Z350 ; Z350), a flowable composite resin(Filtek P60 : P60), a compomer(Dyract$^{(R)}$ AP ; DY), and a glass-ionomer cement(KetacTM Molar Easymix ; KM). were used in the study. Eighty-eight specimens of each material were fabricated, randomly divided into two groups(n=44): experimental group(15% carbamide peroxide) and control group(distilled water). These groups were then divided into four subgroups(n=11). All groups were bleached 4 hours per day for 14 days using pH cycling model. The authors measured the color, microhardness, and roughness of the specimens before and after bleaching. The data were analyzed with ANOVA and T-test. Results : Z350 and P60 showed a slight color change(${\Delta}E^*$), whereas DY and KM showed significantly color change(p<0.05). Among them, the greatest color change was observed in DY. Percentage microhardness loss(PML) of the distilled water group was 1.8 to 5.1%, and 15% peroxide peroxide group was 5.0 to 25.2%. Microhardness of DY and KM showed a statistically significant decrease(p<0.05). Roughness was increased in all groups after bleaching. Z350 and P60 does not have a significant difference(p>0.05), however DY and KM significantly increased more than the 0.2 ${\mu}m$(p<0.05). Conclusions : The effects of bleaching on restorative materials were material dependent. It is necessary to consider the type of the material before starting the treatment.