This study has been made to investigate into the behavior of fatigue limit, of fatigue crack initiation, and of fatigue crack propagation under the condition of rotating bending stress; specifically on the independency of stress field as well as the crack behavior of surface micro hole defect, which is made artificially through the specimen. The results obtained can be summarized as followa; 1) For the single micro hole defect, initiation of fatigue crack is occurred at both tips of microhole defect simultaneosly along the slip which are produced in the range of maximum principal stress arround micro hole defect independent of the size of micro hole defect. 2) For the neighbored deuble micro hole defects with equal size, in the range ($\frac{L}{r}$)ratio $\gtrsim$ 3 defined as the size of micro hole defect(2r) to the distance between the centers of micro hole defects (2L), the crack behavior of the micro hole defects is same as single one. However, for the range of $\frac{L}{r}$<3, the interference effect becomes significant as the ratio approaches to 1.

• 대한기계학회논문집
• /
• 제10권1호
• /
• pp.78-85
• /
• 1986

본 연구에서는 결함재의 결함선단에 발생 전파하는 피로거동을 검토하기 위해서 미소원공과 미소슬릿을 가공하고, 이것들의 피로한도를 기준으로 해서 이들 결함의 형상이 피로크랙 전파특성에 미치는 영향을 상세히 고찰하고자 한다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 춘계학술대회 논문집
• /
• pp.856-860
• /
• 2002

The main objective of this study is to consider the effect of fatigue crack behavior on the variable depth of micro hole defects in SM20C at the symmetric position. The fatigue crack propagation test is performed by rotary bending fatigue test machine. The relationship between crack length(2a), cycles(N) and crack growth rate(da/dN) are investigated in this study. The result from the rotary bending fatigue test under the applied stress at 250MPa turned out that the fatigue life illustrated almost constant when the depth of symmetric micro hole deflects is both part A and B at the hope depth(h) = 0.5mm.

• 대한기계학회논문집A
• /
• 제21권5호
• /
• pp.842-849
• /
• 1997

The aim of this study is an investigation of the interaction of two micro hole defects affecting fatigue crack initation life and propagation behavior. The locatio of two micro hole defects was considered as an angle of alignment and the distance between the centers of two micro hole defects. The fatigue cracking behavior is experimented under bending. When micro defects are located close to each other, the fatigue crack initiation lives are varied with their relative locations. In the experiments, the area of local plastic strain strongly played a role in the fatigue crack initiation lives. Therefore we introduce a parameter which contains the plastic deformation area at stress concentrations and propose a fatigue crack initiation life prediction curve. In addition, the directions and propagation rates of fatigue cracks initiated at two micro hole defects are studied experimentally.

• 대한기계학회논문집
• /
• 제12권2호
• /
• pp.278-285
• /
• 1988

본 연구에서는 SM15C재와 SM35C재에 퍼얼라이트, 페라이트 조직의 영향을 배재한 비교적 균질한 조직인 구상화시멘타이트조직과 SM35C재에 실용조직 이면서 비교적 균질한 조직인 마르텐사이트 조직을 만들고, 가공하였다.

• 대한기계학회논문집A
• /
• 제24권5호
• /
• pp.1288-1296
• /
• 2000

In this study, fatigue crack behavior between arbitrarily located defects was investigated by experiment. Especially, stress interaction between micro hole defects and fatigue cracking, and fatigue crack initiation life following the variation of location of micro hole defects were considered. In addition, crack initiation position by micro hole stress interaction and the relationship between stress concentration factor and fatigue initiation life are studied in detail.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 춘계학술대회 논문집
• /
• pp.521-527
• /
• 1997

Irregular shapes and growth behavior of surface micro-crack showed very complex and nonlinear propeties and many investigators have performed theoretical analysesand experiments on them to characterize fatigue strength. They had difficulties in estimating fatigue life due to random distribution, growth and coalescence of surface micro-cracks. The straightness of crack growth along intergranular and transgranular was prevented from irregular microstructure and precipitates. Euclid geometry can't quantify shape of surface micro-crack but ftractal geometry can. Therefore, it is suggested that average fractal dimension of surface micro-cracks is able to estimate fatigue life but fractal dimension of maximum surface micro-crack is not in Al 2024-T3 alloy.

• 대한기계학회논문집
• /
• 제8권2호
• /
• pp.141-144
• /
• 1984

본 연구에서는 완전 역 피로응력(completely reversed fatgue stress)를 받는 타원 노치에서 균열 발생과 전파에 대한 이론 임계 피로 한도를 응력 세기 계수 개념 을 도입하여 임의의 재질과 임으의 타원 노치 형상에 대해서 적용할 수 있도록 유도하 며 그 결과는 기존 이론보다 Frost의 실험치에 더 잘 일치함을 보이고자 한다.

• Journal of Mechanical Science and Technology
• /
• 제14권10호
• /
• pp.1021-1027
• /
• 2000

In this study, fatigue tests were performed to examine the effects of micro drill hole on fatigue limit of as cast and austempered ductile cast iron (ADI) using the rotary bending fatigue tester. As results, micro drill holes ($diameter{\leq}0.4mm$) did not influence the fatigue limit of ADI, compared to annealed ductile cast iron; the critical defect size of crack initiation, in ADI was larger than as cast. If the ${\sqrt{area}}$ of micro drill hole and graphite nodule in ADI are comparable, crack initiates at the graphite nodule. When the ruggedness developes through austempering treatment process, microstructure on crack initiation at micro drill hole is tougher than that of as cast ductile cast iron.

• 대한기계학회논문집
• /
• 제9권2호
• /
• pp.150-157
• /
• 1985

본 연구에서는 자연적인 미소흠함주위에 발생, 전파하는 피로크랙의 거동을 검토하기 위하여, 기존재료가 갖고 있는 흠함이나 비금속개재물을 대신할 수 있다고 생각되는 크기가 다른 비관통 인공미성구멍을 갖는 여러 종류의 시험편을 준비하고, 이 시험편들이 갖는 인공미성구멍주위에 발생전파하는 피로크랙의 거동을, 금속현미경 관찰을 토대로 상세히 고찰하였다. 그리고 이러한 관찰을 기초로 하여 비관통인공미 성구멍의 대성에 따른 피로한계도거동에 대해서도 고찰하였다.