• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.289-294
• /
• 1995

As the results of the study on the effects of mixing time for raw materials to the electric and magnetic properties of Mg-ferrite, the fraction of spinel phase after calcination and the geometry density of sintered Mg-ferrite increased from 30% to 100% and from 2.5g/cc to 4.25g/cc respectively due to mixing-homobenity of raw materials. The AC resistivity of grains decreased and lattice parameter, saturation magnetization increased due to the increase in Fe+2 of sintered body. conclusively the characteristic of powder after calcination had strong influence on the microstructure, electric, and magnetic properties in Mg-ferrite sintered body.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.1-10
• /
• 1995

Effects of calcination temperature on microstructure and electric-magnetic properties of Mg-ferrite were investigated. As the calcination temperature increase, the green density and the sintered density increase due to the enhancement of densification of calcined powder. The grain size in the sintered ferrite increases with increasing the calcination temperatures from 800 to 100$0^{\circ}C$, but decreases from 1000 to 120$0^{\circ}C$. The resistivity decreases with increasing the calcination temperatures from 800 to 110$0^{\circ}C$, but increases from 1100 to 120$0^{\circ}C$ due to the microstructure which consists of small, uniform grian size and pores at grain boundaries. Magnetization increases slightly due to the increasement of the sintered density while Curie temperature is almost constant regardless of calcination temperatures.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1991.11a
• /
• pp.54-55
• /
• 1991

• Resources Recycling
• /
• v.14 no.3
• /
• pp.63-67
• /
• 2005

As there are recent tendencies to raise horizontal frequencies so as to improve screen definition for high-quality TV and high definition display, ferrite core for deflective yokes requires materials with low coreloss in the areas of high frequencies. The researcher added CuO to low-loss Mg-Zn ferrite. After choosing MgO, ZnO, Fe$_2O_3$ and CuO, the researcher changed a ratio of composition, substituting MgO for CuO. These samples were sintered for three hours up to 980$^{\circ}C$~1350$^{\circ}C$. Measure magnetic permeability, electric loss, core loss and a rate of contraction.

• Journal of the Korean Ceramic Society
• /
• v.31 no.3
• /
• pp.235-240
• /
• 1994

The electric and magnetic properties of Mg1.9-2xMn0.05Fe4xO4+${\gamma}$+2wt% Al2O3, and its microstructure have been investigated as a function of ferrite composition (x=0.45, 0.5, 0.55). The microstructure turned out to be independent on the ferrite composition. The resistivity was decreased with increasing Fe contents, whereas the Curie temperature decreased. Saturation magnetization was varied from 1741 to 2022 G with composition, and squareness ratio (SR), coercive force (BHc) were decreased and increased with increasing Fe contents respectively, so the sample which SR and BHc were 0.97 Oe and 1.49 Oe can be attainable at x=0.45.